Haley, Jack | Search NASA

DOE OSTI2023

Microstructural evolution and transmutation in tungsten under ion and neutron irradiation

This study aims to compare the effects of neutron and self-ion irradiation on the mechanical properties and microstructural evolution in W. Neutron irradiation at the HFR reactor to 1.67 dpa at 800 °C resulted in the formation of large Re and Os rich clusters and voids. The post-irradiation composition was measured using APT and verfified against FISPACT modelling. The measured Re and Os concentration was used to create alloys with equivalent concentrations of Re and Os. These alloys were exposed to self-ion irradiation to a peak dose of 1.7 dpa at 800 °C. APT showed that self-ion irradiation leads to the formation of small Os clusters, wheras under neutron irradiation large Re/Os clusters form. Voids are formed by both ion and neutron irradiation, but the voids formed by neutron irradiation are larger. By comparing the behaviour of W-1.4Re and W-1.4Re-0.1Os, suppression of Re cluster formation was observed. Irradiation hardening was measured using nanoindentation and was found to be 2.7 GPa, after neutron irradiation and 1.6 GPa and 0.6 GPa for the self-ion irradiated W-1.4Re and W-1.4Re-0.1Os. The higher hardening is attributed to the barrier strength of large voids and Re/Os clusters that are observed after neutron irradiation.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Cavity evolution and void swelling in dual ion irradiated tempered martensitic steels

Microstructural evolutions in two variants of the F82H 8 wt%Cr tempered martensitic steel under dual (He + plus Fe 3+ ) ion irradiations at 500 °C have been characterized by transmission electron microscopy. Emphasis is on understanding the combined effects of displacements per atom (dpa) and the helium/dpa ratio (He/dpa) on cavity evolution and void swelling (f v ). The dual ion database includes 231 alloy-dpa-He/dpa conditions for irradiations up to ~ 82 dpa and 3700 appm helium. Here, we hypothesize that the large “scatter” observed in the f v data is primarily due to local microstructural variations, especially those that shield regions at shallower depths from the effects of injected interstitial atoms, which would otherwise reduce f v . More generally, our hypothesis is that the highest f v data, at a specified dpa and He/dpa, provides the most appropriate estimate of swelling for fusion neutron irradiation conditions. The dose dependence of f v can be described by an incubation dpa i , marking the onset of significant void growth, and a post-incubation swelling rate, f v ’ = Δf v /Δdpa. Both dpa i and f v ’ decrease with increasing He/dpa. The f v ’ data are quantitatively consistent with a simple model for defect partitioning between evolving bubble, void, and dislocation sinks strengths and biases. Most notably, the model correctly predicts both the incubation dpa i , and the subsequent f v ’, in spite of the fact that they reflect somewhat different physics. Our analysis also suggests that defect recombination is modest at 500 °C. Along with other considerations, this supports the hypothesis that, even at high dpa rates, dual ion irradiations can be used to reasonably emulate void nucleation and growth for a range of fusion-relevant neutron irradiation service conditions. A companion paper incorporates the results of this study in a reduced-order, data-driven void swelling model.

36 MATERIALS SCIENCE↗