Engineering topics
Publications and source records attributed to Halder, Avik.
High fidelity selectivity tuning of the oxidative dehydrogenation of cyclohexene was achieved through the control of the atomic composition of CuPd clusters and their interactions with the support.
Size-selected clusters are important model catalysts because of their narrow size and compositional distributions, as well as enhanced activity and selectivity in many reactions. Still, their structure-activity relationships are, in general, elusive. The main reason is the difficulty in identifying and quantitatively characterizing the catalytic active site in the clusters when it is confined within subnanometric dimensions and under the continuous structural changes the clusters can undergo in reaction conditions. Using machine learning approaches for analysis of the operando X-ray absorption near-edge structure spectra, we obtained accurate speciation of the Cu x Pd y cluster types during the propane oxidation reaction and the structural information about each type. As a result, we elucidated the information about active species and relative roles of Cu and Pd in the clusters.
We report that subnanometer copper tetramer-zirconia catalysts turn out to be highly efficient for CO 2 hydrogenation and its conversion to methane. The cluster size and substrate morphology are controlled to optimize the catalytic performance. The two types of zirconia supports investigated are prepared by atomic layer deposition (~ 3 nm thick film) and supersonic cluster beam deposition (nanostructured film, ~ 100 nm thick). The substrate plays a crucial role in determining the activity of the catalyst as well as its cyclability over repeated thermal ramps. A temperature-programmed reaction combined with in situ X-ray characterization reveals the correlation between the evolution in the oxidation state and catalytic activity. Ex situ photoelectron spectroscopy indicates Cu clusters with stronger interactions with the nanostructured film, which can be the cause for the higher activity of this catalyst. Density functional theory calculations based on the Cu 4 O 2 cluster supported on a ZrOx subunit reveal low activation barriers and provide mechanism for CO 2 hydrogenation and its conversion to methane. Altogether, the results show a new way to tune the catalytic activity of CO 2 hydrogenation catalysts through controlling the morphology of the support at the nanoscale.
The invention provides a method for generating alkenes, the method having the steps of contacting an alkane with catalyst clusters no greater than 10 nm for a time sufficient to convert the alkane to alkene.
X-ray absorption near edge structure (XANES) spectroscopy is widely used for operando catalyst characterization. We show that, for highly fluxional supported nanoclusters, the customary extraction of the oxidation state of the metal from the XANES data by fitting to the bulk standards is highly questionable. The XANES signatures as well as the apparent oxidation state for such clusters arise from a complex combination of many factors, and not only from the chemical composition in reaction conditions (e.g., oxygen content in oxidizing atmosphere). The thermally accessible isomerization and population of several structurally distinct cluster forms, cluster-support interaction, and intrinsic size effects all impact the metal oxidation state and XANES signal. We demonstrate this on copper oxide clusters with different compositions, Cu4Ox(x = 2-5) and Cu5Oy (y = 3, 5), deposited on amorphous alumina and ultrananocrystalline diamond, for which we computed the XANES spectra and compare the results to the experiment. We show in addition that fitting the experimental spectrum to calculated spectra of supported clusters can, in contrast, provide good agreement and insight into the spectrum-composition-structure relation. Experimental XANES interpreted using the proposed fitting scheme shows the partial reduction of Cu oxide clusters at rising temperatures, and pinpoints the specific stoichiometries that dominate in the ensemble of cluster states as the temperature changes.
The metal-organic framework (MOF), NU-1000, and its metalated counterparts have found proof-of-concept application in heterogeneous catalysis and hydrogen storage amongst others. A vapor-phase technique, akin to atomic layer deposition (ALD), is used to selectively deposit divalent Cu ions on oxo, hydroxo-bridged hexa-zirconium(IV) nodes capped with terminal –OH and -OH 2 ligands. Subsequent reaction with steam yields node-anchored, CuII-oxo,hydroxo clusters. We find that cluster installation via AIM (= ALD In MOFs) is accompanied by an expansion of MOF mesopore (channel) diameter . We investigated the behavior of the cluster-modified material, termed Cu-AIM-NU-1000, to heat treatment up to 325 °C, at atmospheric pressure with a low flow of H2 into the reaction cell. The response under these conditions revealed two important results: (1) Above 200 °C, the initially installed few-metal-ion clusters reduce to neutral Cu atoms. The neutral atoms migrate from the nodes and aggregate into Cu nanoparticles. While the size of particles formed in the MOF interior is constrained by the width of mesopores (ca. 3 nm), those formed on the exterior surface of the MOF can grow as large as ca. 8 nm. (2) Reduction and release of Cu atoms from the MOFs nodes is accompanied NU-1000 undergoes dynamic structural transformation as it reverts back to its original dimension following the release. These results show while the MOF framework itself remains intact at 325 °C in an H 2 atmosphere, the small, AIM-installed Cu II -oxo,hydroxo clusters are stable with respect to reduction and conversion to metallic nanoparticles only up to ~200 °C.