Groden, Kyle J. | Search NASA

DOE OSTI2020

Probing Active-Site Relocation in Cu/SSZ-13 SCR Catalysts during Hydrothermal Aging by in situ EPR Spectroscopy, Kinetic Studies, and DFT Calculations

Cu/SSZ-13 selective catalytic reduction catalysts display activity loss after mild hydrothermal aging without support degradation or loss of isolated Cu ion content. By applying electron paramagnetic resonance spectroscopy to compare hydrated, dehydrated and NH3-saturated catalysts before and after hydrothermal aging, as well as density functional theory calculations, it is found that hydrothermal aging induces Cu relocation, leading to stronger Cu-support interactions. This is particularly evidenced by ZCuOH conversion to Z2Cu, which leads to the generation of a unique structure with two Cu(II) ions positioned in a double 6-membered ring prism. The Cu(II) ions that do not undergo such dramatic changes also appear to stay closer to framework windows as evidenced by the overall increased anisotropy during EPR measurements. In situ EPR measurements under SCR conditions demonstrate that, in comparison to the fresh catalyst, higher percentages of Cu species stay as Cu(II) in the aged catalyst. This suggests that the reduction half-cycle of the SCR redox, i.e., Cu(II) ? Cu(I), becomes slower for the hydrothermally aged catalyst.

42 ENGINEERING↗

DOE OSTI2020

Accelerated Cu2O Reduction by Single Pt Atoms at the Metal-Oxide Interface§

The reducibility of metal oxides, when serving as the catalyst support or the active sites themselves, plays an important role in heterogeneous catalytic reactions. Here we present an integrated experimental and theoretical study that reveals how the addition of small amounts of atomically dispersed Pt at the metal/oxide interface dramatically enhances the reducibility of a Cu2O thin film by H2. X-ray photoelectron spectroscopy (XPS) and temperature-programmed desorption (TPD) results reveal that upon oxidation, a PtCu single-atom alloy (SAA) surface is covered by a thin Cu2O film and is therefore unable to dissociate H2. Despite this, in situ studies using ambient pressure (AP) XPS reveal that the presence of a small amount of Pt under the oxide layer can, at the single-atom limit, promote the reduction of Cu2O by H2 at room temperature. We build two density functional theory based surface models to better understand these experimental findings: A Cu2O/Cu(111)-like surface oxide layer, known as the ‘29’ oxide, in which Pt is alloyed into the Cu(111) surface as well as a PtCu SAA. Our calculations suggest that the increased activity is due to the presence of atomically dispersed Pt under the surface oxide layer, which weakens the Cu-O bonds in its immediate vicinity, thus making the interface between subsurface Pt and the surface oxide a nucleation site for the formation of metallic Cu. This initial step in the reduction process results in the presence of surface Pt atoms surrounded by metallic Cu patches, and the Pt atoms become active in H2 dissociation, which consequently accelerates the reduction of the oxide layer. This work demonstrates how isolated Pt atoms at the metal/oxide interface of a Cu-based catalyst accelerate the reduction of the oxide and, therefore, helps maintain the active, reduced state of the catalyst under reaction conditions, as is required for the synthesis of methanol from CO2 hydrogenation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗