Quenching and Thermal Distortion Behavior of a Uranium Alloy Part - Experiments and Modeling
Explore the source record for details and available documents.
Phase Transformations, Thermal Stress, Heat Transf↗
Engineering topics
Glover, Alexandra Gannon
Publications and source records attributed to Glover, Alexandra Gannon.
The Viability of Selected Vacuum Furnace Quench Methods for Heat Treatment of Uranium
Recent developments in high-pressure gas-quench furnaces have allowed them, in many applications, to achieve heat transfer coefficients similar to those of oil-quench furnaces. Simultaneously, high-pressure gas quench furnaces offer many attractive qualities including a smaller footprint, limited waste generation, and a more consistent quench rate across a range of temperatures. With these benefits in mind, an experimental matrix was developed to assess the feasibility of implementing a high-pressure gas quenching furnace in the Sigma facility for processing of uranium alloys. The details of this experimental matrix, as well experimental results gathered during FY21 and FY22, will be presented.
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
17-7PH Housing Weld Report FY21
This report presents the work performed for welding 17-7PH stainless steel hemispheres, flanges, and accelerometer blocks. This includes weld development, microhardness measurements, calculated strengths, and distortion measurements after welding and heat treatment. The results of this report are utilized to propose a recommended welding procedure which was implemented for this experiment.
42 ENGINEERING↗
Tempering and Austempering of Double Soaked Medium Manganese Steels
The addition of a tempering or austempering step to the double soaking of a 0.14C–7.17Mn (wt pct) steel was investigated in the present contribution. The double soaking heat treatment is a two-step intercritical annealing heat treatment, which generates microstructures of athermal martensite, retained austenite and ferrite when applied to medium manganese steels. Microstructures following double soaking and (aus)tempering contained a combination of retained austenite, athermal or tempered martensite, and blocky or bainitic ferrite. X-ray diffraction, dilatometry and transmission Kikuchi diffraction were utilized to investigate microstructural changes which occurred during tempering or austempering. The resulting mechanical properties were measured using uniaxial tensile testing. The double soaking plus tempering heat treatment was shown to generate an ultimate tensile strength of 1,340 MPa in combination with 28 pct total elongation while the double soaking plus austempering heat treatment resulted in an ultimate tensile strength of 1,675 MPa and total elongation of 22 pct. Overall, both novel heat treatments produced a combination of strength and ductility desired for the third generation of advanced high strength steels.
36 MATERIALS SCIENCE↗