Grain orientation in high Tc superconductors by molten salt powder synthesis

The molten salt or the flux method is used to fabricate a grain oriented YBa2Cu3O(7-x) (123) superconductor. Here we suggest a two-stage approach in using the 'green phase', Y2BaCuO5 (211), as seed crystals in the formation of YBa2Cu3O(7-x). The process uses Y2BaCuO5 formed by molten salt synthesis. The Y2BaCuO5 phase was observed to be stable in water and in most of the salt systems. Salt processing can form a small quantity of anisotropic particles of Y2BaCuO5. This material can form the 123 phase when tape cast and sintered in the presence of the required levels of Ba and Cu.

Gopalakrishnan, Sudhakar↗

NASA NTRS1990

Grain orientation studies in superconductors

Grain oriented fabrication of ceramics utilizes the presence of some form of anisotropy in the particles of the starting material to obtain textured microstructures. The molten salt, or flux method, a popular technique for growing crystals and particles with anisotropic morphology, is utilized in this study. The formation of Ba2YCu3O(7-x) in the presence of molten salts of Na, K, Li belonging to chloride and sulfate systems does not appear feasible in the temperature range up to 900 C. Researchers also present the results of studies in using BaY2CuO5 as seed crystals in the formation of Ba2YCu3O(7-x) wherein BaY2CuO5 has been observed to have better stability in water and against most of the salts as compared to Ba2YCu3O(7-x). Additional results of molten salt processing of bismuth systems are also presented.

Gopalakrishnan, Sudhakar↗