NASA NTRS1992

Failure mechanisms of 3-D woven SiC/SiC composites under tensile and flexural loading at room and elevated temperatures

Nicalon silicon carbide 3D yarn with silicon carbide matrix composites made through a chemical vapor infiltration (CVI) process were investigated under tensile and flexural loading at 23, 1200 and 1550 C in air. The effectiveness of a chemical vapor deposition (CVD) SiC surface coating was also evaluated in severe oxidizing environment. Acoustic emission sensors and in situ optical microscopy were used at room temperature to monitor the failure mechanisms. It is shown that the level of tensile stress at which nonlinear behavior begins is not drastically reduced at 1200 and 1550 C when composites were protected by a SiC surface coating. Extensive fiber pull-out was observed only in the 1550 C specimen. Similar behaviors were also found in flexural specimens.

Chulya, Abhisak↗

NASA NTRS1992

An evaluation of strain measuring devices for ceramic composites

A series of tensile tests were conducted on SiC/RBSN composites using different methods of strain measurement. The tests were used to find the optimum strain sensing device for use with continuous fiber reinforced ceramic matrix composites in ambient and high temperature environments. Bonded resistance strain gages were found to offer excellent performance for room temperature tests. The clip-on gage offers the same performance but significantly less time is required for mounting it to the specimen. Low contact force extensometers track the strain with acceptable results at high specimen temperatures. Silicon carbide rods with knife edges are preferred. The edges must be kept sharp. The strain measuring devices should be mounted on the flat side of the specimen. This is in contrast to mounting on the rough thickness side.

Gyekenyesi, John Z.↗

NASA NTRS1992

Damage mechanisms in three-dimensional woven reinforced ceramic matrix composites under tensile and flexural loading at room and elevated temperatures

Three-dimensional Nicalon SiC/SiC matrix composites made through a chemical vapor infiltration process were studied under tensile and flexural loading at 23, 1200, and 1550 C in air. In situ damage accumulation monitoring NDE techniques were utilized to identify failure mechanisms in these materials. The effectiveness and durability of a chemical vapor deposition SiC surface coating were also evaluated in severe oxidizing environment. Results show that the failure response was very similar for the 23 and 1200 C specimens, while at 1550 C there were significant changes in both the composite mechanical behavior and the matrix microstructure. Extensive fiber pull-out was observed only in the 1550 C specimen. It is also found that the SiC surface coating can protect the composite up to the critical matrix cracking strength.

Chulya, Abhisak↗

NASA NTRS1991

An evaluation of strain measuring devices for ceramic composites

A series of tensile tests was conducted on SiC/reaction bonded silicon nitrides (RBSN) composites using different methods of strain measurement. The tests were used to find the optimum strain sensing device for use with continuous fiber reinforced ceramic matrix composites in ambient and high temperature environments. Bonded resistance gages were found to offer excellent performance for room temperature tests. The clip-on gage offers the same performance, but less time is required for mounting it to the specimen. Low contact force extensometers track the strain with acceptable results at high specimen temperatures. Silicon carbide rods with knife edges are preferred. The edges must be kept sharp. The strain measuring devices should be mounted on the flat side of the specimen. This is in contrast to mounting on the rough thickness side.

Gyekenyesi, John Z.↗

NASA NTRS1991

Polymeric routes to silicon carbide and silicon oxycarbide CMC

An overview of two approaches to the formation of ceramic composite matrices from polymeric precursors is presented. Copolymerization of alkyl- and alkenylsilanes (RSiH3) represents a new precursor system for the production of Beta-SiC on pyrolysis, with copolymer composition controlling polymer structure, char yield, and ceramic stoichiometry and morphology. Polysilsesquioxanes which are synthesized readily and can be handled in air serve as precursors to Si-C-O ceramics. Copolymers of phenyl and methyl silsesquioxanes display rheological properties favorable for composite fabrication; these can be tailored by control of pH, water/methoxy ratio and copolymer composition. Composites obtained from these utilize a carbon coated, eight harness satin weave Nicalon cloth reinforcement. The material exhibits nonlinear stress-strain behavior in tension.

Hurwitz, Frances I.↗

NASA NTRS1991

Thermal shock fiber-reinforced ceramic matrix composites

Monolithic silicon carbide and silicon nitride and a Nicalon fiber reinforced silicon carbide composite were subjected to severe thermal shock conditions via impingement of a hydrogen-oxygen flame. Surface heating rates of 1000 C/sec to 2500 C/sec were generated. The performance of the monolithic reference materials are compared and contrasted to the significantly greater thermal shock resistance of the composite. Ultrasonic and radiographic NDE techniques were used to evaluate the integrity of the composite subsequent to thermal shock. Tensile tests were performed to determine the residual tensile strength and modulus. Physical property changes are discussed as a function of number and severity of thermal shock cycles.

Eckel, Andrew J.↗

NASA NTRS1991

Polymeric routes to silicon carbide and silicon oxycarbide CMC

Hurwitz, Frances I.↗

NASA NTRS1990

Nicalon/siliconoxycarbide ceramic composites

A series of silsesquioxane copolymers was synthesized by acid hydrolysis and condensation of trimethoxysilanes of the form RSi(OCH3)3, where R = methyl or phenyl. By varying pH, water/methoxy and methyl/phenyl ratios, the molecular structure, polymer rheology and ceramic composition can be controlled. The polymers form an amorphous siliconoxycarbide on pyrolysis. Composites of Nicalon/siliconoxycarbide were fractured in four-point flexure and in tension to evaluate the influence of matrix composition, final fabrication temperature and use of filler on composite mode of failure, modulus, strain capability and strength. Incorporation of filler was found to increase matrix compressive strength. Employment of processing temperatures of 1375 to 1400 C enhanced strain to failure and reduced the tendency toward brittle fracture. Mixed mode (compression/shear and tension/shear) failures were observed in flexural samples processed to the higher temperatures, giving rise to nonlinear stress-strain curves. Tensile samples pyrolyzed to 1400 C showed linear-elastic behavior and failed by fracture of fiber bundles. Matrix material was found to be adherent to the fiber surface after failure. These results demonstrate the need for tensile testing to establish composite behavior.

Hurwitz, Frances I.↗

NASA NTRS1989

Polymer derived Nicalon/Si-C-O composites - Processing and mechanical behavior

Ceramic matrix composites fabricated using Nicalon fiber and several polysilsesquioxane-derived Si-C-O matrices were characterized by optical and SEM and in four-point bending. In the matrix material linear shrinkages of up to 19 percent were observed for the vinylmethyl copolymer pyrolyzed to 1200 C, and up to 13 percent for the phenylmethyl material pyrolyzed to the same temperature, resulting in considerable matrix cracking. Under four-point loading, most composite samples fractured in a brittle manner as the result of strong fiber-matrix bonding. Flexural strengths, moduli, and ultimate strain varied with fiber sizing and processing parameters. Testing and analysis is being applied to promote more fibrous pullout during fracture.

Hurwitz, Frances I.↗

NASA NTRS1988

High temperature tensile testing of ceramic composites

The various components of a high temperature tensile testing system are evaluated. The objective is the high temperature tensile testing of SiC fiber reinforced reaction bonded Si3N4 specimens at test temperatures up to 1650 C (3000 F). Testing is to be conducted in inert gases and air. Gripping fixtures, specimen configurations, furnaces, optical strain measuring systems, and temperature measurement techniques are reviewed. Advantages and disadvantages of the various techniques are also noted.

Gyekenyesi, John Z.↗

NASA NTRS1987

Optical strain measuring techniques for high temperature tensile testing

A number of optical techniques used for the analysis of in-plane displacements or strains are reviewed. The application would be for the high temperature, approximately 1430 C (2600 F), tensile testing of ceramic composites in an oxidizing atmosphere. General descriptions of the various techniques and specifics such as gauge lengths and sensitivities are noted. Also, possible problems with the use of each method in the given application are discussed.

Gyekenyesi, John Z.↗