NASA NTRS1998

Determination of Yield in Inconel 718 for Axial-Torsional Loading at Temperatures up to 649 C

An experimental program has been implemented to determine small offset yield loci under axial-torsional loading at elevated temperatures. The nickel-base superalloy Inconel 718 (IN718) was chosen for study due to its common use in aeropropulsion applications. Initial and subsequent yield loci were determined for solutioned IN718 at 23, 371, and 454 C and for aged (precipitation hardened) IN718 at 23 and 649 C. The shape of the initial yield loci for solutioned and aged IN718 agreed well with the von Mises prediction. However, in general, the centers of initial yield loci were eccentric to the origin due to a strength-differential (S-D) effect that increased with temperature. Subsequent yield loci exhibited anisotropic hardening in the form of translation and distortion of the locus. This work shows that it is possible to determine yield surfaces for metallic materials at temperatures up to at least 649 C using multiple probes of a single specimen. The experimental data is first-of-its-kind for a superalloy at these very high temperatures and will facilitate a better understanding of multiaxial material response, eventually leading to improved design tools for engine designers.

Gil, Christopher M.↗

NASA NTRS1998

Determination of Yield in Inconel 718 for Axial-Torsional Loading at Temperatures up to 649 C

An experimental program has been implemented to determine small offset yield loci under axial-torsional loading at elevated temperatures. The nickel-base superalloy Inconel 718 (IN718) was chosen for study due to its common use in aeropropulsion applications. Initial and subsequent yield loci were determined for solutioned IN718 at 23, 371, and 454 C and for aged (precipitation hardened) IN718 at 23 and 649 C. The shape of the initial yield loci for solutioned and aged IN718 agreed well with the von Mises prediction. However, in general, the centers of initial yield loci were eccentric to the origin due to a strength-differential (S-D) effect that increased with temperature. Subsequent yield loci exhibited anisotropic hardening in the form of translation and distortion of the locus. This work shows that it is possible to determine yield surfaces for metallic materials at temperatures up to at least 649 C using multiple probes of a single specimen. The experimental data is first-of-its-kind for a superalloy at these very high temperatures and will facilitate a better understanding of multiaxial material response, eventually leading to improved design tools for engine designers.

Gil, Christopher M.↗

NASA NTRS1998

Determination of Yield and Flow Surfaces for Inconel 718 Under Axial-Torsional Loading at Temperatures Up to 649 C

An experimental program to determine flow surfaces has been established and implemented for solution annealed and aged IN718. The procedure involved subjecting tubular specimens to various ratios of axial-torsional stress at temperatures between 23 and 649 C and measuring strain with a biaxial extensometer. Each stress probe corresponds to a different direction in stress space, and unloading occurs when a 30 microstrain (1 micro eplison = 10(exp -6) mm/mm) offset is detected. This technique was used to map out yield loci in axial-torsional stress space. Flow surfaces were determined by post-processing the experimental data to determine the inelastic strain rate components. Surfaces of constant inelastic strain rate (SCISRS) and surfaces of constant inelastic power (SCIPS) were mapped out in the axial-shear stress plane. The von Mises yield criterion appeared to closely fit the initial loci for solutioned IN718 at 23 C. However, the initial loci for solutioned IN718 at 371 and 454 C, and all of the initial loci for aged IN718 were offset in the compression direction. Subsequent loci showed translation, distortion, and for the case of solutioned IN718, a slight cross effect. Aged IN718 showed significantly more hardening behavior than solutioned IN718.

Gil, Christopher M.↗

NASA NTRS1998

Investigation of Anomalous Behavior in Metallic-Based Materials Under Compressive Loading

An anomalous material response has been observed under the action of applied compressive loads in fibrous SiC/Ti (both Ti-6242 and Ti-15-3 alloys) and the monolithic nickel-base alloy IN-718 in the aged condition. The observed behavior is an increase, rather than a decrease, in the instantaneous Young's modulus with increasing load. This increase is small, but can be significant in yield surface determination tests, where an equivalent offset strain on the order of 10 micron(1 x 10(exp -6) m/m) is being used. Stiffening has been quantified by calculating offset strains from the linear elastic loading line. The offset strains associated with stiffening during compressive loading are positive and of the same order as the target offset strains in yield surface determination tests. At this time we do not have a reasonable explanation for this response nor can we identify a deformation mechanism that might cause it. On the other hand, we are not convinced that it is an artifact of the experimental procedure because a number of issues have been identified and seemingly ruled out. In fact, stiffening appears to be temperature dependent, since it decreases as the temperature increases.

Gil, Christopher M.↗