The mission of the Life Science Division at the NASA Ames Research Center is to investigate the effects of gravity on living systems in the spectrum from cells to humans. The range of these investigations is from microgravity, as experienced in space, to Earth's gravity, and hypergravity. Exposure to microgravity causes many physiological changes in humans and other mammals including a headward shift of body fluids, atrophy of muscles - especially the large muscles of the legs - and changes in bone and mineral metabolism. The high cost and limited opportunity for research experiments in space create a need to perform ground based simulation experiments on Earth. Models that simulate microgravity are used to help identify and quantify these changes, to investigate the mechanisms causing these changes and, in some cases, to develop countermeasures.

Mulenburg, G. M.↗

NASA NTRS1984

Binder for Carbon-Fiber Coating

Insoluble, even coating formed by soaking in polyacrylic acid. Carbon fiber material prepared by soaking in solution of 20 percent polyacrylic acid in water. Material blotted and dried at 120 degrees C for at least 2 hours. Dried material reacted with boiling aqueous solution of calcium acetate. Treated material removed from boiling solution, blotted, dried at 120 degrees C, washed with distilled water, and dried again.

Dowler, W. L.↗

NASA NTRS1984

Off-axis tensile properties and fracture in a unidirectional graphite/polyimide composite (Celion 6000/PMR 15)

Tensile properties of unidirectional Celion 6000 graphite/PMR 15 polyimide composites prepared by hot molding and cold molding processes were measured at room temperature and 316 C, the upper use temperature of the polyimide resin, at both 45 and 90 deg to the fiber axis. The resulting fractures were characterized by scanning electron microscopy and materialographic techniques. Variation in tensile properties with processing history occurred in the elastic modulus and strain to failure for specimens loaded at 90 deg at 316 C, and in the fracture stress, and hence the in-plane shear stress, for those loaded at 45 deg at room temperature. Significant plastic deformation was observed in the 45 deg orientation at 316 C for material produced by both processing methods. In general, fracture occurred by both failure within the matrix and at the fiber-matrix interface; the degree of interfacial failure increased with temperature. Secondary cracking below the primary fracture surface was also observed.

Harper, J.↗