NASA NTRS1987

NASCRAC - A computer code for fracture mechanics analysis of crack growth

NASCRAC - a computer code for fracture mechanics analysis of crack growth - is described in this paper. The need for such a code is increasing as requirements grow for high reliability and low weight in aerospace components. The code is comprehensive and versatile, as well as user friendly. The major purpose of the code is calculation of fatigue, corrosion fatigue, or stress corrosion crack growth, and a variety of crack growth relations can be selected by the user. Additionally, crack retardation models are included. A very wide variety of stress intensity factor solutions are contained in the code, and extensive use is made of influence functions. This allows complex stress gradients in three-dimensional crack problems to be treated easily and economically. In cases where previous stress intensity factor solutions are not adequate, new influence functions can be calculated by the code. Additional features include incorporation of J-integral solutions from the literature and a capability for estimating elastic-plastic stress redistribution from the results of a corresponding elastic analysis. An example problem is presented which shows typical outputs from the code.

Harris, D. O.↗

NASA NTRS1986

A review of fracture mechanics life technology

Lifetime prediction technology for structural components subjected to cyclic loads is examined. The central objectives of the project are: (1) to report the current state of the art, and (2) recommend future development of fracture mechanics-based analytical tools for modeling subcritical fatigue crack growth in structures. Of special interest is the ability to apply these tools to practical engineering problems and the developmental steps necessary to bring vital technologies to this stage. The authors conducted a survey of published literature and numerous discussions with experts in the field of fracture mechanics life technology. One of the key points made is that fracture mechanics analyses of crack growth often involve consideration of fatigue and fracture under extreme conditions. Therefore, inaccuracies in predicting component lifetime will be dominated by inaccuracies in environment and fatigue crack growth relations, stress intensity factor solutions, and methods used to model given loads and stresses. Suggestions made for reducing these inaccuracies include development of improved models of subcritical crack growth, research efforts aimed at better characterizing residual and assembly stresses that can be introduced during fabrication, and more widespread and uniform use of the best existing methods.

Besuner, P. M.↗

NASA NTRS1985

Predicting the Fatigue life of Structures

Report reviews fracture-mechanics technology for predicting life expectancy of structural components subjected to cyclic loads. Report covers analytical tools for modeling and forecasting subcritical fatigue-crack growth in structures. It emphasizes use of tools in practical, day-to-day problems of engineering design, development, and decisionmaking.

Besuner, P. M.↗

NASA NTRS1985

A review of fracture mechanics life technology

Current lifetime prediction technology for structural components subjected to cyclic loads was reviewed. The central objectives of the project were to report the current state of and recommend future development of fracture mechanics-based analytical tools for modeling and forecasting subcritical fatigue crack growth in structures. Of special interest to NASA was the ability to apply these tools to practical engineering problems and the developmental steps necessary to bring vital technologies to this stage. A survey of published literature and numerous discussions with experts in the field of fracture mechanics life technology were conducted. One of the key points made is that fracture mechanics analyses of crack growth often involve consideration of fatigue and fracture under extreme conditions. Therefore, inaccuracies in predicting component lifetime will be dominated by inaccuracies in environment and fatigue crack growth relations, stress intensity factor solutions, and methods used to model given loads and stresses. Suggestions made for reducing these inaccuracies include: development of improved models of subcritical crack growth, research efforts aimed at better characterizing residual and assembly stresses that can be introduced during fabrication, and more widespread and uniform use of the best existing methods.

Thomas, J. M.↗

NASA NTRS1972

Detection of fiber cracking by acoustic emission.

A theoretical model is presented that relates acoustic emission to fiber cracking which occurs during a rising load tension test on a fiber reinforced composite. The percentage of broken fibers in an Al3Ni fiber reinforced aluminum was measured as a function of tensile strain by optical inspection of the polished surface of strained specimens. This information was used in conjunction with the proposed model to predict the acoustic emission response of the composite material. These predictions were compared with experimental observations, and a good agreement was obtained between the two sets of results. These results indicate that it is possible to relate acoustic emission quantitatively to the micromechanics of the deformation processes occurring within fiber reinforced composites, thereby demonstrating the applicability of acoustic emission to materials studies and also to nondestructive evaluation of the integrity of composite materials.

Harris, D. O.↗