Hall, Jacklyn | Search NASA

DOE OSTI2026

Understanding_the_deactivation_mechanisms_of_ethanol_conversion_over_Cu-Y_Beta_catalyst

Direct conversion of bioethanol to C₃⁺olefins is a promising pathway for sustainable aviation fuel (SAF) production, but catalyst deactivation limits long-term operation. The stability and deactivation mechanisms of multifunctional Cu–Y/Beta zeolite catalysts were investigated for ethanol-to-olefins conversion over 300 h time-on-stream in the presence of H2. Catalytic testing reveals progressive losses in ethanol conversion and C₃⁺ olefin selectivity accompanied by increased acetaldehyde formation. The catalyst testing studies correlate with a suite of characterizations of fresh, spent, and regenerated catalysts to identify the deactivation factors. The loss of Y Lewis acid sites is the primary deactivation element. Reversible acid site deactivation is caused by coke deposition, which blocks Y-derived Lewis acid sites responsible for aldol condensation, MPV reduction, and alcohol dehydration. Minor irreversible deactivation is observed and possibly results from hydrothermal dehydroxylation of Y–silanol interactions, resulting in permanent loss of Lewis acidity without zeolite framework degradation or Y aggregation. Cu sites undergo limited agglomeration into small nanoparticles but contribute insignificantly to catalyst deactivation, under the investigated time frame. Oxidative regeneration removes coke and redistributes Cu sites, leading to full recovery of the initial catalytic performance though the Y Lewis acid sites are unable to fully recover. These findings establish Lewis acid site degradation as the primary deactivation mechanism impacting long-term catalyst stability

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Synthesis of platinum nanoparticles on strontium titanate nanocuboids via surface organometallic grafting for the catalytic hydrogenolysis of plastic waste

Pt/SrTiO 3 (Pt/STO), prepared on small scale by atomic layer deposition (ALD), is a capable heterogeneous catalyst for the selective hydrogenolysis of polyolefins to hydrocarbon oils, providing a promising approach for upcycling plastic waste. However, because deposition by ALD is costly and resource-intensive, a new synthesis of Pt/STO is needed to effectively scale catalyst production and pursue the commercialization of upcycling processes. To that effect, this work details a scalable deposition method for Pt/STO made by surface organometallic chemistry (SOMC) techniques using Pt(II) acetylacetonate or and trimethyl(methylcyclopentadienyl)platinum. The STO support was calcined (550 °C), treated with ozone (200 °C), and finally steamed (200 °C) to afford a clean STO surface populated with only hydroxyl groups. Pt precursors were dissolved in toluene and deposited onto STO. After reduction at 300 °C, the STO support was decorated with 1.0–1.5 nm Pt nanoparticles. The size and loading of these nanoparticles were varied by employing a multi-cycle deposition and oxidation and/or reduction process designed to ALD techniques. In conclusion, these Pt/STO catalysts hydrogenolyzed isotactic polypropylene into liquid products (>95% yield) with average molecular weights of 200–300 Da (~25 carbon atoms) and narrow size distributions at 300 °C and 180 psi H 2 .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗