α Irradiation Response on the Electronic Transport Properties of p -B 12 P 2
B 12 P 2 , a wide bandgap semiconductor, has been previously reported to self-heal from high-energy electron bombardment as determined from transmission electron microscopy. However, the effect of irradiation on the electronic transport properties of B 12 P 2 has not been studied. We report electrical transport measurements on B 12 P 2 after α irradiation. The temperature-dependent Hall effect was measured on p-type B 12 P 2 after successive α irradiation from 210 Po over a fluence range of 1 × 10 11 –1 × 10 13 α/cm 2 to test for self-healing of B 12 P 2 to α bombardment. Prior to irradiation, B 12 P 2 displayed electrical transport characteristics of both hopping and impurity/defect band conduction due to background impurities and growth-induced defects. Fluences of 5 × 10 12 α/cm 2 or greater caused a decrease in the hole mobility and an increase in defect band conduction, suggesting defect accumulation in B 12 P 2 .