Guo, Yaqing | Search NASA

DOE OSTI2024

Multifunctional nitrile additives for inducing pseudo-concentration gel-polymer electrolyte: Enabling stable high-voltage lithium metal batteries

High-voltage lithium metal batteries (LMBs) are promising for next-generation high-energy storage systems. Unfortunately, their implementation has been severely plagued by the interfacial instability between the high-voltage cathodes/lithium metal (LM) anodes and electrolytes. To tackle these challenges, a novel nitrile additive, 1,4-dicyanobenzene (DCB) (Synonyms: terephthalonitrile), is added to the in situ polymerized pentaerythritol tetraacrylate-based gel polymer electrolyte (GPE). The DCB additive, as demonstrated both theoretically and experimentally, plays a crucial role in altering the Li+ coordinated solvation structure within the GPE. This alteration leads to the formation of a pseudo-concentrated electrolyte with a tightly packed Li+ cluster, expanding the electrochemical stability window of the electrolyte. Moreover, the DCB-included GPE significantly improves its compatibility with both LM anode and high-voltage cathode, attributed to the modified solvation structure and the generated LiF-rich electrolyte/electrode interphases. Accordingly, the GPE enables stable cyclic performance of LMBs based on a 4.9 V LiNi 0.5 Mn 1.5 O 4 cathode at a low relative negative/positive ratio of 4, achieving a high reversible capacity of 123.8 mAh g -1 with a capacity retention of 87.7% over 500 cycles at 0.5 C. This work provides new insights into enhancing the cyclability of high-voltage LMBs via the synergistic effect of additives and GPE.

25 ENERGY STORAGE↗

DOE OSTI2022

Uniform lithiophilic layers in 3D current collectors enable ultrastable solid electrolyte interphase for high-performance lithium metal batteries

Uniform lithium plating/stripping during charging/discharging in 3D lithiophilic current collectors (3DLCC) is essential to suppress growth of lithium dendrites and to mitigate infinite volume variations of lithium metal for long-lived lithium metal batteries. Additionally, this study reveals the decisive role played by uniformity of the lithiophilic layer of the 3DLCC in achieving uniform lithium plating/stripping. Herein, a series of metal oxide-based 3DLCCs are successfully fabricated with a simple and an ultrafast solution combustion method, from which formation of a uniform and stable lithium dendrite-free solid electrolyte interphase via a uniform lithiophilic layer is demonstrated. Taking Co 3 O 4 as the lithiophilic material deposited on a nickel foam as the 3DLCC (Co@NF) for a proof of concept, the loading amount of Co 3 O 4 , closely correlated with the uniformity of the Co 3 O 4 layer, is modulated to optimize its lithium ion hosting performances. With a uniform Co 3 O 4 layer grown in the 3DLCC, an ultralow nucleation overpotential of 33.4 mV is achieved in half-cell tests at 1 mA cm -2 and 1 mAh cm -2 , and a high Coulombic efficiency of 97.1% is maintained after 210 cycles under a severe cycling condition of 2 mA cm -2 and 1 mAh cm -2 . A small polarization voltage of 13 mV together with an ultralong cycle life of 2400 h at 0.5 mA cm -2 and 1 mAh cm -2 in symmetric Li cells is achieved. Moreover, the composite Li anode delivers sensational rate capability and cyclability in full-cells. This work not only provides new and valuable insights into the interphasial chemistry of solid electrolyte interphase layers, but also sheds light on the development of ultrastable lithium metal batteries.

25 ENERGY STORAGE↗