Grant, N. J.

Publications and source records attributed to Grant, N. J..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1986

Metal powder production by gas atomization

The confined liquid, gas-atomization process was investigated. Results from a two-dimensional water model showed the importance of atomization pressure, as well as delivery tube and atomizer design. The atomization process at the tip of the delivery tube was photographed. Results from the atomization of a modified 7075 aluminum alloy yielded up to 60 wt pct. powders that were finer than 45 microns in diameter. Two different atomizer designs were evaluated. The amount of fine powders produced was correlated to a calculated gas-power term. An optimal gas-power value existed for maximized fine powder production. Atomization at gas-power greater than or less than this optimal value produced coarser powders.

Ting, E. Y.↗
NASA NTRS1985

The Role of Entrained Surface Oxides in RS-PM Aluminum Alloys on Resultant Structures and Properties

The RS-PM aluminum alloys which show less than anticipated toughness properties were studied. After eliminating negative variables such as sodium and potassium in lithium containing alloys, hydrogen in all Al alloys, and trapped impurities from the atomization processing the data pointed to fine oxides, as the primary cause of poor toughness properties. The oxide content of aluminum powders increases with: decreasing powder size, deviations from spherical powder shapes, exposure to moist atmospheres either during atomization or in subsequent powder handling, and alloy compositions which contain significant amounts of lithium, magnesium, cerium, and other reactive elements.

Grant, N. J.↗
NASA NTRS1982

The structure and properties of rapidly solidified high alloy aluminum materials

A series of 2024 type aluminum alloys modified by additions of 1 to 2% Li were studied to determine the role of the Cu:Li and the (Cu + Mg):Li ratios on resultant strength, ductility, notch-tensile behavior, and crack propagation rates. Ultrasonically gas atomized powders with quench rates of 10 to 100 thousand degrees/s were atomized in an argon atmosphere, producing yields of powder such that almost 100% was finer than 250 microns. The powders are free of gases and porosity, are quite spherical, have few satellites (adhering fine powder particles) and are of uniform microstructure. Strength properties are such that yield strength is 20% greater than for lithium-free 2024 ingot alloy, tensile strength is 10% greater than that of 2024 ingot material, and ductilities are comparable. In terms of specific strength and specific modulus, these RS 2024-Li alloys are significantly better than IM 2024.

Grant, N. J.↗
NASA NTRS1982

Powder and particulate production of metallic alloys

Developments of particulate metallurgy of alloyed materials where the final products is a fully dense body are discussed. Particulates are defined as powders, flakes, foils, silvers, ribbons and strip. Because rapid solidification is an important factor in particulate metallurgy, all of the particulates must have at least one dimension which is very fine, sometimes as fine as 10 to 50 microns, but move typically up to several hundred microns, provided that the dimension permits a minimum solidification rate of at least 100 K/s.

Grant, N. J.↗
NASA NTRS1982

Rapid solidification of metallic particulates

In order to maximize the heat transfer coefficient the most important variable in rapid solidification is the powder particle size. The finer the particle size, the higher the solidification rate. Efforts to decrease the particle size diameter offer the greatest payoff in attained quench rate. The velocity of the liquid droplet in the atmosphere is the second most important variable. Unfortunately the choices of gas atmospheres are sharply limited both because of conductivity and cost. Nitrogen and argon stand out as the preferred gases, nitrogen where reactions are unimportant and argon where reaction with nitrogen may be important. In gas atomization, helium offers up to an order of magnitude increase in solidification rate over argon and nitrogen. By contrast, atomization in vacuum drops the quench rate several orders of magnitude.

Grant, N. J.↗
NASA NTRS1982

Rapid solidification of metallic particulates

In order to maximize the heat transfer coefficient the most important variable in rapid solidification is the powder particle size. The finer the particle size, the higher the solidification rate. Efforts to decrease the particle size diameter offer the greatest payoff in attained quench rate. The velocity of the liquid droplet in the atmosphere is the second most important variable. Unfortunately the choices of gas atmospheres are sharply limited both because of conductivity and cost. Nitrogen and argon stand out as the preferred gases, nitrogen where reactions are unimportant and argon where reaction with nitrogen may be important. In gas atomization, helium offers up to an order of magnitude increase in solidification rate over argon and nitrogen. By contrast, atomization in vacuum drops the quench rate several orders of magnitude. Previously announced in STAR as N82-26433

Grant, N. J.↗
NASA NTRS1978

Applications of metastable microcrystalline alloys

The mechanical properties of rapidly quenched superalloys, aluminum alloys, stainless steels, and titanium alloys are briefly reviewed. Studies on the materials are mentioned, and the superplasticity properties of the alloys are highlighted.

Grant, N. J.↗
NASA NTRS1977

Structure-property relationships in oxide-dispersed iron-beryllia alloys

Two BeO dispersed iron alloys containing about 2.5 and 5.5 v/o dispersoid were produced by attritting, internally oxidizing, and extruding dilute, prealloyed Fe-Be powders. As-extruded alloys were given various thermomechanical treatments involving room temperature swaging and annealing above and below the allotropic transformation temperature. The elevated temperature rupture strengths were measured and correlated with changes in structure; strengthening trends were examined in the light of proposed models for such strengthening. The results obtained showed that the elevated temperature strength was determined by the oxide interparticle spacing (IPS) in recrystallized material and IPS as well as prior deformation in swaged specimens. In fact, a parametric correlation was found between rupture strength values in the longitudinal direction with prestrain during swaging. The overall pattern in strength and microstructural observations were more consistent with a strength-stored energy (substructure) dependence than a strength-grain shape (grain aspect ratio) relation.

Wolf, S.↗
NASA NTRS1976

Properties of splat-quenched 7075 aluminum type alloys

The 7075 alloy belonging to the Al-Zn-Mg-Cu system, prepared by powder metallurgy techniques, was used in a study of alloys prepared from splat-quenched foils consolidated into bar material by hot extrusion. Ni and Fe were included in one alloy specimen, producing a fine dispersion of FeAl3 type particles which added to the strength of the aged alloy but did not coarsen upon heat treatment. Fine oxide films showing up on air-splatted foils induce finely dispersed oxide stringers (if the foils are not hot-worked subsequently) which in turn promote axial cracking (but longitudinal tensile strength is not seriously impaired). Splatting in a protective atmosphere, or thermomechanical processing, is recommended to compensate for this.

Durand, J. P. H. A.↗
NASA NTRS1975

Precipitation of silicon from splat-cooled Al-Si alloys

Splat cooled Al-Si solid solutions with 1 to 11 at.% Si were prepared and their precipitation kinetics were studied by transmission electron microscopy. The time required for appearance of particles visible at a magnification of 35,000 times was determined at temperatures between 248 K and 573 K. The resulting Arrhenius plots yielded activation energies ranging from 55 to 40 plus or minus 2kJ/mol over the composition range. Precipitate densities were higher and denuded zones of 100 to 150 nm were narrower than in comparable solid quenched samples. The activation energies are explained in terms of excess point defect concentrations.

Matyja, H.↗
NASA NTRS1975

Structure-property relationships in thermomechanically treated beryllia dispersed nickel alloys

BeO dispersed nickel alloys, produced by powder metallurgy techniques, were studied extensively in stress rupture at 815, 982, and 1093 C (1088, 1255, and 1366 K) and by transmission electron microscopy. The alloys were subjected to a variety of thermomechanical treatments (TMT) to determine the benefits of TMT on properties. It is shown that the use of intermediate annealing treatments after 10 pct reduction steps is highly beneficial on both low and high temperature properties. It is indicated that the high temperature strength is not primarily dependent on the grain aspect ratio or texture but depends strongly on the dislocation density and distribution of dislocations in a stable substructure which is pinned by the fine oxide dispersion.

Grewal, M. S.↗
NASA NTRS1974

Structure and properties of a splat cooled 2024 aluminum alloy

In the investigation the alloy was melted, heated to 750 C, and atomized into fine droplets. The droplets were rapidly quenched against a heavy copper disk rotating at 1725 rpm. The resultant splat cooled flakes were screened. Three flake sizes were finally separated. Flakes of each size were separately processed. The characteristics of the splat cooling process and the properties of the obtained products are discussed. Splat cooling against a metallic substrate permits cooling rates up to about 1,000,000 deg C/sec. Increases in yield strength and tensile strength of 14 to 19% are observed for the splat products. Other improvements are connected with increases in fatigue life and stress rupture performance.

Lebo, M.↗
NASA NTRS1974

Liquid-metal atomization for hot working preforms

Rapid quenching of a liquid metal by atomization or splat cooling overcomes the major limitation of most solidification processes, namely, the segregation of alloying elements, impurities, and constituent phases. The cooling rates of different atomizing processes are related to the dendrite arm spacings and to the microstructure of the atomized powders. The increased solubility limits and the formation of metastable compounds in splat-cooled alloys are discussed. Consolidation of the powders by hot isostatic compaction, hot extrusion, or hot forging and rolling processes yields billets with properties equivalent to or better than those of the wrought alloys. The application of this powder processing technology to high-performance alloys is reviewed.

Grant, N. J.↗
NASA NTRS1973

Thoria stability in TD-NiCr at high temperatures in the presence of chromium in solution.

Study of the influence of chromium in solid solution on the coarsening of ThO2 in TD-NiCr. Comparisons were made of ThO2 coarsening in chromium-free TD-Ni and in TD-NiCr, which is known to be low in Cr2O3 as a contaminant. The results of these comparisons indicate that the presence of 20% Cr in solid solution in a nickel-base alloy does not lead to a more rapid coarsening of ThO2 at temperatures of at least 2462 deg F (1350 deg C).

Dalal, H.↗
NASA NTRS1972

Study of a splat cooled Cu-Zr-noncrystalline phase.

By rapid quenching from the melt, using the splat forming gun technique, a noncrystalline phase has been obtained in a Cu-Zr alloy containing 60 at. % Cu. Upon heating, rapid crystallization of the samples takes place at 477 C with a heat release of about 700 cal per mol. The variation of the electrical resistivity of the samples with temperature confirms the transformation. Very high resolution electron microscopy studies of the structural changes of the samples upon heating are presented and show the gradual crystallization of the amorphous structure.

Revcolevschi, A.↗