Engineering topics
Guo, Liejin
Publications and source records attributed to Guo, Liejin.
Structural and Catalytic Properties of Isolated Pt 2+ Sites in Platinum Phosphide (PtP 2 )
This article describes the synthesis and catalytic properties of supported, 2-3 nm platinum phosphide (PtP 2 ) nanoparticles (NPs). Depending on the P loading, two PtP 2 structures are formed, that is, a PtP 2 surface on a (metallic) Pt core (Pt@PtP 2 ) and single-phase PtP 2 NPs. The structures were determined using extended X-ray absorption fine structure , in situ synchrotron X-ray diffraction, and scanning transmission electron microscopy. In PtP 2 NPs, Pt 2+ ions are geometrically isolated by P 2 2- ions, at a Pt-Pt distance of 4.02 Å, which is much longer than 2.78 Å in (metallic) Pt NPs. The oxidation state of Pt in PtP 2 NPs was determined by in situ X-ray absorption near-edge structure and in situ X-ray photoelectron spectroscopy and was found to be consistent with Pt 2+ ions even after treatment in H 2 at 550 °C. Unlike Pt NPs, which are highly active for propylene hydrogenation at room temperature, PtP 2 NPs are not active below about 150 °C, suggesting the absence of metallic surface Pt. In contrast to metallic Pt, which is poorly selective for acetylene hydrogenation, PtP 2 NPs display high selectivity toward ethylene. PtP 2 , also has high olefin selectivity for propane dehydrogenation, although the rate per g Pt is about 7 times lower than that of metallic Pt NPs of the same size. In situ resonant inelastic X-ray scattering spectroscopy shows that the energy of the filled Pt 5d valence orbitals is 1.5 eV lower than that of metallic Pt, which leads to weaker adsorbate binding consistent with its catalytic properties. Here, a H 2 -stable Pt 2+ site suggests different catalytic applications for these catalysts as compared to Pt NPs.
Tandem Electrocatalytic CO 2 Reduction with Efficient Intermediate Conversion over Pyramid-Textured Cu–Ag Catalysts
If combined with renewably generated electricity, electrochemical CO 2 reduction (E-CO 2 R) could be used as a sustainable source of chemicals and fuels. Tandem catalysis approaches are attractive for providing the product selectivity, which would be required for commercial applications. Here, we demonstrate a two-step tandem electrocatalytic E-CO 2 R with efficient conversion of the intermediate species. The catalyst scaffold is Si(100), which is etched to form a textured surface consisting of micron-sized pyramid structures with the {111} facets. Two metals are used in the electrocatalytic cascade: Ag is employed to perform a two-electron reduction of CO 2 to the intermediate CO, and Cu performs conversion to more reduced products. Using high-angle physical vapor deposition, we form separated, micron-scale areas of the two electrocatalysts on opposite sides of the pyramids, with their relative surface coverages being tunable with the deposition angle. Compared to the textured scaffolds with blanket Ag and Cu used as controls, bimetallic pyramid tandem catalysts have higher current densities and much lower faradic efficiencies (FE) for CO. These effects are due to efficient conversion of the CO formed on Ag to more reduced products on Cu. Methane is the main product to be enhanced by the cascade pathway: a bimetallic catalyst with approximately equal coverages of Ag and Cu produces methane with a FE of 62% at -1.1 V RHE , corresponding to a partial current density of 12.7 mA cm -2 . We estimate an intermediate conversion yield for the CO intermediate of 80-90%, which is close to the mass-transport limited value predicted by reaction-diffusion simulations.