Exploring the interfacial structure and crystallinity for direct growth of Mn 3 Sn(0001) on sapphire (0001) by molecular beam epitaxy
The Kagome antiferromagnet Mn 3 Sn has garnered a lot of attention due to the presence of interesting properties such as anomalous Hall effects and Nernst effects. Until now, few papers have been reported to grow using molecular beam epitaxy with a buffer layer or on other substrates. In this paper, we discuss the synthesis of crystalline Mn 3 Sn layers, prepared on Al 2 O 3 (0001) without a buffer layer using molecular beam epitaxy. The growth is monitored in-situ using reflection high energy electron diffraction and measured ex-situ using X-ray diffraction, Rutherford back-scattering, and cross-sectional scanning transmission electron microscopy. The samples were deposited at 524 ± 5 °C, with an Mn: Sn atomic flux ratio of 3.2:1 for 90 minutes. Orientation relationships between the Mn 3 Sn films and the sapphire substrates are determined from in-plane and out-of-plane measurements. Our analysis indicates that the resulting film is predominantly c−plane oriented. Lastly, the samples prepared in this way were found to be discontiguous, showing a 3-dimensional morphology. According to first-principles calculations, the Mn 3 Sn exhibits a displaced Kagome structure in the very first stages of growth, for 2ML and 4ML growth on Al 2 O 3 (0001). This result is corroborated by calculating the surface formation energies and explains the observed RHEED patterns.