NASA NTRS2020

Calorimetric Measurements of the Thermodynamic Properties of RE-Silicate Coating Materials

Thermodynamic quantities of coatings materials and siliceous debris-induced corrosion products are crucial to understand in order to develop mitigation strategies necessary to improve the durability of gas-turbine engines. Siliceous induced corrosion can occur when debris consisting mainly of CaO-MgO-Al2O3-SiO2 (CMAS) is ingested by aircraft engines during and after take-off, which sticks to hot surfaces and forms calcium rare-earth silicate oxyapatites. In this work, high-temperature oxide melt drop solution calorimetry (HT drop solution calorimetry) was used to obtain the enthalpies of formation for RE silicate (RE2Si2O7, RE2SiO5 where RE = Yb, Er, Y, Dy, Nd, Lu and Gd) environmental barrier coatings (EBCs) and the calcium RE silicate oxyapatite Ca2RE8(SiO4)6O2 (RE = Yb, Er, Y, Dy, Nd, Gd and Sm) corrosion products. Trends in the enthalpy of formation as a function of the ionic potential of the rare-earth cations in their related crystallographic sites are discussed.

Costa, Gustavo↗

NASA NTRS2019

Thermochemistry of Protective Coatings and Molten Silicate Debris

The durability of gas-turbine engine components can be significantly affected by the ingestion of siliceous particles, which can melt at high temperature and corrode protective coatings that are essential for long life requirements. The silicate debris consists mainly of CaO-MgO-Al2O3-SiO2 (CMAS) and is usually ingested by aircraft engines during and after take-off, sticking to their hot surfaces and resulting in the formation of calcium rare-earth silicate oxyapatites. The thermochemistry of coatings and their reaction products with molten silicate debris are crucial to understand in order to improve the durability of gas-turbine engines. Here we discuss results of high temperature drop solution calorimetry, drop-and-catch calorimetry (DnC) and differential thermal analysis (DTA) techniques for the thermodynamic properties of both thermal barrier coatings (TBCs) and environmental barrier coatings (EBCs) and their reaction with CMAS compositions. The enthalpies of solution of Y2Si2O7, Yb2Si2O7, 31YSZ, and 16RESZ based coatings and the oxyapatite are moderately positive. However, oxyapatite formation is only favorable over coating dissolution in terms of enthalpy for 7YSZ. The enthalpies of mixing between the coatings and the molten silicate are less exothermic for Yb2Si2O7 and CaYb4Si3O13 than for 7YSZ, indicating lower energetic stability of the latter against molten silicate corrosion. We also report for the first time the calorimetric measurements of the enthalpies of formation of rare-earth silicate based EBC coatings and oxyapatites (rare-earth, RE = Y, Yb, Gd, Dy, Er, Nd and Sm).

Costa, Gustavo↗

NASA NTRS2019

Compositional and Microstructural Effects in the Protection of SiC Components in Water Vapor

Greater gas turbine engine efficiency is a major goal in aeronautics research often pursued through increased engine operating temperatures. However, it is necessary to replace the current hot-stage alloy components with more thermally robust parts, such as promising Silicon-based ceramics and composites. Unfortunately, these materials are still susceptible to the effects of oxidation, water vapor, and (Calcium-Magnesium-Alumino-Silicate) CMAS interaction, among other issues at high temperature. To mitigate these effects, environmental barrier coating (EBC) materials are employed to help control the rate of degradation to the underlying composite. Often, a thermally grown oxide (TGO) layer forms between the EBC and the composite which can act as a point of failure. The current study focuses on the combined effects of water vapor, composite composition, and microstructure in TGO formation on protected and unprotected SiC samples which have been produced under different processing conditions.

Kowalski, Benjamin↗

NASA NTRS2017

Development of Advanced Environmental Barrier Coatings for SiC/SiC Ceramic Matrix Composites: Path Toward 2700 F Temperature Capability and Beyond

Advanced environmental barrier coating systems for SiC-SiC Ceramic Matrix Composite (CMC) turbine and combustor hot section components are currently being developed to meet future turbine engine emission and performance goals. One of the significant coating development challenges is to achieve prime-reliant environmental barrier coating systems to meet the future 2700F EBC-CMC temperature stability and environmental durability requirements. This presentation will emphasize recent NASA environmental barrier coating system testing and down-selects, particularly the development path and properties towards 2700-3000F durability goals by using NASA hafnium-hafnia-rare earth-silicon-silicate composition EBC systems for the SiC-SiC CMC turbine component applications. Advanced hafnium-based compositions for enabling next generation EBC and CMCs capabilities towards ultra-high temperature ceramic coating systems will also be briefly mentioned.

Ceramic Matrix Composite↗

NASA NTRS2017

Flexural Fatigue Behavior of an EBC CMC Composite System In Air and Steam at High Temperature

Both coated and uncoated SiCSiC ceramic matrix composite (CMC) samples were tested in flexure under sustained peak low cycle fatigue (SPLCF) conditions in air or steam at elevated temperatures. The SiCSiC composites were reinforced with 2-D plies of boron nitride coated Hi-Nicalon Type-S SiC fibers which were woven as 5 harness satin (5HS) cloth. The composites were densified by chemical vapor infiltration (CVI) followed by slurry melt infiltration (SMI). A multilayer barium strontium aluminosilicate (BSAS) coating was applied to the samples by a plasma spray method. Fatigue loading limits were determined from monotonic flexure tests at room temperature and 1200oC. Stress levels under the proportional limit of the composite material were selected for the SPLCF tests. After cyclic testing, the composites were evaluated to determine crack propagation and failure modes in the coated and uncoated composites. Microstructural examination was used to identify coating degradation and failure modes of the EBCCMC system.

Steam testing↗

NASA NTRS2017

Cyclic Fatigue Durability of Uncoated and EBC Coated 3D SiC/SiC Composites Under Thermal Gradient Conditions at 2700F in Air

Ceramic matrix composites (CMCs) such as SiCSiC are currently being designed and implemented in high temperature sections of aerospace turbine engines. Such components will be subject to through-thickness thermal gradients, which may affect the durability. In this study, SiCSiC CMCs with a hybrid chemical vapor infiltrated (CVI) and polymer infiltration and pyrolysis (PIP) matrix were loaded in tension while one surface was heated with a laser and the opposite surface was cooled. The samples were each coated with an environmental barrier coating (EBC), which was produced by electron beam physical deposition (EBPVD). Results for CMCs tested with and without the EBC be discussed.

Ceramic matrix composite↗

NASA NTRS2017

Advanced Environmental Barrier Coating Development for SiC-SiC Ceramic Matrix Composite Components

This presentation reviews the NASA advanced environmental barrier coating (EBC) system development for SiC-SiC Ceramic Matrix Composite (CMC) combustors particularly under the NASA Environmentally Responsible Aviation, Fundamental Aeronautics and Transformative Aeronautics Concepts Programs. The emphases have been placed on the current design challenges of the 2700-3000F capable environmental barrier coatings for low NOX emission combustors for next generation turbine engines by using advanced plasma spray based processes, and the coating processing and integration with SiC-SiC CMCs and component systems. The developments also have included candidate coating composition system designs, degradation mechanisms, performance evaluation and down-selects; the processing optimizations using TriplexPro Air Plasma Spray Low Pressure Plasma Spray (LPPS), Plasma Spray Physical Vapor Deposition and demonstration of EBC-CMC systems. This presentation also highlights the EBC-CMC system temperature capability and durability improvements under the NASA development programs, as demonstrated in the simulated engine high heat flux, combustion environments, in conjunction with high heat flux, mechanical creep and fatigue loading testing conditions.

CMAS↗

NASA NTRS2017

Oxidation of Alumina-Forming MAX Phases in Turbine Environments

Protective coatings for high temperature turbine components are based on YSZ thermal barriers and oxidation resistant, alumina-forming NiAl or NiCoCrAlY bond coats. Ti2AlC and Cr2AlC MAX phases are thus of special interest because of good oxidation resistance and CTE that can match Al2O3 and YSZ. Their alumina scales grow according to cubic kinetics due to grain growth in the scale, with initial heating dominated by fast TiO2 growth. Protective cubic kinetics are also found in high pressure burner rig tests of MAXthal 211 Ti2AlC, but with reduced rates due to volatile TiO(OH)2 formation in water vapor. YSZ-coatings on bulk Ti2AlC exhibit remarkable durability up to 1300C in furnace tests and at least a 25x life advantage compared to superalloys. At another extreme, Cr2AlC is resistant to low temperature Na2SO4 hot corrosion and exhibits thermal cycling stability bonded to a superalloy disk material. Accordingly, sputtered Cr2AlC coatings on disk specimens prevented hot corrosion detriments on LCF. Breakaway oxidation (Ti2AlC), scale spallation (Cr2AlC), interdiffusion, and processing as coatings still present serious challenges. However the basic properties of MAX phases provide some unusual opportunities for use in high temperature turbines.

ceramics↗

NASA NTRS2017

Cyclic Fatigue Durability of Uncoated and EBC Coated 3D SiC/SiC Composites Under Thermal Gradient Conditions at 2700F in Air

Ceramic matrix composites (CMCs) such as SiC/SiC are currently being designed and implemented in high temperature sections of aerospace turbine engines. Such components will be subject to through-thickness thermal gradients, which may affect the durability. In this study, SiC/SiC CMCs with a hybrid chemical vapor infiltrated (CVI) and polymer infiltration and pyrolysis (PIP) matrix were loaded in tension while one surface was heated with a laser and the opposite surface was cooled. Issues associated with laser testing will be discussed, along with initial results for coated and uncoated samples.

Ceramic matrix composite↗

NASA NTRS2017

Environmental Stability and Oxidation Behavior of HfO2-Si and YbGd(O) Based Environmental Barrier Coating Systems for SiCSiC Ceramic Matrix Composites

Ceramic environmental barrier coatings (EBC) and SiCSiC ceramic matrix composites (CMCs) will play a crucial role in future aircraft propulsion systems because of their ability to significantly increase engine operating temperatures, improve component durability, reduce engine weight and cooling requirements. Advanced EBC systems for SiCSiC CMC turbine and combustor hot section components are currently being developed to meet future turbine engine emission and performance goals. One of the significant material development challenges for the high temperature CMC components is to develop prime-reliant, environmental durable environmental barrier coating systems. In this paper, the durability and performance of advanced Electron Beam-Physical Vapor Deposition (EB-PVD) NASA HfO2-Si and YbGdSi(O) EBC bond coat top coat systems for SiCSiC CMC have been summarized. The high temperature thermomechanical creep, fatigue and oxidation resistance have been investigated in the laboratory simulated high-heat-flux environmental test conditions. The advanced NASA EBC systems showed promise to achieve 1500C temperature capability, helping enable next generation turbine engines with significantly improved engine component temperature capability and durability.

Ceramic Matrix Composites↗

NASA NTRS2016

Microstructure Evolution and Durability of Advanced Environmental Barrier Coating Systems for SiC/SiC Ceramic Matrix Composites

Environmental barrier coated SiC-SiC ceramic matrix composites (CMCs) systems will play a crucial role in next generation turbine engines for hot-section component applications because of their ability to significantly increase engine operating temperatures with improved efficiency, reduce engine weight and cooling requirements. Advanced HfO2 and rare earth silicate environmental barrier coatings (EBCs), along with multicomponent hafnium and rare earth silicide EBC bond coats have been developed. The coating degradation mechanisms in the laboratory simulated engine thermal cycling, and fatigue-creep operating environments are also being investigated. This paper will focus on the microstructural and compositional evolutions of an advanced environmental barrier coating system on a SiC-SiC CMC substrate during the high temperature simulated durability tests, by using a Field Emission Gun Scanning Electron Microscopy, Energy Dispersive Spectroscopy (EDS) and Wavelength Dispersive Spectroscopy (WDS). The effects of Calcium-Magnesium-Alumino-Silicate (CMAS) from road sand or volcano-ash deposits on the degradation mechanisms of the environmental barrier coating systems will also be discussed. The detailed analysis results help understand the EBC-CMC system performance, aiming at the durability improvements to achieve more robust, prime-reliant environmental barrier coatings.

ceramic matrix composites↗

NASA NTRS2016

Performance and Durability of Environmental Barrier Coatings on SiC/SiC Ceramic Matrix Composites

This presentation highlights advanced environmental barrier coating (EBC) and SiC-SiC Ceramic Matrix Composites (CMC) systems for next generation turbine engines. The emphasis will be placed on fundamental coating and CMC property evaluations; and the integrated system performance and degradation mechanisms in simulated laboratory turbine engine testing environments. Long term durability tests in laser rig simulated high heat flux the rmomechanical creep and fatigue loading conditions will also be presented. The results can help improve the future EBC-CMC system designs, validating the advanced EBC-CMC technologies for hot section turbine engine applications.

Environment and Fatigue↗

NASA NTRS2016

Combined Thermomechanical and Environmental Durability of Environmental Barrier Coating Systems on SiC/SiC Ceramic Matrix Composites

Environmental barrier coatings (EBCs) and SiC/SiC ceramic matrix composites (CMCs) will play a crucial role in next generation turbine engines for hot-section component applications. The development of prime-reliant environmental barrier coatings is essential to the EBC-CMC system durability, ensuring the successful implementations of the high temperature and lightweight engine component technologies for engine applications.This paper will emphasize recent NASA environmental barrier coating and CMC developments for SiC/SiC turbine airfoil components, utilizing advanced coating compositions and processing methods. The emphasis has been particularly placed on thermomechanical and environment durability evaluations of EBC-CMC systems. We have also addressed the integration of the EBCs with advanced SiC/SiC CMCs, and studied the effects of combustion environments and Calcium-Magnesium-Alumino-Silicate (CMAS) deposits on the durability of the EBC-CMC systems under thermal gradient and mechanical loading conditions. Advanced environmental barrier coating systems, including multicomponent rare earth silicate EBCs and HfO2-Si based bond coats, will be discussed for the performance improvements to achieve better temperature capability and CMAS resistance for future engine operating conditions.

Ceramic Matrix Composites↗

NASA NTRS2016

Advanced Environmental Barrier Coating Development for SiC-SiC Ceramic Matrix Composite Components

This presentation reviews the NASA advanced environmental barrier coating (EBC) system development for SiCSiC Ceramic Matrix Composite (CMC) components for next generation turbine engines. The emphasis has been placed on the current design challenges of the 2700F environmental barrier coatings; coating processing and integration with SiCSiC CMCs and component systems; and performance evaluation and demonstration of EBC-CMC systems. This presentation also highlights the EBC-CMC system temperature capability and durability improvements through advanced compositions and architecture designs, as shown in recent simulated engine high heat flux, combustion environment, in conjunction with mechanical creep and fatigue loading testing conditions.

Simulated Engine Test↗

NASA NTRS2016

Thermomechanical and Environmental Durability of Environmental Barrier Coated Ceramic Matrix Composites Under Thermal Gradients

This paper presents the developments of thermo-mechanical testing approaches and durability performance of environmental barrier coatings (EBCs) and EBC coated SiCSiC ceramic matrix composites (CMCs). Critical testing aspects of the CMCs will be described, including state of the art instrumentations such as temperature, thermal gradient, and full field strain measurements; materials thermal conductivity evolutions and thermal stress resistance; NDE methods; thermo-mechanical stress and environment interactions associated damage accumulations. Examples are also given for testing ceramic matrix composite sub-elements and small airfoils to help better understand the critical and complex CMC and EBC properties in engine relevant testing environments.]

Enviornmental Barrier Coatings↗

NASA NTRS2016

Development Status and Performance Comparisons of Environmental Barrier Coating Systems for SiCSiC Ceramic Matrix Composites

Environmental barrier coatings (EBC) and SiCSiC ceramic matrix composites (CMCs) will play a crucial role in future aircraft turbine engine systems, because of their ability to significantly increase engine operating temperatures, reduce engine weight and cooling requirements. This paper presents current NASA EBC-CMC development emphases including: the coating composition and processing improvements, laser high heat flux-thermal gradient thermo-mechanical fatigue - environmental testing methodology development, and property evaluations for next generation EBC-CMC systems. EBCs processed with various deposition techniques including Plasma Spray, Electron Beam - Physical Vapor Deposition, and Plasma Spray Physical Vapor Deposition (PS-PVD) will be particularly discussed. The testing results and demonstrations of advanced EBCs-CMCs in complex simulated engine thermal gradient cyclic fatigue, oxidizing-steam and CMAS environments will help provide insights into the coating development strategies to meet long-term engine component durability goals.

Processing and Properties↗

NASA NTRS2014

Calcium-Magnesium-Aluminosilicate (CMAS) Infiltration and Cyclic Degradations of Thermal and Environmental Barrier Coatings in Thermal Gradients

In a continuing effort to develop higher temperature capable turbine thermal barrier and environmental barrier coating systems, Calcium-Magnesium-Aluminosilicate (CMAS) resistance of the advanced coating systems needs to be evaluated and improved. This paper highlights some of NASA past high heat flux testing approaches for turbine thermal and environmental barrier coatings assessments in CMAS environments. One of our current emphases has been focused on the thermal barrier - environmental barrier coating composition and testing developments. The effort has included the CMAS infiltrations in high temperature and high heat flux turbine engine like conditions using advanced laser high heat flux rigs, and subsequently degradation studies in laser heat flux thermal gradient cyclic and isothermal furnace cyclic testing conditions. These heat flux CMAS infiltration and related coating durability testing are essential where appropriate CMAS melting, infiltration and coating-substrate temperature exposure temperature controls can be achieved, thus helping quantify the CMAS-coating interaction and degradation mechanisms. The CMAS work is also playing a critical role in advanced coating developments, by developing laboratory coating durability assessment methodologies in simulated turbine engine conditions and helping establish CMAS test standards in laboratory environments.

Thermal Barrier Coatings↗

NASA NTRS2013

Absolute Thickness Measurements on Coatings Without Prior Knowledge of Material Properties Using Terahertz Energy

This study investigates the applicability of a novel noncontact single-sided terahertz electromagnetic measurement method for measuring thickness in dielectric coating systems having either dielectric or conductive substrate materials. The method does not require knowledge of the velocity of terahertz waves in the coating material. The dielectric coatings ranged from approximately 300 to 1400 m in thickness. First, the terahertz method was validated on a bulk dielectric sample to determine its ability to precisely measure thickness and density variation. Then, the method was studied on simulated coating systems. One simulated coating consisted of layered thin paper samples of varying thicknesses on a ceramic substrate. Another simulated coating system consisted of adhesive-backed Teflon adhered to conducting and dielectric substrates. Alumina samples that were coated with a ceramic adhesive layer were also investigated. Finally, the method was studied for thickness measurement of actual thermal barrier coatings (TBC) on ceramic substrates. The unique aspects and limitations of this method for thickness measurements are discussed.

Nondestructive evaluation↗