Grimes, H. H.

Publications and source records attributed to Grimes, H. H..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1983

Thermal degradation of the tensile properties of undirectionally reinforced FP-Al2O3/EZ 33 magnesium composites

The effects of isothermal and cyclic exposure on the room temperature axial and transverse tensile strength and dynamic flexural modulus of 35 volume percent and 55 volume percent FP-Al203/EZ 33 magnesium composites were studied. The composite specimens were continuously heated in a sand bath maintained at 350 C for up to 150 hours or thermally cycled between 50 and 250 C or 50 and 350 C for up to 3000 cycles. Each thermal cycle lasted for a total of six minutes with a hold time of two minutes at the maximum temperature. Results indicate no significant loss in the room temperature axial tensile strength and dynamic flexural modulus of composites thermally cycled between 50 and 250 C or of composites isothermally heated at 350 C for up to 150 hours from the strength and modulus data for the untreated, as-fabricated composites. In contrast, thermal cycling between 50 and 350 C caused considerable loss in both room temperature strength and modulus. Fractographic analysis and measurement of composite transverse strength and matrix hardness of thermally cycled and isothermally heated composites indicated matrix softening and fiber/matrix debonding due to void growth at the interface and matrix cracking as the likely causes of the strength and modulus loss behavior. Previously announced in STAR as N82-21260

Bhatt, R.T.↗
NASA NTRS1982

Fatigue behavior of SiC reinforced Ti/6Al-4V/ at 650 C

Axial, low cycle fatigue properties of 25 and 44 fiber vol pct SiC/Ti(6Al-4V) composites, measured at 650 C, were compared with the fatigue properties of unreinforced Ti(6Al-4V) at the same temperature. A prior study of the fatigue behavior of this composite system at room temperature indicated that the SiC fiber reinforcement did not provide the anticipated improvement of fatigue resistance of this alloy. At 650 C, the composite fatigue properties degraded somewhat from those at room temperature. However, these properties degraded more for the unreinforced matrix at 650 C with the result that the composite fatigue strength was two to three times the fatigue strength of the matrix alloy. The reasons for this reversal are discussed in terms of crack initiation at broken fibers and residual matrix stresses.

Bhatt, R. T.↗
NASA NTRS1982

Thermal degradation of the tensile properties of undirectionally reinforced FP-AI203/EZ 33 magnesium composites

The effects of isothermal and cyclic exposure on the room temperature axial and transverse tensile strength and dynamic flexural modulus of 35 volume percent and 55 volume percent FP-Al2O3/EZ 33 magnesium composites were studied. The composite specimens were continuously heated in a sand bath maintained at 350 C for up to 150 hours or thermally cycled between 50 and 250 C or 50 and 350 C for up to 3000 cycles. Each thermal cycle lasted for a total of six minutes with a hold time of two minutes at the maximum temperature. Results indicate to significant loss in the room temperature axial tensile strength and dynamic flexural modulus of composites thermally cycled between 50 and 250 C or of composites isothermally heated at 350 C for up to 150 hours from the strength and modulus data for the untreated, as fabricated composites. In contrast, thermal cycling between 50 and 350 C caused considerable loss in both room temperature strength and modulus. Fractographic analysis and measurement of composite transverse strength and matrix hardness of thermally cycled and isothermally heated composites indicated matrix softening and fiber/matrix debonding due to void growth at the interface and matrix cracking as the likely causes of the strength and modulus loss behavior.

Bhatt, R. T.↗
NASA NTRS1979

Fatigue behavior of SiC reinforced titanium composites

The low cycle axial fatigue properties of 25 and 44 fiber volume percent SiC/Ti(6Al-4V) composites were measured at room temperature and at 650 C. At room temperature, the S-N curves for the composites showed no anticipated improvement over bulk matrix behavior. Although axial and transverse tensile strength results suggest a degradation in SiC fiber strength during composite fabrication, it appears that the poor fatigue life of the composites was caused by a reduced fatigue resistance of the reinforced Ti(6Al-4V) matrix. Microstructural studies indicate that the reduced matrix behavior was due, in part, to the presence of flawed and fractured fibers created near the specimen surfaces by preparation techniques. Another possible contributing factor is the large residual tensile stresses that can exist in fiber-reinforced matrices. These effects, as well as the effects of fatigue testing at high temperature, are discussed.

Bhatt, R. T.↗
NASA NTRS1979

Fatigue behavior of SiC reinforced titanium composites

The low cycle axial fatigue properties of 25 and 44 fiber volume percent SiC/Ti(6Al-4V) composites were measured at room temperature and at 650 deg C. The S-N curves for the composites showed no anticipated improvement over bulk matrix behavior at room temperature. Although axial and transverse tensile strength results suggest a degradation in SiC fiber strength during composite fabrication, it appears that the poor fatigue life of the composites was caused by a reduced fatigue resistance of the reinforced Ti(6Al-4V) matrix. The reduced matrix behavior was due, to the presence of flawed and fractured fibers created near the specimen surfaces by preparation techniques and to the large residual tensile stresses that can exist in fiber reinforced matrices. The effects of fatigue testing at high temperature are discussed.

Bhatt, R. T.↗
NASA NTRS1978

Ultra-high-strength boron fibers

Boron-on-tungsten fibers with tensile strength and strain-to-failure values increased by fifty percent over commercial grades are produced by controlled chemical-etching process. Improved fibers have potential applications as lightweight composites in ground vehicles, spacecraft, and rotors for energy storage.

Behrendt, D. R.↗
NASA NTRS1978

Thermal environment effects on strength and impact properties of boron-aluminum composites

A systematic study was conducted regarding the degradation of fracture strength and impact energy in commercial B-Al composites in both static and cyclic thermal environments. The composites used in the study contained approximately 50 vol % boron fibers, unidirectionally aligned in either a 6061 Al or 1100 Al matrix. The tensile strengths of the composites after 3000 thermal cycles as a function of upper cycle temperature are presented in graphs. The temperature at which the strengths of 6061 Al matrix, B-Al composites were significantly degraded after 3000 cycles was noticeably higher than that for the 1100 Al matrix composites. Static heating at 420 C resulted in no significant strength degradation for the 6061 Al matrix composites. In the case of 1100 matrix composites, some degradation was observed at 420 C but markedly less than in the composites cycled to 420 C.

Grimes, H. H.↗
NASA NTRS1977

Thermal degradation of the tensile strength of unidirectional boron/aluminum composites

The variation of ultimate tensile strength with thermal treatment of B-Al composite materials and of boron fibers chemically removed from these composites is studied systematically in an attempt to determine the mechanism of the resulting strength degradation. The results indicate that thermally cycling of B-Al represents a more severe condition than equivalent time at temperature. Degradation of composite tensile strength from about 1.3 GN/sq m to as low as 0.34 GN/sq m was observed after 3000 cycles to 420 C for 203-micron B-1100 Al composite. In general, the 1100 Al-matrix composites degraded somewhat more than the 6061 matrix material studied. Measurement of fiber strengths confirmed a composite strength loss due to the degradation of fiber strength. Microscopy indicated a highly flawed fiber surface. On the basis of various thermal-cycling studies and electron diffraction analysis, a mechanism is favored in which B reacts with Al, freshly exposed by cold working during cycling, to form AlB2. The nonuniform interface reaction leads to a highly flawed and weakened B fiber.

Grimes, H. H.↗
NASA NTRS1977

Thermal degradation of the tensile strength of unidirectional boron/aluminum composites

The variation of ultimate tensile strength with thermal treatment of B-Al composite materials and of boron fibers chemically removed from these composites in an attempt to determine the mechanism of the resulting strength degradation was studied. Findings indicate that thermally cycling B-Al represents a more severe condition than equivalent time at temperature. Degradation of composite tensile strength from about 1.3 GN/m squared to as low as 0.34 GN/m squared was observed after 3,000 cycles to 420 C for 203 micrometers B-1100 Al composite. In general, the 1100 Al matrix composites degraded somewhat more than the 6061 matrix material studied. Measurement of fiber strengths confirmed a composite strength loss due to the degradation of fiber strength. Microscopy indicated a highly flawed fiber surface.

Grimes, H. H.↗
NASA NTRS1977

Thermal environment effects on strength and impact properties of boron-aluminum composites

Thermal effects on fracture strength and impact energy were studied in 50 volume percent unidirectional composites of 143 and 203 micron boron fibers in 6061 and 1100 aluminum matrices. For 6061 matrix composites, strength was maintained to approximately 400 C in the cyclic tests and higher than 400 C in the static tests. For the 1100 matrix composites, strength degradation appeared near 260 C after cycling and higher than 260 C in static heating. This composite strength degradation is explained by a fiber degradation mechanism resulting from a boron-aluminum interface reaction. The impact energy absorption degraded significantly only above 400 C for both matrix alloys. Thus, while impact loss for the 6061 composite correlates with the fiber strength loss, other energy absorption processes appear to extend the impact resistance of the 1100 matrix composites to temperatures beyond where its strength is degraded. Interrupted impact tests on as-received and thermally cycled composites define the range of load over which the fibers break in the impact event.

Grimes, H. H.↗
NASA NTRS1975

Radiation effects on beta /10.6/ of pure and europium doped KCl

Changes in the optical absorption coefficient as the result of X-ray and electron bombardment of pure monocrystalline and polycrystalline KCl and of divalent europium doped polycrystalline KCl were determined. A constant heat flow calorimetric method was used to measure the optical absorption coefficients. Both 300 kV X-ray irradiation and 2 MeV electron irradiation produced increases in the optical absorption coefficient at room temperature. X-ray irradiation produced more significant changes in pure monocrystalline KCl than equivalent amounts of electron irradiation. Electron irradiation of pure and Eu-doped polycrystalline KCl produced increases in the absorption by as much as a factor of 20 over untreated material. Bleaching of the electron-irradiated doped KCl with 649 millimicron light produced a further increase.

Grimes, H. H.↗
NASA NTRS1975

Radiation effects on beta 10.6 of pure and europium doped KCl

Changes in the optical absorption coefficient as a result of X-ray and electron bombardment of pure KCl (monocrystalline and polycrystalline), and divalent europium doped polycrystalline KCl were determined. The optical absorption coefficients were measured by a constant heat flow calorimetric method. Both 300 KV X-irradiation and 2 MeV electron irradiation produced significant increases in beta 10.6, measured at room temperature. The X-irradiation of pure moncrystalline KCl increased beta 10.6 by 0.005/cm for a 113 MR dose. For an equivalent dose, 2 MeV electrons were found less efficient in changing beta 10.6. However, electron irradiation of pure and Eu-doped polycrystalline KCl produced marked increases in adsorption. Beta increased to over 0.25/cm in Eu-doped material for a 30 x 10 to the 14th power electrons/sq cm dose, a factor of 20 increase over unirradiated material. Moreover, bleaching the electron irradiated doped KCl with 649 m light produced and additional factor of 1.5 increase. These findings will be discussed in light of known defect-center properties in KCl.

Grimes, H. H.↗
NASA NTRS1973

Use of a torsional pendulum as a high-pressure gage and determination of viscosity of helium gas at high pressures

Three torsional crystal parameters were examined for suitability in sensing pressure in gases up to 131 million newtons per square meter. The best parameters were found to be the change in crystal decrement at resonance and the change in crystal electrical resistance at resonance. The change in crystal resonant frequency did not appear to be a reliable pressure measuring parameter. Pure argon and pure helium gases were studied for use as working fluids. Helium functioned better over a wider pressure range. Calibration of the gage also provided a measure of the viscosity-density product of the gas as a function of pressure. These data, together with known extrapolated density data, permitted the determination of the viscosity of helium to 131 million N/square meter.

Maisel, J. E.↗
NASA NTRS1968

Vacancy relaxations in b.c.c. crystals.

Vacancy relaxations in bcc crystals using energy dependence on radial displacements from defect of nearest neighbor sets, discussing crystal size and shape

Grimes, H. H.↗