High-Resolution X-ray Spectromicroscopy Reveals Process-Structure Correlations in sub-5-μm Diameter Carbon Nanotube-Polymer Composite Dry-Spun Yarns

A persistent lack of detailed and quantitative structural analysis of these hierarchical carbon nanotube (CNT) ensembles precludes establishing processing-structure-property relationships that are essential to enhance macroscale performance (e.g., in mechanical, electrical, thermal applications). Here, in this work, we use scanning transmission X-ray microscopy (STXM) to analyze the hierarchical, twisted morphology of dry-spun CNT yarns and their composites, quantifying key structural characteristics such as density, porosity, alignment, and polymer loading. As the yarn twist density increases (15,000 to 150,000 turns per meter), the yarn diameter decreased (4.4–1.4 μm) and density increased (0.55–1.26 g·cm –3 ), as intuitively expected. Yarn density, ρ, ubiquitously scaled with diameter d according to ρ ~ d –2 for all parameters studied here. Spectromicroscopy probes with 30 nm resolution and elemental specificity were employed to analyze the radial and longitudinal distribution of the oxygen-containing polymer content (~30% weight fraction), demonstrating nearly perfect filling of the voids between CNTs with a vapor-phase polymer coating and cross-linking process. These quantitative correlations highlight the intimate connections between processing conditions and yarn structure with important implications for translating the nanoscale properties of CNTs to the macroscale.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Liquid-free covalent reinforcement of carbon nanotube dry-spun yarns and free-standing sheets

Carbon nanotubes (CNTs) possess exceptional mechanical properties, surpassing stiffness and strength metrics of common materials such as steel alloys by 100× at the nanoscale. However, when myriads of individual CNTs are bundled together into macroscopic ensembles like fibers or sheets, the result is a 100-fold drop in strength compared to its individual components. Here we present a general strategy aimed to close this gap in property scaling. By using vapor-phase polymerization of a crosslinkable polymer, we reinforced the weak interlinkages among individual CNTs within both yarns and sheets to promote a better transference of mechanical load across the structure. Furthermore, after the treatment, dry-spun, low-density 2.3 μm thin yarns increased their elastic moduli by at least 300%, and free-standing CNT sheets exhibited a 10× boost. In-situ synchrotron small-angle X-ray scattering revealed that polymer-reinforced yarns undergo limited CNT bundle rearrangement when subjected to tensile loads compared to pristine yarns. This evidence supports the hypothesis that the polymer hinders CNTs slippage, the root cause of the poor scaling of mechanical properties in these materials. While we demonstrated this reinforcement method for CNT structures, it is not specific to CNTs and could be used in a wide variety of other hierarchical nanostructured ensembles.

36 MATERIALS SCIENCE↗