3 records

NASA NTRS1981

Recrystallization of polycrystalline silicon

Optical metallography is used to investigate the recrystallization properties of polycrystalline semiconductor-grade silicon. It is found that polycrystalline silicon recrystallizes at 1380 C in relatively short times, provided that the prior deformation is greater than 30%. For a prior deformation of about 40%, the recrystallization process is essentially complete in about 30 minutes. Silicon recrystallizes at a substantially slower rate than metals at equivalent homologous temperatures. The recrystallized grain size is insensitive to the amount of prestrain for strains in the range of 10-50%.

Lall, C.↗

NASA NTRS1978

Hot forming of silicon sheet, silicon sheet growth development for the large area silicon sheet task of the low cost silicon solar array project

The hot workability of polycrystalline silicon was studied. Uniaxail stress-strain curves are given for strain rates in the range of .0001 to .1/sec and temperatures from 1100 to 1380 C. At the highest strain rates at 1380 C axial strains in excess of 20% were easily obtainable without cracking. After deformations of 36%, recrystallization was completed within 0.1 hr at 1380 C. When the recrystallization was complete, there was still a small volume fraction of unrecyrstallized material which appeared very stable and may degrade the electronic properties of the bulk materials. Texture measurements showed that the as-produced vapor deposited polycrystalline rods have a 110 fiber texture with the 110 direction parallel to the growth direction and no preferred orientation about this axis. Upon axial compression perpendicular to the growth direction, the former 110 fiber axis changed to 111 and the compression axis became 110 . Recrystallization changed the texture to 110 along the former fiber axis and to 100 along the compression axis.

Graham, C. D., Jr.↗

NASA NTRS1976

Experiments to evaluate high-temperature rolling as a low-cost process for silicon solar cells

Mechanical rolling (a process used in industry for producing large quantities of metallic sheet and strip) has been suggested for the rapid low-cost manufacture of silicon sheet to be used for photovoltaic power generation equipment, such as solar arrays. The advantages of rolling include: high rates of production, wide sheets as products, good control of dimension, and (in the case of solar grade silicon) minimal development of impurities. Experiments have been performed using high-temperature, high-speed compression of polycrystalline silicon cylinders. Metallography and X-ray diffraction techniques have been used to examine the samples both before and after compression, and a model process has been designed to evaluate the technical practicality and economic feasibility of the method.

Noel, G. T.↗