Highly Specialized GSE Required for JWST Verification

Todays presentation will highlight development of the optical, mechanical, and thermal test systems for the OTIS cryotest

Havey, Keith↗

NASA NTRS1995

Effects of long term space environment exposure on optical substrates and coatings

At the time of our Second LDEF Post-Retrieval Symposium report, we had completed cleaning and measuring the post flight spectral performance of all of the samples except for the fused silica substrate with an antireflection (SiO2/TiO2) coating. As was documented in that report, after cleaning, all of the samples returned to their original pre-flight performance, with the exception of the fused silica anti-reflectance coated sample, which had significant degraded performance. All normal methods of removing the contaminant from the surface of this sample failed except for oxygen plasma etch. At the time of the previous report, we had only exposed the sample to three hours of plasma etch. We have since continued the plasma etch for a total of 32 hours, after which time, the transmission of the sample almost reached its pre-flight values. The peak areas of the transmission curves remained shifted approximately 150 nm. Of interest is the fact that the control samples, which hadn't flown, did not exhibit any spectral shifting. In summary, after the 6 yr exposure to the space environment, all of the coatings and substrates returned to their pre-flight performance after cleaning, with the exception of the antireflection coated fused silica sample. On this sample, the spectral transmission curves shifted approximately 150 nm.

Vallimont, John↗

NASA NTRS1991

Effects of long term exposure on optical substrates and coatings (SOO50-1)

The experiment consisted of fused silica and ultra low expansion (ULE(tm)) glass samples which were either uncoated or had high reflectance silver, antireflectance, or solar rejection coatings. A set of duplicate control samples was manufactured and stored in a controlled environment for comparison purposes. Data on the analysis of the contaminate deposited on the samples, micrometeoroid impact, and the environmental effects on the substrate materials and coatings are presented. Some results of particular interest are that the contaminate composition varied between different types of samples, fractures were incurred in the glass at the micrometeoroid impact site, and no darkening of the ULE(tm) glass occurred due to the radiation exposure.

Vallimont, John↗