Engineering topics
Publications and source records attributed to Grunthaner, P. J..
Concepts developed in study of SiO2/Si interface applied to analysis of native oxide/GaAs interface. High-resolution X-ray photoelectron spectroscopy (XPS) has been combined with precise chemical-profiling technique and resolution-enhancement methods to study stoichiometry of transitional layer. Results are presented in report now available.
An analytical method based on oxide/substrate intensity ratios is used to deduce the product of the atomic number density and electron mean free path as a function of depth, for the cases of device-quality gate oxides grown on Si substrates and irradiated with zero to 20 eV electrons during in situ X-ray photoelectron spectroscopy. These structures had been thinned stepwise to 25-60 A by means of a wet chemical depth-profiling procedure. Si(3+) species are formed in the Si/SiO2 interface region, and their observation during their relaxation and annihilation is correlated with strained Si-O-Si bonds. The observation of bond of cleavage and bond strain gradients in these samples is used to extend silica devitrification models for the explanation of fixed oxide charge generation and interface states.
Via a systematic study of the correlation between the core and valence level X-ray photoemission spectra, the nature of the chemical bonding and charge redistribution for bulk transition metal silicides has been examined. Particular emphasis is placed on Pt2Si and PtSi. It is observed that the strength of the metal (d)-silicon (p) interaction increases in the order Ni2Si, Pd2Si, Pt2Si. It is also observed that both the metal and silicon core lines shift to higher binding energy as the silicides are formed. The notion of charge redistribution for metallic bonds is invoked to explain these data.
The effect of implanted oxygen impurities on the Ni/Ni2Si interface is investigated using X-ray photoelectron spectroscopy, He-4(+) backscattering and O(d, alpha)-16 N-14 nuclear reactions. Oxygen dosages corresponding to concentrations of 1, 2, and 3 atomic percent were implanted into Ni films evaporated on Si substrates. The oxygen, nickel, and silicon core lines were monitored as a function of time during in situ growth of the Ni silicide to determine the chemical nature of the diffusion barrier which forms in the presence of oxygen impurities. Analysis of the Ni, Si, and O core levels demonstrates that the formation of SiO2 is responsible for the Ni diffusion barrier rather than Ni oxide or mixed oxides, such as Ni2SiO4. It is determined that 2.2 x 10 to the 16th O/qu cm is sufficient to prevent Ni diffusion under UHV annealing conditions.
The valence level spectra of the Ni/Si and Pd/Si systems have been investigated using high resolution X-ray photoelectron spectroscopy. Temperature dependence studies for Ni deposited on thin thermal SiO2 demonstrate the importance of metal aggregation effects in the interpretation of binding energies as chemical shifts. Temperature studies for the Ni/Si system indicate that substantial chemical interaction occurs at the interface at temperatures as low as 100 K. These studies also show the presence of Ni in interstitial voids in the Si near the interface. A comparative study of the core and valence band features for the Ni and Pd silicides provides many valuable insights and a self-consistent picture of the attendent valence charge redistribution and its influence on the observed chemical shifts.
X-ray photoelectron spectroscopy and channeling measurements with MeV He-4(+) ions have been used to probe the structure of the interface in the Ni/Si system. It is found that reactions occur where Ni is deposited on Si at 10 to the -10th torr: Si atoms are displaced from lattice sites, the Ni atoms are in an Si-rich environment, and the Ni/Si interface is graded in composition. Composition gradients are present at both interfaces in the Si/Ni2/Si/Ni system. For the Ni-Si system, cooling the substrate to 100 K slows down the reaction rate. The temperature dependence of the interfacial reactivity indicates the kinetic nature of metal-semiconductor interfaces.
The chemical nature of the Ni/Si, Ni/Ni2Si, and Si/Ni2Si interfaces is studied using X-ray photoelectron spectroscopy. Two approaches are employed: (1) the Ni/silicide and Si/silicide interfaces are examined by dynamically monitoring the advancing reaction front during in situ growth and (2) as-deposited Ni/Si interfacial properties are analyzed by sequential evaporating monolayer Ni films on Si. These experiments show that the Ni/Ni2Si interface consists of a Ni-rich silicide phase, while the Si/Ni2Si interface has a transitional region that is correspondingly Si-rich silicide.
The final-state oxidation products and their distribution in thin native oxides (30-40 A) on GaAs have been studied using X-ray photoelectron spectroscopy in conjunction with chemical depth profiling. Extended room-temperature-oxidation conditions have been chosen to allow the native oxide to attain its equilibrium composition and structure. The work emphasizes the use of chemical depth-profiling methods which make it possible to examine the variation in chemical reactivity of the oxide structure. A minimum of two distinct regions of Ga2O3 with differing chemical reactivity is observed. Chemical shift data indicate the presence of As2O3 in the oxide together with an elemental As overlayer at the interface. A change in relative charge transfer between oxygen and both arsenic and gallium-oxide species is observed in the region of the interface.
The chemical structures of thin SiO2 films, thin native oxides of GaAs (20-30 A), and the respective oxide-semiconductor interfaces, have been investigated using high-resolution X-ray photoelectron spectroscopy. Depth profiles of these structures have been obtained using argon ion bombardment and wet chemical etching techniques. The chemical destruction induced by the ion profiling method is shown by direct comparison of these methods for identical samples. Fourier transform data-reduction methods based on linear prediction with maximum entropy constraints are used to analyze the discrete structure in oxides and substrates. This discrete structure is interpreted by means of a structure-induced charge-transfer model.