Elementally Resolved Dissolution Kinetics of a Ni-Fe-Cr-Mn-Co Multi-Principal Element Alloy in Sulfuric Acid Using AESEC-EIS

Atomic emission spectroelectrochemistry (AESEC) combined with linear sweep voltammetry (LSV) and electrochemical impedance spectroscopy (EIS) provided insights on both active and passive dissolution of Ni-Fe-Cr-Mn-Co multi-principal element alloy. Elemental dissolution rates measured by AESEC during open circuit experiment were in agreement with those extrapolated from AESEC-LSV and indicated element-specific dissolution tendencies. AESEC-EIS at open circuit potential showed nearly in-phase elemental dissolution during potential modulation which suggests direct dissolution from the alloy surface to the electrolyte. In the passive potential domain, no oscillation of the elemental dissolution rate was detected by AESEC-EIS, suggesting non-oxidative chemical dissolution of the outer layer of the passive film. In this case, dissolution at the passive film/electrolyte interface was equal to the metal oxidation rate (passive current density) at the metal/passive film interface and the passive current density was independent of potential.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Potential Dependent Mn Oxidation and Its Role in Passivation of Ni 38 Fe 20 Cr 22 Mn 10 Co 10 Multi-Principal Element Alloy Using Multi-Element Resolved Atomic Emission Spectroelectrochemistry

The identity of passivating oxides on multi-principal element alloys is of great interest as their optimization offers the potential for exceptional corrosion resistance in aqueous solutions over a broad range of potential and pH. This study focuses on a non-equiatomic Ni 38 Fe 20 Cr 22 Mn 10 Co 10 solid solution alloy and tracks the fate of each alloying element during linear sweep voltammetry, low and intermediate potential holds in the passive potential domain as well as during open circuit relaxation after anodic polarization in slightly acidified Cl − solution. Ni dissolves at all potentials investigated in this work, Fe and Co are incorporated into oxides or hydroxides in low concentrations whilst Cr and Mn are enriched at passive potentials. At low passivating potentials, Mn(II) dissolves and is incorporated in minor amounts in oxides containing large concentrations of Cr(III). Considerable enrichment in Mn(II)-species occurs relative to Cr(III) in the oxide at 0.1 V vs SCE. Electrochemical impedance spectroscopy suggests the presence of layered oxides with marginal passivation at high Mn(II) levels. The formation of these oxides depends on a combination of thermodynamic and kinetic factors as well as the sequence of passivation.

Han, Junsoo (ORCID:0000000192952954)↗

DOE OSTI2020

Potential-pH diagrams considering complex oxide solution phases for understanding aqueous corrosion of multi-principal element alloys

The potential-pH diagram, a graphical representation of the thermodynamically predominant reaction products in aqueous corrosion, is originally proposed for the corrosion of pure metals. The original approach only leads to stoichiometric oxides and hydroxides as the oxidation products. However, numerous experiments show that non-stoichiometric oxide scales are prevalent in the aqueous corrosion of alloys. In the present study, a room temperature potential-pH diagram considering oxide solid solutions, as a generalization of the traditional potential-pH diagram with stoichiometric oxides, is constructed for an FCC single-phase multi-principal element alloy (MPEA) based on the CALculation of PHAse Diagram method. The predominant reaction products, the ions in aqueous solution, and the cation distribution in oxides are predicted. The oxide solid solution is stabilized by the mixing free energy (or mixing entropy) and the stabilizing effect becomes more significant as the temperature increases. Consequently, solid solution oxides are stable in large regions of the potential-pH diagram and the mixing free energy mostly affects the equilibrium composition of the stable oxides, while the shape of stable regions for oxides is mostly determined by the structure of the stable oxides. Agreements are found for Ni 2+ , Fe 2+ , and Mn 2+ between the atomic emission spectroelectrochemistry measurements and thermodynamic calculations, while deviations exist for Cr 3+ and Co 2+ possibly due to surface complexation with species such as Cl - and the oxide dissolution. By incorporating the solution models of oxides, the current work presents a general and more accurate way to analyze the reaction products during aqueous corrosion of MPEAs.

Materials Science↗