DOE OSTI2024

Tailoring High Hardness and Rigidity in Biodegradable Thermoplastic Polyurethanes

In response to escalating environmental concerns, there is a pressing demand for materials capable of delivering both sustainability and robust mechanical properties, thereby substituting nonrenewable counterparts in various applications. This study presents a comprehensive investigation into the synthesis and characterization of biobased aliphatic thermoplastic polyurethanes (TPUs) that exhibit impressive mechanical properties, including tensile strength in the range of 48–41 MPa and flexural modulus up to 2.2 GPa. These biodegradable TPUs displayed high shore A and D hardness between 95 and 98 and 51–42, respectively, and thus can be categorized as “extra hard” plastics according to the durometer scale for PUs. Herein, we have prepared a series of four 100% biobased polyester polyols from biobased diacid and chain-extender as precursors with molecular weights varying from 500 to 1400 g/mol. The corresponding TPUs that were prepared by using an aliphatic diisocyanate were evaluated for their thermal stability, microphase separation, mechanical properties, and biodegradation. By leveraging renewable feedstocks, these TPUs offer a sustainable alternative to petroleum-derived materials, with their mechanical performance meeting conventional benchmarks. Furthermore, postcomposting analysis revealed significant surface degradation, affirming their biodegradability and environmental compatibility.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Variation of Aliphatic Diisocyanates in Bio-Based TPUs

The utilization of bio-based materials for polymer production poses a challenge to both the industrial and academic sectors due to the availability and production costs of the necessary raw materials. Diisocyanates necessary for polyurethane synthesis have posed a particular challenge, given the paucity of natural diamine precursors for traditional phosgenation. We recently developed a phosgene-free flow chemistry methodology that allows for the safe, efficient, and scalable preparation of diisocyanates from naturally produced diacids. This chemistry broadens the potential for the development of renewable diisocyanates for a broad variety of applications. Here, we expand upon this work by demonstrating the scaled production of a panel of bio-based linear, aliphatic diisocyanates, with chain lengths ranging from four to eight carbons in good yields of 57–81% and high purity (~97%). Furthermore, these are applied to the synthesis of thermoplastic polyurethanes (TPUs) containing up to a 100% renewable carbon content. TPUs formulated using shorter carbon-chained diisocyanates displayed a higher tensile strength compared to those formulated using longer chains. Ready access to diisocyanates of varying chain length affords the ability to tailor TPU properties through careful selection of the diisocyanate, polyol, and chain extender, offering hard and soft TPUs for multiple end-use applications.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Synthesis of Acid Hydrazides from Carboxylic Acids in Continuous Flow

A concise methodology for the synthesis of acid hydrazides from carboxylic acids via a continuous flow process in yields ranging from 65 to 91% is described. Using short residence times of between 13 and 25 mins, the conditions proved amenable to a variety of mono- and diacids, including aliphatic, aromatic, and heteroaromatic functionalities. Furthermore, to demonstrate scalability, a large-scale (200 g) synthesis of azelaic dihydrazide was conducted over a continuous run of 9 h with an 86% overall yield, equating to a 22 g/h output.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Bio‐based glycerol plasticizers for flexible poly(vinyl chloride) blends

Abstract A series of glycerol‐based compounds were investigated for their application as plasticizers for flexible poly(vinyl chloride) (PVC) blends. The effect of plasticizer chemical structure on the performance, migration behavior, and blend morphology were evaluated and compared to blends produced using the commercial plasticizer dioctyl terephthalate (DOTP). Blends containing 40 phr (parts per hundred rubber) of glycerol‐based plasticizer showed a considerable reduction (between 54 to 86°C) in glass transition temperature ( T g ) relative to neat PVC ( T g ~ 80°C). Tensile testing of samples prepared with the glycerol analogs demonstrated higher ductility (elongation at break values of up to 97%) than DOTP (elongation at break value of 75%) at identical plasticizer loadings. The surface morphologies showed excellent incorporation of the glycerol plasticizers functionalized with alkyl chains longer than four carbons in length into the PVC matrix, whereas droplet formation was observed in blends with shorter chain glycerol derivatives. Leaching behavior of the plasticized samples were evaluated into different media and showed that plasticizers comprised of branched, or longer alkyl chains produced 2‐ to 4‐fold lower migration rates compared to those with shorter alkyl chains into polar solutions.