DOE OSTI2024

The effect of stretching on polyamide – 6: assessment of crystallinity, mechanical properties, and surface roughness

Polyamide-6 (PA6), or nylon-6, is a widely used low-cost polymer material for various applications. Manufacturing PA6 into fibers involves a spinning process such as melt extrusion, which orients the polymer chains into a semicrystalline structure. When stretching the produced fibers to high strains, the PA6 fibers transition the metastable gamma phase back into the stable gamma phase. The effects of these large stretches on mechanical properties have not been explored after the stretch has been released. In this study, the effects on mechanical properties were studied by stretching the PA6 fibers from 10% to 50% tensile strain and subsequently releasing the fibers. The stretched fibers were characterized by X-ray diffraction and atomic force microscopy to determine the changes to the crystal structure and surface roughness. The stretched fibers were then tensile tested to failure and the tensile properties were examined. The stress-strain curves on the post-stretched PA6 fibers showed clear softening in the fibers with lower initial moduli after 30% stretching. Furthermore, these results may hold a clue to softening of fibers in applications with repeated loading and have implications for mechanical stability and fatigue of this polymeric material.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Evaluating consumer 3D printing nozzles as a low cost alternative for mesophase pitch-derived carbon fiber production

Synthetic fibers, such as Kevlar fibers, SiC fibers, and carbon fibers, are essential components for constructing high performance structures. Whether for engineering, sports, energy storage (batteries and supercapacitors), or aerospace applications, fiber microstructure plays a critical role in fiber properties and functionalities. However, studying fiber nozzle configurations and spinning parameters to achieve the desired microstructure remains challenging, costly, and time consuming. Here, mesophase pitch-derived fibers were used as an example to demonstrate that low cost, commercially available 3D printer nozzles can “print” fibers. Four different nozzles were used to “print” fibers and the effects of their features on fiber properties were observed and compared to other lab spun and commercial pitch- derived CF. A longer orifice length resulted in higher modulus fiber whereas a larger draw-down ratio yielded a stronger fiber. Furthermore, the findings provide a new opportunity for 3D printer hardware application and open up opportunities for developing low-cost fibers.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Analysis of the turbostratic structures in PAN-based carbon fibers with wide-angle x-ray diffraction

Carbon fiber (CF) is a versatile material renowned for its excellent mechanical, thermal, and electrical properties. Polyacrylonitrile (PAN)-based CFs dominate the market due to their high tensile strength, rendering them suitable for structural applications in a wide variety of applications ranging from sporting goods to aerospace. Over five decades of commercial development of PAN-based CF has resulted in a range of varieties with different tensile moduli and tensile strengths. The microstructures, nanostructures, and crystal structures of PAN-based CF play pivotal roles in the macroscale properties of this material. In particular, the crystal structure and crystallite orientation in CF is closely related to the mechanical properties. The crystal structure of PAN-based CF generally consists of turbostratic carbon, which is a disordered form of graphite, the characteristics of which can be effectively characterized in a bulk format through wide-angle x-ray diffraction (WAXD). In this work, we employed a three-part approach to the analysis of WAXD patterns collected from four intermediate modulus PAN-based CFs. The approach incorporates a Scherrer analysis, a Debye analysis, and an orientational analysis to provide precise estimates of crystallite sizes, crystallite distributions, and crystallite orientations with the fiber axis. Furthermore, the results presented here suggest that intermediate modulus PAN-based CF mostly consists of small turbostratic crystallites (<4 nm), with larger crystallites having increased orientation with the fiber axis. The results here imply the presence of curvature and/or wrinkling of the turbostratic layers within the CF structure.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Effect of tension during sulfonation stabilization for UHMWPE-derived carbon fibers

Polyethylene is a promising low-cost alternative precursor material for carbon fiber production, but it has yet to show mechanical properties near or surpassing polyacrylonitrile-derived carbon fibers. The high molecular weight and order of ultra-high molecular weight polyethylene (UHMWPE) may offer a pathway to realizing this promise by enabling long-range graphitic structure formation and superior mechanical properties. The tension applied during the precursor stabilization process is crucial to maintaining the shape of the fibers during the conversion process, but no published study has yet probed the relationship between sulfonation tension and carbon fiber microstructure and mechanical properties. In this work, a logarithmic sweep of tensile stress was applied to UHMWPE fibers during the stabilization process followed by carbonization. Increasing tension significantly reduced fiber shrinkage, resulted in straighter fibers with less severe kink bands, and greatly improved the mechanical properties of the fibers. Raman spectroscopy and X-ray diffraction revealed that in all cases the carbon fibers were largely amorphous, but increasing tension resulted in increased size and alignment of the turbostratic crystallites with the fiber axis. Large voids were present in the sample fibers, so the Griffith-Irwin relation was employed to predict the potential ultimate tensile strength of the fibers with voids reduced to sizes comparable to commercially produced fibers. Furthermore, this work demonstrates the importance of tension applied during the stabilization of polyethylene fibers for carbon fiber production and establishes a framework for achieving high mechanical properties from these precursors.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Influence of Oxygen Uptake on Pitch Carbon Fiber

Carbon fiber precursor materials, such as polyacrylonitrile, pitch, and cellulose/rayon, require thermal stabilization to maintain structural integrity during conversion into carbon fiber. Thermal stabilization mitigates undesirable decomposition and liquification of the fibers during the carbonization process. Generally, the thermal stabilization of mesophase pitch consists of the attachment of oxygen-containing functional groups onto the polymeric structure. In this study, the oxidation of mesophase pitch precursor fibers at various weight percentage increases (1, 3.5, 5, 7.5 wt%) and temperatures (260, 280, 290 °C) using in situ differential scanning calorimetry and thermogravimetric analysis is investigated. The results are analyzed to determine the effect of temperature and weight percentage increase on the stabilization process of the fibers, and the fibers are subsequently carbonized and tested for tensile mechanical performance. Finally, the findings provide insight into the relationship between stabilization conditions, fiber microstructure, and mechanical properties of the resulting carbon fibers.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Unveiling the microstructural evolution of carbon fibers derived from polyamide-6

Polyacrylonitrile-based carbon fibers have dominated the industry for decades, but the high cost of polyacrylonitrile has prevented the widespread adoption of carbon fiber in high-volume structural applications. As such, a significant amount of research has been dedicated to finding an alternative, low-cost carbon fiber precursor. In this work, carbon fibers were produced from polyamide-6 using metal salt impregnation and a thermo-oxidative stabilization step. To gain further insight into the carbonization process and microstructural transformation, the morphologies, crystallinities, elemental compositions, and thermal stabilities of the fibers were characterized at various stages of processing. The stabilization step resulted in a significant increase in carbon yield, indicating a dramatic increase in thermal stability. This is due to the crosslinking of polyamide-6 chains, which was confirmed by functional group analysis. The crystallinity of the fibers was also significantly altered during processing, as the produced carbon fibers consisted of pseudo-amorphous carbon with two distinct regions of metal salt impregnation. Finally, the findings and microstructural evolution mechanisms provide guidelines for further research into carbon fiber produced from polyamide-6.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Extracting single fiber transverse and shear moduli from off-axis misalignment fiber tensile testing

Small diameter (<100 μm) fibers (e.g. carbon fibers, Kevlar, and fiberglass) and wires (e.g. ultrafine copper and aluminum wires) are frequently used in many different engineering applications, such as for light weighting structures, electromagnetic shielding for aircraft/infrastructure/EVs, vibration damping, biological sensors, aerospace electrical devices, and electric windings just to name a few. Due to the manufacturing process, the fibers and wires are pulled and stretched to produce a preferential alignment. Therefore, thin fibers and wires typically display different properties along the length of the fiber as opposed to their cross section and many fibers/wires are considered transversely isotropic. The axial properties of fibers/wires can be ascertained via tensile testing of single-filaments or fiber tows, but the radial properties require much more effort to measure. Knowing these properties is important for the accurate prediction of micromechanical models and manipulation of fibers during micromanufacturing. In this paper, a new technique was developed to determine the transverse/shear moduli and strength of a material by conducting tensile tests of the material at increasing misalignment angles from the tensile axis. Due to the transversely isotropic nature of the material, the transverse/shear moduli and strength influence the experimental results recorded by the test machine to different degrees based on the amount of misalignment in the test setup. An equation was derived to determine the influence of each of the material properties based on the misalignment angle by manipulating the stiffness matrix for transversely isotropic materials using the transformation matrices. Then, curve fitted coefficients were used to identify the material properties. Here, the strengths were similarly determined by curve fitting an off-axis Tsai-Hill failure criteria to determine the influence of transverse, shear, and tensile strengths based on the complex loading condition provided by the off-axis tensile test. Zoltek Panex 35 carbon fibers were used to demonstrate this new technique and the determined properties were then compared to those obtained from nanoindentation and from literature. Fracture surfaces provide insight into the different failure mechanisms at various misalignment angles.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Carbon fibers derived from commodity polymers: A review

Carbon fiber composites are prohibitively expensive for a wide array of applications that would greatly benefit from their superior specific strength and specific stiffness. Replacing the market-dominant carbon fiber precursor material, polyacrylonitrile, with a low-cost alternative would significantly reduce the cost of carbon fiber production. Commodity polymers may provide such an alternative thanks to their abundance and ease of production into fibers. Furthermore, this review presents state-of-the-art carbon fiber production from polyacrylonitrile, an overview of melt-spinnable alternative precursors broadly, and an in-depth review of the latest advances in the synthesis of carbon fibers from low-cost, commodity thermoplastics such as polyethylene, polyamide, polystyrene, polyester, and poly(vinyl chloride).

36 MATERIALS SCIENCE↗

DOE OSTI2021

Unveiling damage mechanisms of chromium-coated zirconium-based fuel claddings at LWR operating temperature by in-situ digital image correlation

Here, we investigate the coupled thermomechanical fracture mechanisms of coated nuclear fuel claddings at Light Water Reactor (LWR) operating temperatures. These coated claddings are a highly attractive, near-term solution, which addresses the demands for accident-tolerant fuel systems and provide greater oxidation resistance. However, the fracture mechanisms of these coatings, which may create channels for oxidation ingression, must be fully understood prior to implementation. Thus, high-temperature expanding plug experiments were conducted on coated cladding specimens at a temperature of 315 °C, consistent with the operating environment of LWRs. Furthermore, in-situ thermomechanical deformation was measured with stereo digital image correlation during heating and mechanical testing to separately resolve contributions of thermal and mechanical strain. Digital image correlation, supported by acoustic emissions (AE) detection, was also leveraged to track cracking activity during loading. Coating fracture was found to initiate at total hoop strains of 0.34%. The thermal deformation of the coated claddings was investigated via finite element simulations, revealing a bidirectional stress-state within the coating with axial and circumferential strains of 0.026 and 0.031%. This bidirectional stress-state was attributed with the generation of off-axis fracture pattern within the coating as identified via post-experiment scanning electron microscopy. Thus, this study unveiled critical, coupled thermomechanical mechanisms governing the coating fracture of coated claddings at LWR temperatures.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Analyzing the effect of misalignment on single-filament carbon fiber tensile testing via stereoscopic computer vision imaging

An understanding of the constitutive properties of carbon fibers (CF) is critical to the accuracy of high-resolution composite simulations and to the development of CF derived from low-cost alternative precursor materials. Single-fiber tensile testing is a capable tool to measure CF properties and is well suited to research efforts where only a small number of fibers may be available. However, single-fiber tensile tests are challenging to conduct due to the difficulty in handling small diameter fibers (5-15 μm), the brittleness of single fibers, and the required nanoscale/microscale resolution of testing equipment. The accuracy of the measured properties depends on several factors, but a critical factor is fiber misalignment, especially at short gauge lengths. Current standards do not address the effect of tensile specimen misalignment on measured properties. Furthermore, this work presents a robust method of fiber alignment using stereoscopic computer vision that enables users to align fibers vertically for tensile testing to improve the accuracy of resulting mechanical properties. Additionally, an analytical relationship between fiber misalignment angle and measured properties is developed and validated against the experimental results. As a result, new best practices for single-fiber tensile testing of CF are recommended.

47 OTHER INSTRUMENTATION↗