Hatzell, Marta C.

Publications and source records attributed to Hatzell, Marta C..

9 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Physical and Electrochemical Characterization of Aluminum Electrodes during Electrocoagulation

Electrocoagulation (EC) of synthetic groundwater was conducted using a sacrificial aluminum electrode in a flow-through EC reactor with short retention times (<1 min) under varying hydrodynamic and electrochemical conditions. The treated water was allowed to settle for 24 h and achieved silicate removal of up to 50 ± 4%, and hardness removal of 11 ± 1%. Physical, chemical, and electrochemical characterization was performed to explore changes in electrode surface morphology and composition. Electrochemical impedance spectroscopy (EIS) showed that chemical reactions at the electrode/water interface are sensitive to changes in the immediate chemical environment. We demonstrate that the most energy-intensive step in EC is aluminum dissolution at the anode, which remained fairly constant due to the continuous renewal of the anode’s surface, a result of aluminum dissolution. At the cathode, a structural change in the oxide layer, from γ-Al 2 O 3 to gibbsite, was detected by grazing-incidence X-ray diffraction, which decreased the resistance to charge transfer at the cathode surface, resulting in decreased electrode resistance. The high flow rate in the system minimized the accumulation of aluminum hydroxide solids and aluminum ions at the electrode/water interface, which minimized the formation of thick scalants and amorphous Al(OH) 3 on the cathode and anode, respectively. In conclusion, it was further demonstrated by EIS that under these conditions the resistance to charge transfer was constant throughout the duration of the experiment.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Atomically Ordered PdCu Electrocatalysts for Selective and Stable Electrochemical Nitrate Reduction

Electrochemical nitrate reduction (NO 3 RR) has attracted attention as an emerging approach to mitigate nitrate pollution in groundwater. Here, we report that a highly ordered PdCu alloy-based electrocatalyst exhibits selective (91% N 2 ), stable (480 h), and near complete (94%) removal of nitrate without loss of catalyst. In situ and ex situ XAS provide evidence that structural ordering between Pd and Cu improves long-term catalyst stability during NO 3 RR. In contrast, we also report that a disordered PdCu alloy-based electrocatalyst exhibits non-selective (44% N 2 and 49% NH 4 + ), unstable, and incomplete removal of nitrate. The copper within disordered PdCu alloy is vulnerable to accepting electrons from hydrogenated neighboring Pd atoms. This resulted in copper catalyst losses which were 10× greater than that of the ordered catalyst. The design of stable catalysts is imperative for water treatment because loss of the catalyst adds to the system cost and environmental impacts.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Challenges and Roadmap for Solar-Thermal Desalination

Decarbonizing desalination systems requires combining renewable energy technologies with desalination systems. Solar thermal desalination, which combines a thermal desalination system (e.g., distillation, multistage flash, etc.) with a concentrated solar system is attractive in geographic regions with an abundance of saline water and solar energy. However, the high economic cost and low efficiency limits its adoption. This review provides an overview of the techno-economic, materials, and performance challenges that need to be overcome to realize solar-desalination. The review describes the four most prominent pathways for overcoming thermodynamic and cost limitations present in current systems. Specifically, methodologies and approaches such as direct solar evaporation structures, low-cost thermal energy storage, solar cogeneration schemes for power and desalination, and solar hybrid desalination are discussed. Furthermore, these strategies can enable solar thermal desalination technologies that are resilient to intermittent solar energy.

14 SOLAR ENERGY↗
DOE OSTI2022

PdCu Electrocatalysts for Selective Nitrate and Nitrite Reduction to Nitrogen

Electrocatalytic conversion of nitrate in waste can enable efficient waste remediation (NO 3 - to N 2 ) or waste valorization (NO 3 - to NH 4 + ) depending on the selectivity of the catalyst. Palladium and copper electrocatalysts typically exhibit ideal nitrate and nitrite binding properties, allowing for effective destruction of nitrate. However, rational steering of selectivity through material design remains a critical challenge for PdCu electrocatalyst. Here, we use the electrochemical underpotential deposition method to synthesize palladium nanocube electrocataysts with controlled copper surface coverage (e.g., partial and full copper coatings). We then examine the potential for NO 3 - destruction (conversion) and NO 2 - reduction reaction. We identify that partial copper-coated Pd nanocubes not only effectively facilitate the reduction of 95% of NO 3 - but also increase the reduction of NO 2 - to N 2 with 89% selectivity over 20 consecutive cycles (80 h). We also show that under these conditions, the Pd(100) surface facet is exposed. Complete copper-covered Pd nanocubes effectively facilitate the reduction of ~99% of NO 3 - . Complete coverage of copper; however, prevented exposure of Pd(100) surface facet, promoting the selective reduction of NO 2 - to NH 4 + with a 70% selectivity over 20 consecutive cycles (80 h). Density functional theory (DFT) calculations show that NO 3 - and NO 2 - adsorb more strongly on the Cu(100) surface compared to the Pd(100) surface, while the NO* intermediate generated from NO 3 - or NO 2 - reduction adsorbs more strongly on the Pd surface. Furthermore, barrier calculations show that NO* can readily migrate from the Cu domain to the Pd domain and that the N–N coupling barrier on Pd is significantly diminished at high NO* coverage. Together, these results suggest that the high N 2 selectivity observed on the PdCu electrocatalyst is caused by the spillover of NO* from the Cu domains to the Pd domains.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Neutron tomography of porous aluminum electrodes used in electrocoagulation of groundwater

In this work, neutron computed tomography (CT) is employed to investigate the dissolution of porous aluminum electrodes during electrocoagulation (EC). Porous electrodes were chosen in efforts to reduce electric power requirements by using larger surface-area electrodes, having both inner and outer surface, for the EC process. Neutron CT allowed 3D reconstruction of the porous electrodes, and image analysis provided the volume of each electrode vs. thickness, which can indicate whether the inner surface is effectively involved in EC reactions. For the anode, the volume decreased uniformly throughout the thickness of the electrode, indicating that both the outer and inner surface participated in electrochemical dissolution, while the volume of the cathode increased uniformly vs. thickness, indicating deposition of material on both the outer and inner surface. The attenuation coefficient vs. thickness, increased for both anode and cathode, indicating surface chemistry changes. For the anode, the attenuation coefficient increased slightly but uniformly, probably due to aluminum oxide formation on the surface of the anode. For the cathode, the attenuation coefficient increased more than for the anode and nonuniformly. The higher increase in the attenuation coefficient for the cathode is due to precipitation of aluminum hydroxide on the electrode surface, which added hydrogen. Image analysis also showed that, although the attenuation coefficient increased throughout the thickness of the electrode, most of the hydroxide deposition occurred on the outer surface. Energy analysis showed that porous electrodes can be used to reduce process energy requirements by as much as 4 times compared to solid electrodes.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Electroprecipitation Mechanism Enabling Silica and Hardness Removal through Aluminum-Based Electrocoagulation

We evaluate the effectiveness of an aluminum-based electrocoagulation pretreatment system to remove dissolved silica and hardness. Silica and hardness limit water recovery during membrane-based desalination applications when silica and hardness exceed the solubility limit and generate scale on the membrane surface. We show that simultaneous removal of nearly all silica (95 ± 4%) and a significant amount of hardness (40–60%) occurs with a hydraulic residence time of 2 h and a charge loading between 0 and 1200 C/L. Increasing the residence time maximized the hardness removal (58 ± 8%) via the formation of larger flocs, which allowed for more constituent removal by gravity settling. We highlight the trade-offs between improved energy efficiency at lower charge loadings and an improved removal rate at a higher charge loading. We further compare the percentage of silica and hardness removed in multicomponent solutions and compare this to single component feed solution. We discuss the implications that operational considerations have in terms of cost and treatment capacity. Finally, a cost–benefit analysis comparing chemical coagulation with electrocoagulation indicates that electrocoagulation could be half the cost of chemical coagulation and could produce more stable effluent pH and conductivity.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Mechanocatalytic Ammonia Synthesis over TiN in Transient Microenvironments

Environmentally friendly and energy-efficient ways to produce ammonia are essential to meet global food demands. In this study, a new approach for ammonia production at nominally ambient conditions is introduced. As proof of concept, ammonia is synthesized mechanocatalytically by ball milling titanium in a continuous gas flow. The ammonia synthesis reaction is proposed to follow a transient Mars–van Krevelen mechanism under mechanically activated conditions, where molecular nitrogen incorporation into the titanium lattice and titanium nitride hydrogenation occur in thermodynamically distinct environments. X-ray powder diffraction and X-ray absorption spectroscopy confirm the formation of titanium nitride from titanium and N2. The reactivity of nitrided titanium supports that lattice nitrogen plays a role in ammonia formation. The in situ formed titanium nitride is catalytically active, and the nitride regeneration reaction is determined to be the rate-limiting step. A preliminary technoeconomic analysis shows that this approach could be feasible for distributed ammonia production.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗