Groza, M. | Search NASA

NASA NTRS2008

New Scintillator Materials (K2CeBr5) and (Cs2CeBr5)

Cesium cerium bromide (Cs2CeBr5) and potassium cerium bromide (K2CeBr5) are new scintillator materials for X-ray and gamma ray detector applications. Recently halide scintillator materials, such as Ce doped lanthanum bromide has been proved to be very important material for the same purpose. These materials are highly hygroscopic; a search for high light yield non-hygroscopic materials was highly desirable to advance the scintillator technology. In this paper, we are reporting the crystal growth of novel scintillator materials, cesium cerium bromide (Cs2CeBr5) and potassium cerium bromide (K2CeBr5). Crystals were successfully grown from the melt using the vertical Bridgman-Stockbarger technique, in a comparison with the high performance LaBr3 or LaCl3 crystals, cerium based alkali halides crystals, (Cs2CeBr5) and (K2CeBr5) have similar scintillation properties, while being much less hygroscopic. Furthermore, cesium based compounds will not suffer from the self-activity present in potassium and lanthanum compounds. However the Cs2CeBr5 crystals did not grow properly probably due to non-congruent melting or to some phase transition during cooling. Keywords." Scintillator materials; Ce3+; Energy resolution; Light yield; K2CeBr5

Hawrami, R.↗

NASA NTRS2007

Detailed Studies of Pixelated CZT Detectors Grown with the Modified Horizontal Bridgman Method

The detector material Cadmium Zinc Telluride (CZT) achieves excellent spatial resolution and good energy resolution over a broad energy range, several keV up to some MeV. Presently, there are two main methods to grow CZT crystals, the Modified High-Pressure Bridgman (MHB) and the High-Pressure Bridgman (HPB) process. The study presented in this paper is based on MHB CZT substrates from the company Orbotech Medical Solutions Ltd. [Orbotech Medical Solutions Ltd., 10 Plaut St., Park Rabin, P.O. Box 2489, Rehovot, Israel, 76124]. Former studies have shown that high-work-function materials on the cathode side reduce the leakage current and, therefore, improve the energy resolution at lower energies. None of the studies have emphasized on the anode contact material. Therefore, we present in this paper the result of a detailed study in which for the first time the cathode material was kept constant and the anode material was varied. We used four different anode materials: Indium, Titanium, Chromium and Gold, metals with work-functions between 4.1 eV and 5.1 eV. The detector size was 2.0 x 2.0 x 0.5 cu cm with 8 x 8 pixels and a pitch of 2.46 mm. The best performance was achieved with the low-work-function materials Indium and Titanium with energy resolutions of 2.0 keV (at 59 keV) and 1.9 keV (at 122 keV) for Titanium and 2.1 keV (at 59 keV) and 2.9 keV (at 122 keV) for Indium. Taking into account the large pixel pitch of 2.46 mm, these resolutions are very competitive in comparison to those achieved with detectors made of material produced with the more expensive conventional HPB method. We present a detailed comparison of our detector response with 3D simulations. The latter comparisons allow us to determine the mobility-lifetime-products (mu tau-products) for electrons and holes. Finally, we evaluated the temperature dependency of the detector performance and ls-products. For many applications temperature dependence is important, therefore, we extended the scope of our study to temperatures as low as -30 C. There are two important results. The breakdown voltage increases with decreasing temperature, and electron mobility-lifetime-product decreases by about 30% over a range from 20 C to -30 C. The latter effect causes the energy resolution to deteriorate, but the concomitantly increasing breakdown voltage makes it possible to increase the applied bias voltage and restore the full performance

Jung, I.↗