Tribological behavior of hybrid Aluminum-TiB 2 metal matrix composites for brake rotor applications

Here, this research investigates the feasibility of hybrid aluminum metal matrix composites (MMC) incorporating TiB 2 particles for brake rotor applications. The composites were produced by incorporating both in-situ, submicron-sized TiB 2 particles and regular micron-sized TiB 2 powders via stir and squeeze casting techniques into A206 aluminum alloy matrix. Systematic adjustments in the fractions of in-situ and ex-situ TiB 2 particles were conducted to evaluate their impact on wear behavior and mechanisms. Combination of both particle types allowed composites with up to 10 vol% of reinforcements. Composites with higher proportions of ex-situ particles demonstrated increased wear resistance compared to those solely composed of in-situ particles, control specimens without TiB 2 , and conventional cast iron counterparts. The lowest wear rate for the hybrid composites sliding against phenolic brake pads was 1.1 × 10 -5 mm 3 /Nm, signifying a 3-fold reduction relative to cast iron sliding against the same pads. Wear analysis elucidated distinctive mechanisms within the hybrid composites, characterized by mild fragmented abrasive wear, adhesive wear, and plastic deformation, accompanied by the formation of an intermixed tribo-oxide layer.

42 ENGINEERING↗
DOE OSTI2024

Friction stir processing: A thermomechanical processing tool for high pressure die cast Al-alloys for vehicle light-weighting

This study uses friction stir processing (FSP) for thermomechanical processing of high-pressure die-casting (HPDC) to modify microstructure and improve mechanical properties. FSP is carried out on two different HPDC aluminum alloys: (a) general-purpose, high-iron, HPDC A380 alloy and (b) premium quality, low-iron HPDC Aural-5 alloy in thin wall, flat plate geometry. Subsequent mechanical testing shows ~30 % and ~65 % enhancement in yield strength and tensile ductility. In addition, FSP leads to ~10 times improvement in fatigue life for A380 alloy and ~70 % improvement in fracture toughness for Aural-5 alloy. These findings emphasize the capability of FSP to modify the microstructure of HPDC Al-alloys-based structural components so that they can demonstrate a good combination of strength, ductility, fracture toughness, and high fatigue properties for long-term durability and reliability.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Friction stir processing on a strontium modified, thin-wall, vacuum-assisted high-pressure die-cast Aural-5 alloy to improve tensile and fatigue performance

Here, this study explores the application of friction stir processing (FSP) to enhance the material properties of Sr-modified Aural-5 alloy, with a focus on improved tensile and fatigue properties. Aural-5 is a well-known vacuum-assisted high-pressure die-cast (HPDC) Al-Si7-Mg alloy used in the automotive industry to reduce vehicle weight, enhance fuel efficiency, and lower carbon emissions. This alloy modifies its material chemistry with Sr for fine fibrous networks of eutectic silicon and manganese (Mn) to reduce die soldering. It has significantly less iron (Fe) content resulting in the elimination of detrimental needle-shaped Fe-bearing ß-phase intermetallic and improving ductility. The initial microstructure of as-received HPDC Aural-5 exhibits shrinkage porosity in the middle section, a dendritic microstructure with fibrous Al-Si eutectic colonies, a shear-band structure beneath the die-wall, large dendritic externally solidified crystals (ESCs), needle-shaped Mg 2 Si phase and significant second-phase particulates. Some of those microstructural features, such as porosity, ESCs, needle-shaped Mg 2 Si phase, and large second-phase particles, serve as initiation sites for cracks under mechanical loading, resulting in adverse effects on tensile properties, particularly ductility. FSP effectively transforms the microstructure into a wrought configuration with uniform particle distribution by eliminating porosity and disintegrating dendrites, eutectic colonies, ESCs, second-phase particles, and shear-band structures. FSP-driven microstructure modification enhances yield strength and tensile ductility by ~30% and ~35%, respectively. The fatigue life of the material in a bending mode configuration (stress ratio R = 0.1) after FSP exhibits enhancements ranging from 2.0 to 3.9 times that of the original HPDC Aural-5 alloy, depending on the applied stress level.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Exceptional strength and wear resistance in an AA7075/TiB 2 composite fabricated via friction consolidation

The friction consolidation method successfully reinforced aluminum 7075 alloy (AA7075) with high-volume fractions (12 and 24 vol%) of titanium diboride (TiB 2 ) by high pressure and severe plastic deformation at elevated temperatures. The consolidated AMCs have a uniform dispersion of submicron- and micron-sized TiB 2 particles in the AA7075 matrix, with significant refinement of the matrix grain size and the particles. The addition of TiB 2 significantly increases hardness by up to 50 %, Young’s modulus by up to 62 %, and ultimate tensile strength by up to 28 % to 672 MPa, while reducing ductility by 80 %. Wear resistance of 7075/24 vol% TiB 2 improves seven-fold compared to baseline, making it comparable to that of carburized steels. Microstructure-based finite element modeling provided a theoretical strength limit of ~730 MPa for the composites and indicated that high triaxiality in conjunction with severe equivalent plastic strain in a narrow area between the TiB 2 particles led to early fracture initiations, limiting the ductility.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Impact of Backing Plate and Thermal Boundary Conditions for High-Speed Friction Stir Welding of 25-mm Thick Aluminum Alloy 7175-T79

Here this study demonstrates high-speed (150 mm/min) single pass friction stir butt joining of 25 mm thick aluminum alloy 7175-T79. To understand the impact of quenching and cooling rate on process responses, joint strength, and grain size distributions across the weld thickness, we performed a series of friction stir welding (FSW) trials in air and with a trailing water spray using steel and composite backing plates (BP). Welds made in air and trailing water spray exhibit significantly different hardness distributions across the nugget, heat affected zone (HAZ), and HAZ minimum hardness as evidenced by detailed microhardness mapping. The effect of trailing water spray (TWS) on joint efficiency overshadows the influence of BP composition due to the vastly different contribution to quenching. TWS also resulted in a multifaceted effect on FSW such as lowering processing temperature, increasing X and Z forces while lowering Y force, and narrow heat affecting zone. Finally, digital image correlation (DIC)-based fracture mode analysis and grain size measurements correlate with the hardness distribution.

42 ENGINEERING↗