Field retrieved photovoltaic backsheet survey from diverse climate zones: Analysis of degradation patterns and phenomena
Understanding the impact of climate stressors on photovoltaic (PV) backsheet degradation in real-use conditions is critical to improve the accelerated testing exposures, extend the backsheet lifetime, and increase the confidence in PV reliability. Here, in this work, a total of 33 PV module backsheets were retrieved from six climatic zones worldwide with 2 - 28 years of exposure. These modules included five types of backsheet air-side materials (or outer layer): poly(vinylidene fluoride) (PVDF), poly(tetrafluoroethylene-co-hexafluoropropylene-co-vinylidene fluoride) (THV), poly(vinyl fluoride) (PVF), poly(ethylene terephthalate) (PET), and polyamide (PA). Attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR) was used to identify air-side materials. The degradation induced color change, gloss loss, and chemical material changes analyzed using optical microscopy, differential scanning calorimetry (DSC), scanning electron microscopy (SEM), colorimetry (yellowness index (YI)), and gloss measurements. PVDF, THV, and PVF air-side layer backsheets, in particular PVF, had minimal degradation in the air-side layer appearance and chemical structures after exposure in different climatic zones. The PET air-side backsheets exhibited obvious color increase (22.55 YI units after about 9 years exposure) and the PA/PA/PA backsheets showed large gloss loss (up to 76.4 %) relative to the unexposed backsheets. Severe cracks between cells that penetrated through the entire thickness of backsheets are observed on PA/PA/PA backsheets after 4-6 years of exposure in 6 climatic zones. The current indoor exposure standards were not sufficient to identify this degradation type. However, fluoropolymer based PV backsheets showed lower levels of degradation predictors and increased climatic resistance. Specific samples (PVF) showed little change from baseline after 28 years of outdoor exposure.
Spatiotemporal Modeling of Real World Backsheets Field Survey Data: Hierarchical (Multilevel) Generalized Additive Models
Assessing photovoltaic module backsheet durability is critical to increasing module lifetime. Laboratory-based accelerating testing has recently failed to predict large scale failures of widely adopted polymeric materials. Additionally, there is a growing concern on characterizing the non-uniformity of field exposure. Therefore, data from field surveys are critical to assess the performance of component lifetimes. Using a documented field survey protocol, 19 field surveys were conducted. The focus of this survey strategy is to investigate spatial continuity in degradation modes. By combining field survey data with real-time satellite weather data, stressor / response models have been trained. Generalized additive Models (GAM) model was created to predict the value of degradation based on measured predictors. Two different GAM constructions were testing using different implementations of basis splines. The model includes variables on the environmental stressors of the system and the location of each measurement in the PV mounting structure. The incorporation of hierarchical structure into the models allowed for material specific degradation rates, while maintaining the assumption of a global trend. The model performed well with an adjusted R2 of 0.975 for yellowness index prediction.
Spatiotemporal Modeling of Real World Backsheets Field Survey Data: Hierarchical (Multilevel) Generalized Additive Models: Preprint
Assessing photovoltaic module backsheet durability is critical to increasing module lifetime. Lab based accelerating testing has recently failed to predict large scale failures of widely adopted polymeric materials. Field surveyed data is critical to assess the performance of component lifetime. Using a documented field survey protocol, 13 field surveys where conducted. Each measurement is encoded with it's spatial location in respect to the other modules. By combining field survey data on degradation predictors with real time satellite weather data, data-driven predictive models of backsheet degradation were trained. LOESS models were constructed to investigate the spatial dependence of measurements. It was found that micro-climatic effects like treelines, ground surface changes, and elevation changes effected the magnitude and variance of the measurements. A GAM model was created to predict the value of degradation based on measured predictors. The model includes variables on the climate of the system and the location of each measurement in the PV mounting structure. The model performed well with an adj:R2 of 0:95 for yellowness index prediction. The model was cross-validated using k-folds.
Spatio-Temporal Modeling of Field Surveyed Backsheet Degradation
Assessing photovoltaic module backsheet durability is critical to increasing module lifetime. Lab based accelerating testing has recently failed to predict large scale failures of widely adopted polymeric materials. Field surveyed data is critical to assess the performance of component lifetime. Using a documented field survey protocol, 13 field surveys where conducted. Each measurement is encoded with it's spatial location in respect to the other modules. By combining field survey data on degradation predictors with real time satellite weather data, data-driven predictive models of backsheet degradation were trained. LOESS models were constructed to investigate the spatial dependence of measurements. It was found that micro-climatic effects like tree-lines, ground surface changes, and elevation changes effected the magnitude and variance of the measurements. A GAM model was created to predict the value of degradation based on measured predictors. The model includes variables on the climate of the system and the location of each measurement in the PV mounting structure. The model performed well with an adj.R 2 of 0.95 for yellowness index prediction. The model was cross-validated using k-folds.
Measurement of crack length in width tapered beam experiments
The width tapered beam method for measuring fracture toughness has been contemplated for use in measuring the adhesion of photovoltaic materials, is promoted by it being a viable method for use directly on modules rather than to engineered test specimens. However, precise determination of crack length is often difficult as failure often involves tendril formation, cavitation voids, and other plastic deformation at the crack front in addition to obfuscation by opaque materials. Because fracture energy varies as the square of crack length, imprecise crack tip length results in large measurement uncertainties. In this work, we develop a method to estimate the crack tip length using the relationship between the applied force and the displacement of the load frame. The crack tip is determined for every data point and can be defined from a calibration curve related to the amount of energy put into the beam, or from a theoretically idealized estimation. Once a calibration curve is set up and the equations programmed, the fracture energy as a function of position on the newly formed crack interface can be accurately estimated. The test additionally provides much easier analysis and insight into the joint failure through more precise knowledge of fracture toughness at each de-bonded area.
Characterization of Real-World and Accelerated Exposed PV Module Backsheet Degradation
Backsheet degradation is key to maintaining the lifetime of photovoltaic (PV) modules. Cracking, delamination, bubbling, and discoloration are main types of degradation. PV modules were collected from PV installations in multiple climatic zones. Multiple types of backsheets were obtained with poly(ethylene teraphlate) (PET) and polyamide air side layers being the largest number of backsheets retrieved. Multiple commercial PV backsheets were exposed to multiple accelerated exposures and key degradation mechanisms were identified. Polyamide backsheets showed cracking in retrieved modules and under accelerated exposures. Poly(vinylidene fluoride) (PVDF) and poly(vinyl fluoride) (PVF) showed the highest stability in retrieved and accelerated exposures. While polyamide had the largest amount of large scale degradation.
Characterizing photovoltaic backsheet adhesion degradation using the wedge and single cantilever beam tests, Part I: Field Modules
Photovoltaic backsheets are exposed to harsh outdoor weathering conditions throughout their service lives that can compromise their protective function, through adhesive debonding between their constituent layers and between the backsheet and the module. We report a large-scale study on adhesive degradation was conducted on 37 field-exposed modules, that spanned 19 different module manufacturers, that were deployed among six Köppen–Geiger climatic zones, and that were fielded between 0 and 28 years. Six outer layer polymer classes were identified among the backsheets: polyamide (PA), polyethylene terephthalate (PET), polyvinyl fluoride (PVF), polyvinylidene fluoride (PVDF), fluoroethylene vinyl ether copolymer (FEVE), and tetrafluoroethylene hexafluoropropylene vinylidene fluoride copolymer (THV). Two adhesion tests were used to measure the adhesive strength: the wedge test and the width-tapered single-cantilever beam (SCB) test. Adhesion energies were compared across exposure time and Köppen–Geiger climatic zone. Many of the PET-, PVF-, and PVDF-based backsheets experienced degradation of the adhesive layer between the backsheet outer and core layers. A consistent trend of decreasing adhesion energy with exposure time was observed in five out of the six backsheet types. Trends among adhesion energy and climatic zone, while expected, were not observed, possibly due to broad ranges in temperature, humidity, and precipitation defining Köppen–Geiger climatic zones. The cantilever beam measurements produced an upper cutoff of approximately 100 J/m 2 , above which no modules exhibited field delamination. The results are part of a two-part study quantifying adhesion in both field-weathered and indoor-exposed PV backsheets.
Characterizing photovoltaic backsheet adhesion degradation using the wedge and single cantilever beam tests, Part II: Accelerated tests
Photovoltaic (PV) backsheets provide critical moisture, mechanical, and electrical insulation to the backside of PV modules, but their continued functionality depends upon their ability to remain well adhered over years of harsh environmental exposure. A study of adhesive strength was conducted on several PV backsheet types exposed to indoor accelerated weathering. Two adhesion tests – the wedge test and single cantilever beam test – were used to measure adhesion energy in four backsheets: two with fluoropolymer-based outer (airside) layers – polyvinyl fluoride (PVF), polyvinylidene fluoride (PVDF) – and two with non-fluoropolymer-based outer layers–polyamide (PA) and polyethylene terephthalate (PET). The effects of changes in temperature, ultraviolet (UV) irradiance, relative humidity, and a periodic water spray were studied. The PET-, PVF- and PVDF-based backsheets all showed instances of debonding in an adhesive layer, which is commonly reported. Furthermore, for the PA-, PET-, and PVDF-based backsheets, adhesion energy dropped fairly rapidly with exposure, reaching very low levels by 4000 h. The PVF-based backsheet was relatively robust to weathering. Pull-off of an outer chalking layer in the PA- and PET-based backsheets suggested a sensitivity to UV. Adhesion in these two backsheets was also highly sensitive to changes in moisture level. Changes in UV irradiance and temperature did not show a statistically significant effect on adhesion loss for the exposure levels used. The present work is part of a two-part adhesion study on both field-weathered and indoor-exposed backsheets, and forms a basis for understanding adhesion degradation across a variety of backsheet types and degradation factors.