Characterization of Precipitation-Strengthening Heat-Resistant Austenitic Stainless Steels for Life-Prediction Modeling

In this study, the role of minor alloying additions in 347H stainless steels (UNS34709, ASTM A240/240M) on creep-rupture properties at 650-750°C and microstructure evolution during isothermal exposure at 750°C has been investigated, aiming to provide the experimental dataset as boundary conditions of physics-based modeling for material/component life prediction. Four different 347H heats containing various amounts of boron and nitrogen additions were prepared and evaluated. The combined additions of B and N are found to stabilize the strengthening secondary M23C6 carbides and retarding the transition from M23C6 to sigma phase precipitates during thermal exposure. The observed kinetics of microstructure evolution reasonably explains the improvement of creep-rupture properties of 347H stainless steels with the B and N additions.

Yamamoto, Yukinori↗

Development of creep resistant ferritic-martensitic steels for operation at 650°C

Creep resistant ferritic-martensitic steels capable of operating at 650°C have long been under development for electricity generation. This presentation will showcase the design and development of alloys CPJ-7 and JMP with approximately 420,000 h of in-house creep testing, the equivalent of ~50 years of cumulative creep tests. Approximately fifty different alloy compositions were manufactured as part of an ICME approach. CPJ-7 present superior creep properties compared to COST alloys for steam turbine and P91/92 for boiler applications. The prolonged creep life was attributed to slowing down the destabilization of fine precipitates at 650°C. The JMP steels were designed with higher Co for solid solution strengthening and increased W for matrix strength and stability. The creep life compared to CPJ-7 increased between 118 and 150% at 650°C depending on the stress. On a Larson-Miller plot, the performance of the JMP steels surpasses that of MARBN steel. Composition-microstructure-properties relationships will be discussed.

Detrois, Martin↗

Development of Novel Ferritic-Martensitic Steels with Superior Creep Properties for Power Plant Applications

A creep resistant martensitic steel, CPJ-7, was developed with an operating temperature approaching 650°C. Subsequently, another creep resistant martensitic steel, JMP, was designed with the potential to operate at, or slightly above, 650°C. This report describes the development of these alloys from early iterations of CPJ steels to the final CPJ-7 formulation as well as the more heat resistant JMP steel formulation. The design originated from computational modeling for phase stability and precipitate strengthening using fifteen constituent elements. Approximately forty heats of CPJ and ten of JMP, each weighing ~7 kg, were vacuum induction melted. A computationally optimized heat treatment schedule was developed to homogenize the ingots prior to hot forging and rolling prior to final normalization and tempering. Overall, wrought and cast versions of CPJ-7 present superior creep properties when compared to wrought and cast versions of COST alloys for steam turbine and wrought and cast versions of P91/92 for boiler applications. For instance, the Larson Miller Parameter curve for CPJ-7 at 650°C almost coincides with that of COST E at 620°C. The prolonged creep life was attributed to slowing down the process of the destabilization of the MX and M 23 C 6 precipitates at 650°C. On the other hand, the cast version of CPJ-7 also revealed superior mechanical performance, well above commercially available cast 9% Cr martensitic steel or derivatives, especially for creep life at 650°C. The casting process employed slow cooling to simulate the conditions of a thick wall full-size steam turbine casing but utilized a separate homogenization step prior to final normalization and tempering. To advance the development of CPJ-7 for commercial applications, a process was used to scale up the production of the alloy using vacuum induction melting (VIM) and electroslag remelting (ESR), which underlined the importance of melt processing control of intentionally designed minor and trace elements in these advanced alloys. Following the work on CPJ-7, the JMP steels were designed with higher Co for increased solid solution strengthening, Si for oxidation resistance and increased W (with low Mo content) for matrix strength and stability as well as solid solution strengthening. The JMP steels showed increases in creep life compared to CPJ-7 between 118 to 150% at 650°C for testing at various stresses between 138 MPa and 207 MPa. On a Larson-Miller plot, the performance of the JMP steels surpasses that of state-of-the-art MARBN and other MARBN-type steels. The influence of various elements within the composition of the alloys on the microstructure and mechanical properties are discussed. This report presents approximately 420,000 h of in-house creep testing, the equivalent of almost 50 years of cumulative creep tests.

36 MATERIALS SCIENCE↗

Tailoring the γ-γ'-γ" dual superlattice microstructure of INCONEL® 725 by high temperature aging and Nb/Ta additions for superior creep properties

Next-generation energy systems require superior resistance to creep deformation due to the considerably prolonged exposure times at operating stress and temperature. To improve the elevated temperature properties of INCONEL® 725 (IN725), a corrosion resistant alloy, several variants with different Ti/Al ratio and judicious amounts of Nb and Ta were made. Furthermore, a high temperature aging (HTA) heat treatment, designed to promote favorable precipitate phase formation, was explored. These adjustments allowed to tailor the amount and type of precipitate strengthening which led to significant increases in time to failure. The Ti/Al ratio was used to favor the formation of γ' or γ" precipitates. Compact morphology precipitates, consisting of γ' precipitates surrounded by a γ" shell, were formed in alloys with a low Ti/Al ratio. The HTA increased the creep life of various alloy formulations up to a maximum improvement of 371% as compared to the standard aging heat treatment. The Nb and Ta additions had a similar effect on increasing creep life by promoting and stabilizing γ" precipitation. The positive effect of the additions was even more pronounced when coupled with the HTA. A phase stability study with up to 10,000 h exposure at 700°C revealed that the compact morphology helped in slightly reducing coarsening of the γ' precipitates, although the effect on creep was not significant. The findings of this study enable design of dual superlattice alloys through microstructural engineering that yields superior performance and can be applied to a wide range of alloys in the IN718 and derivatives family.

Antonov, Stoichko↗