DOE OSTI2024

Effect of heat treatment on the microstructure of medium burn-up U-Mo monolithic fuel foils

Using scanning electron microscopy (SEM), this study evaluates the microstructure evolution of U-Mo fuel foils made with and without heat treatment at medium burn-up (of approximately 5 x 10 21 f/cm 3 ). The impact of annealing treatments on critical microstructural properties of the U-Mo fuel foils, including porosity, grain structure, Mo homogeneity, and fuel interaction with the Zr interlayer, was examined using large area lift outs (LALOs). The heat-treated specimens presented less grain refining at these burnups when compared to the un-heated specimens. Grain refinement was associated with porosities and fission products precipitation. Heat treatment can reduce fuel swelling during irradiation. Chemical inhomogeneity (Mo banding) was found to persist in the un-heated samples but was not present in the heat-treated samples. Thus, heat-treated U-Mo foils allows for more predictable fuel behavior under irradiation with respect to un-heated foils. The U-Mo and Zr interaction layer appears to be thicker and more continuous in the heat-treated sample which has been associated with stronger interface integrity during irradiation, as also observed in previous studies. These observations may indicate an overall improved performance of heat-treated fuel foil in a reactor. Further, the effect of local burn-up on grain size/refinement and porosities in each LALO specimen, sampled from different positions in the fuel foil, was difficult to analyze due to the large standard deviation of these parameters. Finally, evidence of grain refinement by polygonization may be present in these specimens.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Contributions to the mechanistic understanding of the microstructural evolution in irradiated U-Mo dispersion fuel

Here, advanced microstructural characterization techniques, such as scanning electron microscopy (SEM) and scanning transmission electron microscopy - energy dispersive x-ray spectroscopy (STEM-EDS), were used to interpret the fuel microstructure evolution and fission products behavior in U-Mo dispersion fuel irradiated in the Advanced Test Reactor (ATR) as part of the European Mini-Plate Irradiation Experiment (EMPIrE) test. The larger as-fabricated fuel grain size achieved by heat-treating the U-Mo powder resulted in slower high burnup structure (HBS) development and reduced fission gas porosity. Slower HBS kinetics was observed at the fuel kernels’ periphery, which contained smaller and less fission gas bubbles at all fission densities (FDs) investigated and was attributed to a locally reduced damage density and fission products concentration, as corroborated with Monte Carlo simulations. The non-refined grains at the fuel kernel periphery hosted a perfectly ordered fission Gas Bubble Superlattice (GBS) up to 6.3 × 10 21 fissions/cm 3 . Nano-scale STEM-EDS analysis presented in this study provided useful information on the GBS characteristic morphology and evolution in U-Mo fuel. The concentration of fission gas in the GBS progressively increased with FD, pointing to an evolution of the nanobubble pressure status with irradiation. A possible connection between the GBS collapse and HBS onset is proposed for which there exists a threshold in the misorientation of the refined sub-grains above which the GBS stability during irradiation is no longer preserved, resulting in the GBS collapse.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Micro X-ray computed tomography examination of mini plate fuel with hot isostatic pressed aluminum cladding

In order to minimize proliferation risks and improve security of nuclear material, the United States high performance research and test reactors (USHPRR) program is tasked with converting nuclear reactors that are fueled with highly enriched uranium (HEU) fuels to operate with low-enriched uranium (LEU) nuclear fuels. One favorable LEU fuel configuration is plate fuel with a metallic uranium-molybdenum foil clad within an aluminum alloy (AA 6061). In this fuel, the aluminum cladding is bonded with a hot isostatic pressing (HIP) method to seal the cladding around the fuel meat. However, the HIP process parameters influence the cladding performance, as a defective or incomplete bond can cause a pathway for corrosion. Micro X-ray computed tomography (XCT), a nondestructive technique that provides volumetric imaging, can be applied to inspect fuel plate cladding at the engineering scale. In this work, XCT methodology was developed and successfully utilized to not only observe the bond line of unirradiated mini fuel plates, but to also identify subsurface abnormalities in the plates’ cladding. Importantly, in future work, this technique could be applied to fuel plates, pre- and post-irradiation, to quantify irradiation effects on cladding defects and bond line integrity.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Tensile behavior of diffusion bonded AA6061 - AA6061 with variation in cooling method

Hot isostatically pressed AA6061 cladding is an important structural component of the high performance, Zr-laminated U-10Mo monolithic fuel system for the application in research and test reactors. In this study, the mechanical behavior of two diffusion bonded aluminum alloy, AA6061, was examined using tensile testing. Solid-to-solid diffusion bonding between two pieces of AA6061 was performed by isothermal annealing at 560 °C for 1.5 h, and diffusion couples were subsequently cooled via three different cooling methods: furnace cooling, air cooling, and water quenching. Dog-bone shaped tensile specimens, with 10 mm in gauge length (with diffusion bonded interface in the middle), and 1.5 × 1.5 mm 2 gauge cross-sections, were fabricated from the diffusion bonded AA6061 by electro-discharge machining. Yield strength (% EL at failure) of furnace cooled, air cooled and water quenched tensile specimens determined was 82 ~ 89 MPa (10 ~ 30%), 112 ~ 116 MPa (10 ~ 14%), and 149 ~ 164 MPa (10 ~ 17%), respectively. This variation in mechanical behavior was examined with cooling-rate dependent, concentrated precipitation of Mg 2 Si at the diffusion bonded interface, with due respect for mechanical properties of the AA6061 alloy that inherently vary as a function of cooling rate from 560 °C. Finite element analysis using ABAQUS was employed to augment experimental findings with the appropriate microstructural constituents and alloy properties. Results suggest that the strength is dominated by matrix/bulk properties of AA6061, while ductility is strongly influenced by the cooling method dependent presence of Mg 2 Si precipitates at the interface.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2023

Annealing influence on the microstructure of irradiated U-Mo monolithic fuel foils

In this study we compared the microstructure evolution of U-Mo fuel foils produced with and without heat treatment at low burn-up via advanced post-irradiation examination. The aim of this study is to observe after irradiation the ways in which the fabrication processes have influenced fuel behavior at early-stage irradiation, as for very low burn up microstructural studies are lacking. In this work it was observed that the larger grain size detected in the heat-treated samples before irradiation led to decreased grain refinement after irradiation. Grain refinement was associated with the presence of small nano-size bubbles and precipitates. This phenomenon is hypothesized to influence early fuel swelling during reactor irradiation. Grain refinement was also observed to increase in regions where γ-U decomposition was present. Thus, it was enhanced in the samples fabricated without heat treatment. The heat treatment also increased the thickness of the U-Mo/Zr interface, namely of the UZr 2 layer. However, the influence of this layer on fuel performance needs further investigation. On one side, it may contribute to better mechanical bonding; on the other, it may influence swelling and blistering in the interaction layer as porosity increases when this layer is increased. This was observed especially in the presence of increased area containing low Mo concentration, and thus containing a higher fraction of the α-U phase, which is highly susceptible to irradiation induced swelling. Strong evidence of reverse transformation under irradiation (α-U + γ'-U2Mo → bcc γ-U) was observed in these samples. While the precipitates (carbides and oxide) seem to be unaffected by the irradiation at these low burnups. However, further analyses are necessary at higher burn-up to assess the exact impact different heat treatments have on fuel performance.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Detailed characterization of a PWR fuel rod at high burnup in support of LOCA testing

Experimental investigations of the fuel microstructure and volatile fission products along the pellet of a high burnup specimen (local burnup 76 GWd/tHM) have been conducted to support future transient testing. Detailed microscopy examinations have been carried out at different length scales. Transmission electron microscopy has highlighted a significant amount of damage across the entire radius with the formation of networks of dislocations. The optical and scanning electron microscopy determined the formation of three zones in the pellet with different characteristics. An intermediate region with no grain subdivision, lower porosity than the central zone porosity and high retained fission gas in nanometric bubbles and in the matrix was present between r/r0 ˜ 0.55 and 0.8. The high retention of gas in this region might suggest that the region will be prone to fine fragmentation, in addition to the HBS. An abrupt transition in the structure was observed at mid radius, with a third region developing from the mid radius to the pellet center. In this part of the pellet, metallic and grey phases with size between hundreds of nanometers and a few micrometers have formed at grain boundaries. The majority of fission gas has been released from the grain matrix and the original grains have polygonised, forming sub-grain domains separated by low-angle grain boundaries. No final explanation can be given for the polygonization occurring in the center, but on the basis of the irradiation history and the analysis of all the post irradiation examination (PIE) data, it is postulated that the polygonization within the original grains is an effect of dynamic recovery occurring at high temperature in the fuel center.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Micro-tensile testing of the bond line in hot isostatic pressed aluminum

Considerable effort is being devoted to development and regulatory qualification of low enriched fuels for research and test reactors by many agencies worldwide. One promising fuel configuration being examined for United States higher power research and test reactors (USHPRRs) are plate-type fuels composed of a metallic uranium-molybdenum foil clad in an aluminum alloy. The two pieces of aluminum alloy cladding are bonded using a hot isostatic pressing method. The mechanical properties of the resulting bond line in the aluminum alloy cladding will vary by the HIP'ing parameters, requiring a need to characterize the bond line. Small scale mechanical testing can provide a path for evaluating the mechanical properties and deformation behavior of the bond line both prior to and following irradiation. Here, in this research, room temperature micro-tensile specimens of non-irradiated and irradiated samples containing an Al alloy (AA 6061) bond line were tested to evaluate its strength and deformation behavior. Observations indicated that the strain rate did not affect the deformation behavior or strength and most of the micro-tensile specimens failed in a ductile mode in grains around the bond line. There was no indication that the microstructural features from the bond line affected the mechanical properties of the micro-tensile specimens. An initial examination was performed on irradiated material but further systematic studies of the effects of irradiation can be performed in the future.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Understanding fission gas bubble distribution, lanthanide transportation, and thermal conductivity degradation in neutron-irradiated α-U using machine learning

U—10Zr based metallic nuclear fuel is the leading candidate for next-generation sodium-cooled fast reactors in the United States. US research reactors have used and tested this fuel type since the 1960s and accumulated considerable experience and knowledge about the fuel performance. Most of the knowledge, however, remains empirical. The lack of mechanistic understanding of fuel performance puts a large burden on proof through experimental verification for the qualification of U—10Zr fuel for commercial use. Further, this paper proposes an image data-driven machine learning approach, coupled with domain knowledge provided by advanced post irradiation examination, to provide unprecedented quantified insights into the morphology, size, density and the connectivity of fission gas bubbles and their effects on the fission product transportation and thermal conductivity. Specifically, we developed a method to automatically detect, extract statistics, and classify ~19,000 fission gas bubbles into different categories, and quantitatively link the data to lanthanide transportation through connected bubbles and degradation of thermal conductivity along the radial temperature gradient in a neutron irradiated U—10Zr annular fuel. Results indicate the approach can be modified to study other irradiation effects, such as secondary phase redistribution and gaseous fuel swelling in other irradiated nuclear fuels.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Dislocation Loops in Proton Irradiated Uranium-Nitrogen-Oxygen System

Here in this study, we investigated the dislocation loop types formed in the proton-irradiated uranium-nitrogen-oxygen (U-N-O) system, which involves uranium mononitride (UN), uranium sesquinitride (a-U2N3), and uranium dioxide (UO2) phases. The dislocation loop formation is examined using specimens irradiated at 400°C and 710°C. Based on the detailed transmission-based electron microscopy characterization with i) the morphology-based on-zone and ii) the invisibility-criterion based two-beam condition imaging techniques, only a single type of dislocation loop in each phase is found: a/2?110?, a/2?111?, or a/3?111? dislocation loops in UN, a-U2N3, and UO2 phases, respectively. Molecular statics calculations for the formation energy of perfect and faulted dislocation loops in UN phases indicate a critical loop size of ~ 6 nm, above which perfect loops are energetically favorable. This could explain the absence of faulted loops in the experimental observation of the irradiated UN phase at two temperatures. This work will enhance the understanding of irradiation induced microstructural evolution for uranium nitrides as advanced nuclear fuels for the next-generation nuclear reactors.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗