Gillespie, J. W. | Search NASA

NASA NTRS1986

Mode II interlaminar fracture of graphite/epoxy and graphite/PEEK

The end notched flexure (ENF) specimen is employed in an investigation of the interlaminar fracture toughness in Mode II (skew symmetric shear) loading of unidirectional graphite/epoxy and graphite/PEEK composites. Important experimental parameters such as the influence of precracking and the data reduction scheme for the Mode II toughness are discussed. Nonlinear load-deflection response is significant for the tough thermoplastic resin composite but is also present for the brittle thermoset composite. The observed nonlinearities, which are highly rate dependent, are attributed to a combination of slow stable crack growth preceding unstable crack growth and material inelastic behavior in the process zone around the crack tip.

Carlsson, L. A.↗

NASA NTRS1980

Failure analyses of composite bolted joints

The complex failure behavior exhibited by bolted joints of graphite epoxy (Hercules AS/3501) was investigated for the net tension, bearing and shearout failure modes using combined analytical and experimental techniques. Plane stress, linear elastic, finite element methods were employed to determine the two dimensional state of stress resulting from a loaded hole in a finite width, semiinfinite strip. The stresses predicted by the finite element method were verified by experiment to lend credence to the analysis. The influence of joint geometric parameters on the state of stress and resultant strength of the joint was also studied. The resulting functional relationships found to exist between bolted joint strength and the geometric parameters, were applied in the formulation of semiempirical strength models for the basic failure modes. A point stress failure criterion was successfully applied as the failure criterion for the net tension and shearout failure modes.

Wilson, D. W.↗