Steam-Assisted Ammonolysis of MoO2 as a Synthetic Pathway to Oxygenated δ-MoN

A common route for the synthesis of molybdenum nitrides is through the temperature-programmed reaction of molybdenum oxides with NH3, or ammonolysis. In this work, the role of precursor phase, gas phase chemistry (impact of H2O), and temperature profile on the reaction outcome (700 °C) was examined, which resulted in varying amounts of MoO2, H2MoO5, and the nitride phases—cubic γ (nominally Mo2N) and hexagonal δ (nominally MoN). The phase fraction of the δ phase increased with precursor in the sequence MoO2 > MoO3 > H2MoO5. Steam in the reaction gas also favored the production of δ over γ, but with too much steam, MoO2 was obtained in the product. Synthesis conditions for obtaining nearly phase-pure δ were identified: MoO2 as the precursor, 2% H2O in the gas stream, and a moderate heating rate (3 °C/min). In situ X-ray diffraction provided insights into the reaction pathway. Extensive physico-chemical analysis of the δ phase, including synchrotron X-ray and neutron diffraction, electron microscopy, thermogravimetric analysis, X-ray photoelectron spectroscopy, and prompt gamma activation analysis, revealed its stoichiometry to be MoO0.108(8)N0.892(8)H0.012(5), indicating non-trivial oxygen incorporation. The presence of N/O ordering and an impurity phase Mo5N6 were also revealed, detectable only by neutron diffraction. Notably, a computationally predicted MoON phase (doi: 10.1103/PhysRevLett.123.236402), of interest due to its potential to display a metal-insulator transition, did not appear under any reaction condition examined.

Pandey, Shobhit↗
DOE OSTI2024

Understanding Direct-Ammonia Protonic Ceramic Fuel Cells: High-Performance in the Absence of Precious Metal Catalysts

Ammonia has received considerable attention as a promising carbon-free hydrogen carrier. At temperatures above 400 °C, NH 3 is thermodynamically unstable with respect to decomposition into nitrogen and hydrogen and is, thus, suitable for direct use in solid oxide fuel cells (SOFCs) without external reforming. However, poor catalytic activity for ammonia decomposition at the moderate temperatures of protonic ceramic fuel cell (PCFC) operation has resulted in low fuel cell power output relative to operation on hydrogen and likely contributes to reported cell degradation. Here we prepared cells based on a thermodynamically robust electrolyte, a high activity cathode, and an anode with a distinctive structure to overcome challenges of poor activity and stability. Furthermore, the cells delivered peak power densities of 0.59 and 0.44 W cm –2 under H 2 and NH 3 , respectively, at 500 °C, excellent stability over a period of 200 h, and no detectable NO x in the anode exhaust gas.

25 ENERGY STORAGE↗
DOE OSTI2024

Methods of forming bilayer cathodes for electrochemical cells

Materials for electrochemical cells are provided. BaZr 0.4 Ce 0.4 M 0.2 O 3 compounds, where M represents one or more rare earth elements, are provided for use as electrolytes. PrBa 0.5 Sr 0.5 Co 2−x Fe x O 5+δ is provided for use as a cathode. Also provided are electrochemical cells, such as protonic ceramic fuel cells, incorporating the compounds as electrolytes and cathodes.

Haile, Sossina M.↗
DOE OSTI2024

Uncovering fast solid-acid proton conductors based on dynamics of polyanion groups and proton bonding strength

Achieving high proton conductivity in inorganic solids is key for advancing many electrochemical technologies, including low-energy nano-electronics and energy-efficient fuel cells and electrolyzers. A quantitative understanding of the physical traits of a material that regulate proton diffusion is necessary for accelerating the discovery of fast proton conductors. In this work, we have mapped the structural, chemical and dynamic properties of solid acids to the elementary steps of the Grotthuss mechanism of proton diffusion. Our approach combines ab initio molecular dynamics simulations, analysis of phonon spectra and atomic structure calculations. We have identified the donor–hydrogen bond lengths and the acidity of polyanion groups as key descriptors of local proton transfer and the vibrational frequencies of the cation framework as the key descriptor of lattice flexibility. The latter facilitates rotations of polyanion groups and long-range proton migration in solid acid proton conductors. The calculated lattice flexibility also correlates with the experimentally reported superprotonic transition temperatures. Using these descriptors, we have screened the Materials Project database and identified potential solid acid proton conductors with monovalent, divalent and trivalent cations, including Ag + , Sr 2+ , Ba 2+ and Er 3+ cations, which go beyond the traditionally considered monovalent alkali cations (Cs + , Rb + , K + , and NH 4 + ) in solid acids.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

From Fundamental Interfacial Reaction Kinetics to Macroscopic Current–Voltage Characteristics: Case Study of Solid Acid Fuel Cell Limitations and Possibilities

The unique properties of solid acid electrolytes, in particular CsH 2 PO 4 , are in many ways ideal for fuel cell operation. However, the technology is constrained by high cathode overpotentials. Here a simplified cathode geometry is employed to obtain the fundamental electrochemical parameters (exchange current density and charge transfer coefficient) describing the oxygen reduction reaction (ORR) at the CsH 2 PO 4 -Pt-gas interface. The parameters are incorporated into a 1D model of the voltage–current characteristics of realistic SAFC cathodes, which reproduced the measured polarization behavior of such cathodes without recourse to fitting adjustable parameters. Following this validation, the model is utilized to evaluate the impact of changes to cathode properties, microstructure, and operating conditions. Of these, the charge transfer coefficient, measured to have a value of ≈0.6 for ORR on Pt in the SAFC cathode environment, is found to have the greatest impact on power output. Nevertheless, even without material modifications, a combination of microstructural and operational modifications are identified with projected performance metrics meeting Department of Energy targets (0.8 V at 300 mA cm –2 , and peak power density of 1 W cm –2 ), albeit at high Pt loadings. However, the analysis indicates that truly meaningful advances will likely necessitate the discovery of alternative ORR catalysts.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Hydrogen in energy and information sciences

Beyond its fascinating chemistry as the first element in the Periodic Table, hydrogen is of high societal importance in energy technologies and of growing importance in energy-efficient computing. In energy, hydrogen has reemerged as a potential solution to long-term energy storage and as a carbon-free input for materials manufacturing. Its utilization and production rely on the availability of proton-conducting electrolytes and mixed proton–electron conductors for the components in fuel cells and electrolyzers. In computing, proton mediation of electronic properties has garnered attention for electrochemically controlled energy-efficient neuromorphic computing. Incorporation of substitutional and interstitial hydride ions in oxides, though only recently established, enables tuning of electronic and magnetic properties, inviting a range of possible exotic applications. This article addresses common themes in the fundamental science of hydrogen incorporation and transport in oxides as relevant to pressing technological needs. The content covers (1) lattice (or bulk) mechanisms of hydrogen transport, primarily addressing proton transport, but also touching on hydride ion transport; (2) interfacial transport; (3) exploitation of extreme external drivers to achieve unusual response; and (4) advances in methods to probe the hydrogen environment and transport pathway. The snapshot of research activities in the field of hydrogen-laden materials described here underscores exciting recent breakthroughs, remaining open questions, and breathtaking experimental tools now available for unveiling the nature of hydrogen in solid-state matter.

08 HYDROGEN↗
DOE OSTI2023

Reconstruction of simulated electrostatic potentials by automatic differentiation-based phase retrieval in electron microscopy imaging

Measuring interfacial electrostatic potentials is vital to understanding many fundamental materials properties. A variety of TEM methods exist for measuring electric potentials from the phase shift produced on an electron wave as it passes through a sample. However, most are either experimentally challenging or poorly suited to resolving nanoscale features. Here, we demonstrate the viability of a simple, automatic differentiation-based exit wave reconstruction from a focal series of images to accurately measure nanoscale electric potentials. Here, the analysis suggests that under optimal measurement conditions, electric potentials can be resolved to less than 0.06 V in magnitude and less than 1 nm in spatial extent.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Accuracy of DFT computed oxygen-vacancy formation energies and high-throughput search of solar thermochemical water-splitting compounds

The enthalpy change involved in metal oxide reduction is a key quantity in various processes related to energy conversion and storage, and is of particular interest for computational prediction. Often this prediction involves the simulation of a high temperature reduction process with a 0K methodology like density functional theory (DFT), and it is not infrequent for the high temperature and 0K stable crystal structures to differ. This introduces a conundrum with regards to the choice of crystal structure to utilize in the computation, with approaches in the literature varying and experimental validation remaining scarce. In this work we address both the crystal structure conundrum and the experimental validation, and then apply the insights we gain to guide a high-throughput search for new materials for solar thermochemical water-splitting applications. By computing the DFT+U oxygen vacancy formation energy (ΔE vf ) of a selection of ABO 3 compounds and comparing different crystal structures for each composition, we highlight the issues that arise when the structure utilized in the computation is dynamically unstable at 0K, namely the presence of an artificial lowering of ΔE vf , and the lack of convergence of ΔE vf with cell size. We solve these limitations by identifying and employing a suitable surrogate dynamically stable structure. We then validate the predictive power of our calculations against appositely generated experimental measurements of reduction enthalpy for a series of Hubbard U values, finding an accuracy ranging between 0.2-0.6 eV/O. In light of such conclusions, we revise and expand a previous a high-throughput DFT study on ABO 3 perovskite oxides. As a result, we provide a list of candidate STCH materials, highlight trends with redox-active cation and structural distortion, and identify Mn 4+ , Mn 3+ and Co 3+ as the most promising redox-active cations.

08 HYDROGEN↗
DOE OSTI2022

Thermodynamic assessment of nonstoichiometric oxides for solar thermochemical fuel production

Two-step solar thermochemical cycling (STC) based on nonstoichiometric oxides is an ideal means of solar fuel (e.g., H 2 , CO) production. Screening of nonstoichiometric oxides with excellent thermodynamic performance is key to achieving high solar-to-fuel efficiency. However, application-driven materials assessment intended for reactor-level solar fuel production performance requires mimicking realistic operating conditions of on-sun tests in a laboratory setting, which makes oxides assessment and screening an onerous task to accomplish experimentally. In this work, a rapid assessment and screening model of nonstoichiometric oxides for two-step solar thermochemical cycling assuming fixed-bed flow pattern and quasi-equilibration of the solid with the flowing gas phase is developed, with solar-to-fuel efficiency being the target function of optimization. The model accounts for the thermodynamic parameters of oxide materials and typical operating conditions of experimental thermochemical cycling. This study employed the model to explore and compare two groups of typical nonstoichiometric oxides (CeO 2 - and (LaSr)MnO 3 -based) for their maximum efficiency under their uniquely optimized cycling conditions. The results show that CeO 2 can reach a maximum efficiency of 12.9% at reduction temperature of 1500 °C, which is superior to other candidate materials, including 20 mol% Zr-doped CeO 2 (10.1%), La 0.6 Sr 0.4 MnO 3 (2.5%) and La 0.8 Sr 0.2 MnO 3 (3.3%). Even when the reduction temperature is lowered to 1350 °C, ceria yields the highest efficiency amongst the candidate STC materials considered. The optimal cycling strategy depends on the inherent thermodynamic properties of the oxides. This approach serves as a framework for assessing the maximum efficiency and optimal conditions of candidate thermochemical materials within a range of constraints rather than comparing materials under arbitrary cycling conditions, which may inherently favor one material over another. For oxidation temperatures below 800–1000 °C, the model could be further improved by considering reaction kinetics.

14 SOLAR ENERGY↗
DOE OSTI2022

Broad Applicability of Electrochemical Impedance Spectroscopy to the Measurement of Oxygen Nonstoichiometry in Mixed Ion and Electron Conductors

Oxygen non-stoichiometry is a fundamental feature of mixed ion and electron conductors (MIECs). In this work a general electrochemical method for determining non-stoichiometry in thin film MIECs, via measurement of the chemical capacitance, is demonstrated using ceria and ceria-zirconia (Ce 0.8 Zr 0.2 O 2-δ ) as representative materials. A.C. impedance data are collected from both materials at high temperature (750-900 °C) under reducing conditions with oxygen partial pressure (pO 2 ) in the range 10-13 to 10-20 atm. Additional measurements of ceria-zirconia films are made under relatively oxidizing conditions with pO 2 in the range 0.2 to 10 -4 atm and temperatures of 800-900 °C. Under reducing conditions, the impedance spectra are described by a simple circuit in which a resistor is in series with a resistor and capacitor in parallel, and thickness dependent measurements are used to resolve the capacitance into interfacial and chemical terms. Under more oxidizing conditions, the impedance spectra (of Ce 0.8 Zr 0.2 O 2-δ ) reveal an additional diffusional feature, which enables determination of the ionic resistance of the film in addition to the capacitance, and hence the transport properties. A generalized mathematical formalism is presented for recovering the non-stoichiometry from the chemical capacitance, without recourse to defect chemical models. The ceria non-stoichiometry values are in good agreement with literature values determined by thermogravimetric measurements but display considerably less scatter and are collected on considerably shorter timescales. Here, the thermodynamic analysis of Ce 0.8 Zr 0.2 O 2-δ corroborates earlier findings that introduction of Zr into ceria enhances its reducibility.

08 HYDROGEN↗
DOE OSTI2021

High-throughput characterization of Lu-doped zirconia

Lu-doped zirconia (LuDZ) was reported in the 1960s to be a poor oxygen ion conductor. However, we identified this system as worthy of reexamination based on the results of a machine learning-based screen for promising oxygen ion conductors, further supported by a physical argument: because Lu is the heaviest and smallest of the lanthanides, it should offer the possibility of high conductivity due to its high polarizability and size compatibility with the zirconia structure. Here the relationship between dopant concentration and conductivity in the LuDZ system was determined using a high throughput experimental methodology in which spatially resolved conductivity was measured across a compositionally graded film, spanning from Zr 0.93 Lu 0.07 O 1.965 to Zr 0.82 Lu 0.18 O 1.91 . The conductivity broadly peaks with composition at 15 cation % Lu, coinciding with the approximate phase boundary of the fully stabilized cubic phase. The composition-dependent conductivity measurements reveal a surprising increase in activation energy for ion transport with increasing Lu content with no change in this trend at the composition of the conductivity maximum. The pre-exponential factor increases sharply with Lu content, but displays a distinct plateau once the conductivity maximum composition is attained. At 500 °C, the conductivity of Zr 0.85 Lu 0.15 O 1.925 is 2 × 10 –3 S cm –1 , approaching that of optimally doped Sc-stabilized zirconia, which has the highest reported conductivity among zirconia compounds. In comparison to other oxide ion conductors, Lu-stabilized zirconia offers the advantage over ceria of negligible electronic conductivity and is easier to process than (La,Sr)(Ga,Mg)O 3-δ .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Local Multimodal Electro-Chemical-Structural Characterization of Solid-Electrolyte Grain Boundaries

Typical models of polycrystalline ionic materials treat the grain boundary properties as single valued, without consideration of the full range of values that define the macroscopically measured average. Here a unique experimental platform suitable for local multimodal characterization of individual grain boundaries in bicrystal fibers is reported. A variation of three orders of magnitude in the grain boundary conductivity of ceria is observed, as measured across six individual bicrystals by both alternating current impedance spectroscopy and direct current (D.C.) linear sweep voltammetry. Nonlinear behavior of the D.C. measurements is consistent with resistance due to a space charge effect. Time-of-flight secondary ion beam spectroscopy reveals a correlation between grain boundary resistance and the concentration of impurities Si, Al, and Ca segregated at the grain boundaries, although the bulk concentrations of these impurities are negligible. Electron backscatter diffraction analysis of the crystal orientations suggests a correlation between the misorientation across the grain boundaries and grain boundary resistance. These correlations point towards a grain boundary resistance that arises from impurity-generated space charge effects and variations in impurity concentration and hence resistivity driven by the energetics of impurity segregation to grain boundaries of differing surface energies.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Quantifying leakage fields at ionic grain boundaries using off-axis electron holography

The electrical properties of interfaces in semiconductors and ionic conductors are immensely important in a wide range of applications. Electron holography is ideally suited for the direct measurement of the electrostatic potential of such interfaces. A key challenge with this approach is the contribution of the leakage field from the sample to the observed electron phase shift. This leakage field cannot be a priori independently determined and can cause an overestimation of the phase shift. In this work, we use finite element simulations to compute the three-dimensional electrostatic potential in the vicinity of an interface associated with a given interfacial charge density distribution. We then evaluate the predicted phase shift and demonstrate that the leakage field strongly affects the recovery of the projected interface potential. From the difference between the true potential and uncorrected, recovered potential, we propose a method to correct for this effect. We then demonstrate the application of this methodology to the analysis of experimental off-axis electron holography data acquired from the grain boundaries in lightly doped ceria.

36 MATERIALS SCIENCE↗