Experimental and computational investigations on the SO 2 poisoning of (La 0.8 Sr 0.2 ) 0.95 MnO 3 cathode materials

To study the formation of detrimental phases under the sulfur gas impurity to the long-term degradation in the LSM cathode material, the classic cathode material, (La 0.8 Sr 0.2 ) 0.95 MnO 3 (LSM), was prepared, sintered, and annealed at 800, 900, and 1000°C in the sulfur-containing atmospheres, respectively. Through X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM), and Transmission electron microscopy (TEM) techniques, as well as the CALPHAD (Computer Coupling of Phase Diagrams and Thermochemistry) methodology, the secondary phases, especially the detrimental ones, under different conditions were predicted and experimentally verified correspondingly. Furthermore, sulfur poisoning results indicate that the accelerated tests might have degradation mechanisms different from actual operation conditions. More importantly, comprehensive comparisons among various impurity-containing conditions were also made to recommend better operation parameters.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Reversible solid oxide cells: Early performance and microstructural evolution during electrolysis and switched mode operation

Incorporating more renewables into our energy mix will require a diversity of technological solutions. Reversible solid oxide cell systems (RSOCs) operating reversibly between fuel cell and electrolysis modes with high round-trip efficiencies offer one such solution. However, questions remain about the stability of the oxygen and fuel electrodes under reversible operation. Here, in this study, single cells with the configuration Ni-YSZ|YSZ|GDC10|NNO-NDC50|NNO are operated by reversible cycling under potentiostatic conditions. Test conditions are chosen to be representative of average stack conditions that are likely to be encountered during operation of a stack constructed of such cells. The results of reversible cycling over 500 h (21 cycles) are compared with operating the cells under potentiostatic conditions in the electrolysis-only mode (i.e., without cycling). Voltage-current density (DC), AC complex impedance spectroscopy, distribution of relaxation times (DRT) analysis, and scanning electron microscopy (SEM) indicate excellent reversibility and stability of the neodymium nickelate-based oxygen electrodes in both electrolysis and reversible cycling modes. Degradation behavior is attributed to the loss and coarsening of connected Ni particles in the fuel electrode, particularly in the active layer. However, reversible operation mitigates this degradation compared to operation in the electrolysis-only (SOEC-only) mode.

25 ENERGY STORAGE↗

DOE OSTI2023

Chromium Poisoning Mitigation Strategy in Strontium-Doped Lanthanum Manganite-Based Air Electrodes in Solid Oxide Fuel Cells

Abstract Chromium poisoning of the air electrode remains an obstacle to the long-term performance of solid oxide fuel cells (SOFCs). In Sr-doped LaMnO3 (LSM) air electrodes, the poisoning process results in two types of deposits, chromium oxide (Cr2O3), and Mn, Cr spinel (MnCr2O4). The former forms electrochemically and the latter forms via a chemical reaction. By applying a small anodic reverse bias, Cr2O3 deposits can be removed because their formation is electrochemical in nature. However, MnCr2O4 deposits remain because their formation is chemical, rather than electrochemical, in nature. In situ chemical decomposition of the Mn, Cr spinel was investigated as an alternate removal method as thermodynamics supports its decomposition into constituent oxides below ∼540 °C in pure oxygen. The spinel decomposition process was characterized using thermogravimetric and X-ray diffraction analyses. The experimentally determined rate of spinel decomposition was undetectable (very slow) with isolated MnCr2O4 powders. The addition of 10 mol% gadolinia doped ceria (GDC) and silver powders significantly increased the rate of decomposition. However, the rate is limited by the diffusion of oxygen through the decomposed oxide layer. Although one strategy may be the addition of GDC and silver to the LSM air electrode to enhance spinel decomposition, the more effective mitigation strategy would be to prevent the formation of MnCr2O4 spinel in the first place through the removal of the reactants: Cr2O3 via electrochemical cleaning and mobile Mn ions in the zirconia electrolyte by incorporating a diffusion barrier layer such as GDC between the air electrode and electrolyte.

Electrochemistry↗