NASA NTRS2004

ITO-MgF2 Film Development for PowerSphere Polymer Surface Protection

Multi-kilogram class microsatellites with a PowerSphere electric power system are attractive for fulfilling a variety of potential NASA missions. However, PowerSphere polymer surfaces must be coated with a film that has suitable electrical sheet resistivity for electrostatic discharge control, be resistant to atomic oxygen attack, be transparent to ultraviolet light for composite structure curing and resist ultraviolet light induced darkening for efficient photovoltaic cell operation. In addition, the film must be tolerant of polymer layer folding associated with launch stowage of PowerSphere inflatable structures. An excellent film material candidate to meet these requirements is co-sputtered, indium oxide (In2O3) - tin oxide (SnO2), known as 'ITO', and magnesium fluoride (MgF2). While basic ITO-MgF2 film properties have been the subject of research over the last decade, further research is required in the areas of film durability for space-inflatable applications and precise film property control for large scale commercial production. In this paper, the authors present film durability results for a folded polymer substrate and film resistance to vacuum UV darkening. The authors discuss methods and results in the area of film sheet resistivity measurement and active control, particularly dual-channel, plasma emission line measurement of ITO and MgF2 plasma sources. ITO-MgF2 film polymer coupon preparation is described as well as film deposition equipment, procedures and film characterization. Durability testing methods are also described. The pre- and post-test condition of the films is assessed microscopically and electrically. Results show that an approx. 500A ITO-18vol% MgF2 film is a promising candidate to protect PowerSphere polymer surfaces for Earth orbit missions. Preliminary data also indicate that in situ film measurement methods are promising for active film resistivity control in future large scale production. Future film research plans are also discussed.

Hambourger, Paul D.↗
NASA NTRS2004

Transparent, Weakly Conductive Films for Space Applications

Electrically insulating spacecraft surfaces are vulnerable to nonuniform charge buildup due to particles emitted by the sun. On Mars, insulating surfaces of exploration vehicles and structures will be affected by dust coatings possibly held in place by triboelectric surface charge. Application of a conductive film may be a solution to the charging problem, but the coating must be highly transparent if used on solar panels, lenses, etc. Sheet resistivity requirements depend on the application and are in the range 10(exp 2) - 10(exp 8) ohms/square. Co-deposited indium tin oxide (ITO) and MgF2 is promising, with high transparency, tailorable electrical properties, and durability to atomic oxygen. Due to ITO's relatively narrow bandgap (approximately 3.5 eV), the film might absorb enough ultraviolet to protect polymeric substrates. Recent work on dual-magnetron-sputtered ITO-MgF2 showed that a variety of polymeric substrates can be coated at room temperature. However, the sheet resistivity is very sensitive to composition, suggestive of a percolation transition. This could be a serious problem for large-scale coating production. We will report on attempts to control film composition by plasma emission monitoring of the ITO and MgF2 guns.

Griffin, John↗
NASA NTRS2003

High Resistivity Transparent/Conductive Coatings for Space Applications: Problems and Possible Improvements

We have prepared transparent films with a sheet relativity of 10(exp 1) to 10(exp 12) ohm/square by co-depositing a transparent conducting oxide (TCO) with magnesium fluoride, using two independently controlled RF magnetron sputter guns to facilitate adjustment of the film composition, Co-deposited indium tin oxide (ITO) and MgF2 on quartz and flexible polymeric substrate exhibited reasonably stable sheet resistivity over several months' time, with substantially lower optical reflectance than that of pure ITO. However, exposure to low-intensity blue light reduces sheet resistivity by as much as two orders of magnitude. Our results suggest this photoconductivity effect may be present in all InO(x)-based materials. We find that sheet resistivity can by "tuned" by admitting a small amount of high-purity air during deposition offering the possibility of closed loop process control.

Cashman, Thomas↗
NASA NTRS2003

Durability of ITO-MgF2 Films for Space-Inflatable Polymer Structures

This paper presents results from ITO-MgF2 film durability evaluations that included tape peel, fold, thermal cycle, and AO exposure testing. Polymer coupon preparation is described as well as ITO-MgF2 film deposition equipment, procedures and film characterization. Durability testing methods are also described. The pre- and post-test condition of the films is assessed visually, microscopically, and electrically. Results show that at ~500 ITO - 9 vol% MgF2 film is suitable to protect polymer surfaces, such as those used in space-inflatable structures of the PowerSphere microsatellite concept, during a 1-year Earth orbiting mission. Future plans for ground-based and orbital testing of this film are also discussed.

Kerslake, Thomas W.↗
NASA NTRS2003

Electrical Properties and Manufacturability of ITO-MgF2 and Related Transparent Arcproof Spacecraft Coatings

To investigate the applicability of co-deposited indium tin oxide and magnesium fluoride as a transparent arcproof coating on the exterior of PowerSphere microsatellites. This included testing coating performance after deposition on flexible polymeric substrates, determining whether ultraviolet (UV) radiation present during deposition might affect the UV-curing resin contained in the substrate, and preparation of coated polymeric samples for radiation damage studies by the PowerSphere team.

Hambourger, Paul D.↗
NASA NTRS1998

Indium Tin Oxide-Magnesium Fluoride Co-Deposited Films for Spacecraft Applications

Highly transparent coatings with a maximum sheet resistivity between 10(exp 8) and 10(exp 9) ohms/square are desired to prevent charging of solar arrays for low Earth polar orbit and geosynchronous orbit missions. Indium tin oxide (ITO) and magnesium fluoride (MgF2) were ion beam sputter co-deposited onto fused silica substrates and were evaluated for transmittance, sheet resistivity and the effects of simulated space environments including atomic oxygen (AO) and vacuum ultraviolet (VUV) radiation. Optical properties and sheet resistivity as a function of MgF2 content in the films will be presented. Films containing 8.4 wt.% MgF2 were found to be highly transparent and provided sheet resistivity in the required range. These films maintained a high transmittance upon exposure to AO and to VUV radiation, although exposure to AO in the presence of charged species and intense electromagnetic radiation caused significant degradation in film transmittance. Sheet resistivity of the as-fabricated films increased with time in ambient conditions. Vacuum beat treatment following film deposition caused a reduction in sheet resistivity. However, following vacuum heat treatment, sheet resistivity values remained stable during storage in ambient conditions.

Dever, Joycer A.↗
NASA NTRS1997

Space Environment Stability and Physical Properties of New Materials for Space Power and Commercial Applications

Useful and informative results were obtained on virtually all materials investigated. For example, the stability of ITO-based arc-proof transparent coatings was greatly improved by substitution of silicon oxide for magnesium fluoride as a dopant. Research on 'air-doped' ITO films has yielded new insight into their conduction mechanism which will help in further development of these coatings. Some air-doped films were found to be extremely pressure sensitive. This work may lead to improved, low-cost gas sensors and vacuum gauges. Work on another promising transparent arc-proof coating (titanium oxide) was initiated in collaboration with industry. Graphite oxide-like materials were synthesized and tested for possible use in high energy-density batteries and other applications. We also started a high-priority project to find the cause of unexpected environmental damage to the exterior of the Hubble Space Telescope (HST) discovered on a recent Shuttle mission. Materials were characterized before and after exposure to soft x-rays and other threats in ground-based simulators.

Hambourger, Paul D.↗
NASA NTRS1997

Space Environment Stability and Physical Properties of New Materials for Space Power and Commercial Applications

To test and evaluate suitability of materials for use in space power systems and related space and commercial applications, and to achieve sufficient understanding of the mechanisms by which, the materials perform in their intended applications. Materials and proposed applications included but were not limited to: Improved anodes for lithium ion batteries, highly-transparent arc-proof solar array coatings, and improved surface materials for solar dynamic concentrators and receivers. Cooperation and interchange of data with industrial companies as appropriate.

Hambourger, Paul D.↗
NASA NTRS1996

Optical Properties of Selective Emitter Materials for Thermophotovoltaic Applications

We investigate the optical properties of new "selective emitter" materials for possible use in high-efficiency thermophotovoltaic power systems. These are systems which directly convert heat to radiation at a wavelength closely matched to the bandgap energy of the solar cell. Candidate materials which have strong absorption lines fairly close to the bandgap of good solar-cell materials were chosen for study. Their emittance was measured as a function of wavelength to evaluate their promise as selective TPV emitters. Useful and informative results were obtained. Some of these results were presented at a January 1996 solar energy conference of the American Institute of Aeronautics and Astronautics.

Hambourger, Paul D.↗
NASA NTRS1996

Mixed composition materials suitable for vacuum web sputter coating

Ion beam sputter deposition techniques were used to investigate simultaneous sputter etching of two component targets so as to produce mixed composition films. Although sputter deposition has been largely confined to metals and metal oxides, at least one polymeric material, poly-tetra-fluorethylene, has been demonstrated to produce sputtered fragments which repolymerize upon deposition to produce a highly cross-linked fluoropolymer resembling that of the parent target Fluoropolymer-filled silicon dioxide and fluoropolymer-filled aluminum oxide coatings have been deposited by means of ion beam sputter coat deposition resulting in films having material properties suitable for aerospace and commercial applications. The addition of fluoropolymer to silicon dioxide films was found to increase the hydrophobicity of the resulting mixed films; however, adding fluoropolymer to aluminum oxide films resulted in a reduction in hydrophobicity, thought to be caused by aluminum fluoride formation.

Banks, Bruce A.↗
NASA NTRS1995

Intercalated-Graphite-Fiber Composites

Electrically conducting composites made from bromine-intercalated graphite fibers in epoxy matrix. Bromine-intercalated graphite fibers have conductivity of about 20,000 ohm-1cm-1 and found to be stable in presence of moisture fibers even submerged for indefinite times) and at reasonably high temperature (200 degrees C). Conventional epoxy resins can be used with such fibers. Composite materials containing 50 percent bromine-intercalated graphite fibers have promising properties. Mechanical properties of composites similar to composites made with pristine fibers: Tensile and flexural strengths and Young's and bending moduli essentially unchanged, and interlaminar shear strengths slightly enhanced. Thermal conductivities of composites also show very little degradation. However, electrical conductivities of composites increase, which invites application of composites in electrical grounding planes and in shields against electro-magnetic interference.

Gaier, James R.↗
NASA NTRS1991

Resistivity of pristine and intercalated graphite fiber epoxy composites

Laminar composites were fabricated from pristine and bromine intercalated Amoco P-55, P-75, and P-100 graphite fibers and Hysol-Grafil EAG101-1 film epoxy. The thickness and r.f. eddy current resistivity of several samples were measured at grid points and averaged point by point to obtain final values. Although the values obtained this way have high precision (less than 3 percent deviation), the resistivity values appear to be 20 to 90 percent higher than resistivities measured on high aspect ratio samples using multi-point techniques, and by those predicted by theory. The temperature dependence of the resistivity indicates that the fibers are neither damaged nor deintercalated by the composite fabrication process. The resistivity of the composites is a function of sample thickness (i.e., resin content). Composite resistivity is dominated by fiber resistivity, so lowering the resistivity of the fibers, either through increased graphitization or intercalation, results in a lower composite resistivity. A modification of the simple rule of mixtures model appears to predict the conductivity of high aspect ratio samples measured along a fiber direction, but a directional dependence appears which is not predicted by the theory. The resistivity of these materials is clearly more complex than that of homogeneous materials.

Gaier, James R.↗
NASA NTRS1989

Resistivity of pristine and intercalated graphite fiber epoxy composites

Laminar composites were fabricated from pristine and bromine intercalated Amoco P-55, P-75, and P-100 graphite fibers and Hysol-Grafil EAG101-1 film epoxy. The thickness and r.f. eddy current resistivity of several samples were measured at grid points and averaged point by point to obtain final values. Although the values obtained this way have high precision (less than 3 percent deviation), the resistivity values appear to be 20 to 90 percent higher than resistivities measured on high aspect ratio samples using multi-point techniques, and by those predicted by theory. The temperature dependence of the resistivity indicates that the fibers are neither damaged nor deintercalated by the composite fabrication process. The resistivity of the composites is a function of sample thickness (i.e., resin content). Composite resistivity is dominated by fiber resistivity, so lowering the resistivity of the fibers, either through increased graphitization or intercalation, results in a lower composite resistivity. A modification of the simple rule of mixtures model appears to predict the conductivity of high aspect ratio samples measured along a fiber direction, but a directional dependence appears which is not predicted by the theory. The resistivity of these materials is clearly more complex than that of homogeneous materials.

Gaier, James R.↗
NASA NTRS1989

Effect of heat-treatment temperature of vapor-grown graphite fibers. I - Properties of their bromine intercalation compounds

Vapor-grown graphite fibers were heat treated at 2000, 2200, 2400, 2600, 2800, and 3000 C, brominated at room temperature for two days, and then characterized by X-ray diffraction analysis, differential scanning calorimetry, and resistivity measurements. Fibers greater than 13 microns in diameter had low resistivities (50 microohms or less) irrespective of the heat treatment temperature. An analysis of the results obtained suggests that resistivities below 6 microohms cannot be achieved through a further reduction in defect level unless the amount of bromine is increased.

Gaier, James R.↗
NASA NTRS1988

Stability of bulk Ba2YCu3O(7-x) in a variety of environments

Small bars of ceramic Ba2YCu3O(7-x) were fabricated and subjected to environments similar to those that might be encountered during some NASA missions. These conditions include ambient conditions, high humidity, vacuum, and high fluences of electrons and protrons. The normal state resistivity or critical current density (J sub c) were monitored during these tests to assess the stability of the material. When normal state resistivity is used as a criterion, the ambient stability of these samples was relatively good, exhibiting only a 2 percent degradation over a 3 month period. The humidity stability was shown to be very poor, and to be a steep function of temperature. Samples stored at 50 C for 40 min increased in normal state resistivity by four orders of magnitude. Kinetic analysis indicates that the degradation reaction is second order with water vapor concentration. It is suspected that humidity degradation also accounts for the ambient instability. The samples were stable to vacuum over a period of at least 3 months. Degradation of J sub c in a 1 MeV electron fluence of 9.7 x 10 to the 14th e(-)/sq cm was determined to be no more than about 2 percent. Degradation of J sub c in a 8.7 x 10 to the 14th p(+)/sq cm of 42 MeV protons was found to be grain size dependent. Samples with smaller grain size and initial J sub c of about 240 A/sq cm showed no degradation. while that with larger grain size and an initial J sub c of about 30 A/sq cm degraded to 37 percent of its original value.

Gaier, James R.↗
NASA NTRS1987

Effects of milling brominated P-100 graphite fibers

Preliminary procedures have been developed for the ball milling of pristine and brominated P-100 graphite fibers. Because of the lubricative properties of graphite, large ball loads (50 percent by volume) are required. Use of 2-propanol as a milling medium enhances the efficiency of the process. The fibers, when allowed to settle from the milling medium, tend to be preferentially aligned with rather few fibers standing up. Milled, brominated P-100 fibers have resistivities that are indistinguishable from their pristine counterparts, apparently because of loss of bromine. This suggests that bromine would not be the intercalate of choice in applications where milled fibers of this type are required. It was found that brominated graphite fibers are stable in a wide variety of organic solvents.

Gaier, James R.↗