Engineering topics
Gray, Lucas
Publications and source records attributed to Gray, Lucas.
Advanced Warning for Intervention in Li-ion Batteries During Abusive Conditions.
Abstract not provided.
Investigating the Effects of Lithium Deposition on the Abuse Response of Lithium-Ion Batteries
Li deposition at the graphitic anode is widely reported in literature as one of the leading causes of capacity fade in lithium-ion batteries (LIBs). Previous literature has linked Li deposition resulting from low-temperature ageing to diminished safety characteristics, however no current research has probed the effects of Li deposition on the abuse response of well-characterized cells. Using overtemperature testing, a relationship between increased concentrations of Li deposition and exacerbated abuse response in 1 Ah pouch cells has been established. A novel Li deposition technique is also investigated, where cells with n:p < 1 (anode-limiting) have been cycled at a high rate to exploit Li + diffusion limitations at the anode. Scanning Electron Microscopy of harvested anodes indicates substantial Li deposition in low n:p cells after 20 cycles, with intricate networks of Li(s) deposits which hinder Li + intercalation/deintercalation. Peak broadening and decreased amplitude of differential capacity plots further validates a loss of lithium inventory to Li + dissolution, and Powder X-ray Diffraction indicates Li + intercalation with staging in anode interstitial sites as the extent of Li deposition increases. A cradle-to-grave approach is leveraged on cell fabrication and testing to eliminate uncertainty involving the effects of cell additives on Li deposition and other degradation mechanisms.
Research three-dimensional hierarchical graphite architectures for anodes for fast charging
With current lithium ion batteries optimized for performance under relatively low charge rate conditions, implementation of XFC has been hindered by drawbacks including Li plating, kinetic polarization, and heat dissipation. This project will utilize model-informed design of 3-D hierarchical electrodes to tune key XFCrelated variables like 1) bulk porosity/tortuosity 2) vertical pore diameter, spacing, and lattice 3) crystallographic orientation of graphite particles relative to exposed surfaces 4) interfacial chemistry of the graphite surfaces through "artificial sEr' formation using ALD 5) current collector surface roughness (aspect ratio, roughness factor, etc.). A key aspect of implementing novel electrodes is characterizing them in relevant settings. For this project, ultimately led out of University of Michigan by Neil Dasgupta, that includes both coin cell and 2+ Ah pouch cell testing, as well as comparison testing against baselines. Sandia National Labs will be conducting detailed cell characterization on iterative versions/improvements of the model-based hierarchical electrodes, as well as COTS cells for baseline comparisons. Key metrics include performance under fast charge conditions, as well as the absence or degree of lithium plating. Sandia will use their unique high precision cycling and rapid EIS capabilities to accurately characterize performance and any lithium plating during 6C charging and beyond, coupling electrochemical observations with cell teardown. Sandia will also design custom fixturing to cool cells during rapid charge, to decouple any kinetic effects brought about by cell heating and allow comparisons between different cells and charge rates. Using these techniques, Sandia will assess HOH electrodes from the University of Michigan, as well as aiding in iterative model and electrode design.