NASA NTRS1991

Micro-mechanical analysis of damage growth and fracture in discontinuous fiber reinforced metal matrix composites

An experimental verification is presented for a new two parameter fracture model based on the equivalent remote biaxial stresses (ERBS). A detailed comparison is made between the new theory and the constant K(sub IC) approach of linear elastic fracture mechanics (LEFM). Fracture is predicted through a failure curve representing the change in a variable fracture toughness K(sub IC) with the ERBS ratio B(sub E). The nonsingular term (T) in the series expansion of the near crack-tip transverse stress is included in the model. Experimental results for polymethyl methacrylate (PPMA) show that the theory can account for the effects of geometry on fracture toughness as well as indicate the initiation of crack branching. It is shown that the new criterion predicts failure for PMMA with a 95 percent confidence zone which is nearly three times smaller than that of the LEFM K(sub IC) approach.

Goree, James G.↗

NASA NTRS1991

The semi-infinite strip problem in the mechanics of composite materials

Many problems, ranging from interface-fiber fracture to determining the strength of fiber-matrix interfaces in composites, can be greatly assisted by a complete understanding of the boundary value problem of a semi-infinite strip. The specific boundary value problem of a semi-infinite strip with symmetric tractions on the transverse edges and normal loads on the end is investigated in the present study. The nature of the singular behavior in the slope of the end vertical displacement at the corner points is found. An asymptotic analysis of the solution shows that, depending on the nature of the applied stresses in the vicinity of the corner points, the singularity in the slope of the end vertical displacement may either be a power or logarithmic type, both, or not exist at all. Illustrative examples, for which exact or numerical results are known, are given. Numerical procedures are also given. The direct application of the results of the paper are illustrated for several problems in the mechanics of composite materials.

Kaw, Autar K.↗

NASA NTRS1990

Micro-mechanical analysis of damage growth and fracture in discontinuous fiber reinforced metal matrix composites

The near-crack-tip stresses in any planar coupon of arbitrary geometry subjected to mode 1 loading may be equated to those in an infinite center-cracked panel subjected to the appropriate equivalent remote biaxial stresses (ERBS). Since this process can be done for all such mode 1 coupons, attention may be focused on the behavior of the equivalent infinite cracked panel. To calculate the ERBS, the constant term in the series expansion of the crack-tip stress must be retained. It is proposed that the ERBS may be used quantitatively to explain different fracture phenomena such as crack branching.

Goree, James G.↗

NASA NTRS1987

Damage growth in composite laminates with interleaves

The influence of placing interleaves between fiber reinforced plies in multilayered composite laminates is investigated. The geometry of the composite is idealized as two dimensional, isotropic, linearly elastic media made of a damaged layer bonded between two half planes and separated by thin interleaves of low extensional and shear moduli. The damage in the layer is taken in the form of a symmetric crack perpendicular to the interface and may extend up to the interface. The case of an H-shaped crack in the form of a broken layer with delamination along the interface is also analyzed. The interleaves are modeled as distributed shear and tension springs. Fourier integral transform techniques are used to develop solutions in terms of singular integral equations. An asymptotic analysis of the integral equations based on Muskhelishvili's techniques reveals logarithmically singular axial stresses in the half plane at the crack tips for the broken layer. For the H shaped crack, similar singularities are found to exist in the axial stresses at the interface crack tips in the layer and the half plane. The solution of the equations is found numerically for the stresses and displacements by using the Hadamard's concept of direct differentiation of Cauchy integrals as well as Gaussian integration techniques.

Goree, James G.↗

NASA NTRS1987

Experimental evaluation of longitudinal splitting in unidirectional composites

An experimental study was conducted to determine the fracture behavior of centernotched, unidirectional graphite/epoxy laminates when subjected to tensile loading. The actual behavior is compared to the behavior predicted by a mathematical model based on classical shear-lag assumptions. Experimental results show the fracture behavior to consist of two modes of longitudinal matrix splitting. After split initiation, a region of slow, stable split growth occurs. This is followed by a distinct transition into a rapid split growth region. However, the shear-lag model predicts a single region of rapid longitudinal split growth behavior with unbounded splitting occurring after approximately a ten percent increase in the applied stress over the split initiation stress. It is therefore concluded that the classical shear-lag model does not accurately predict the complete longitudinal split growth behavior in a brittle matrix composite. This shortcoming in the model and some results obtained from related elasticity solutions are discussed and it is suggested that the slow, stable split growth region is likely dominated by transverse matrix normal stresses which are not accounted for in the classical shear-lag model.

Wolla, Jeffrey M.↗

NASA NTRS1987

Damage growth in composite laminates with interleaves

The influence of interleaves on the fracture behavior of laminated composites is investigated. The geometry of the composite consists of a cracked layer, bonded between two half-planes, which is separated by thin, low modulus, interleaves. The interleaves are modeled as uncoupled tension and shear springs. A stress analysis is carried out for a crack which may grow up to and spread along the interface. Integral transform techniques are used to develop the solution in terms of singular integral equations. An asymptotic analysis reveals logarithmic singularities in the critical stresses for the case of a broken layer. The equations are solved numerically and the effect of damage on critical stresses is studied. Initial results indicate that the interleaf gives a significant reduction in stresses in the adjacent regions and, if properly selected, should result in a more damage tolerant laminate.

Goree, James G.↗

NASA NTRS1985

Fracture and crack growth in orthotropic laminates

A mathematical model based on the classical shear-lag assumptions is used to study the residual strength and fracture behavior of composite laminates with symmetrically placed buffer strips. The laminate is loaded by a uniform remote longitudinal tensile strain and has initial damage in the form of a transverse crack in the parent laminate between buffer strips. The crack growth behavior as a function of material properties, number of buffer-strip plies, spacing, width of buffer strips, longitudinal matrix splitting, and debonding at the interface is studied. Buffer-strip laminates are shown to arrest fracture and increase the residual strengths significantly over those of one material laminates, with S-glass being a more effective buffer strip material than Kevlar in increasing the damage tolerance of graphite/epoxy panels. For a typical graphite/epoxy laminate with S-glass buffer-strips, the residual strength is about 2.4 times the residual strength of an all graphite/epoxy panel with the same crack length. Approximately 50% of this increase is due to the S-glass/epoxy buffer-strips, 40% due to longitudinal splitting of the buffer strip interface and 10% due to bonding.

Goree, James G.↗