DOE OSTI2024

Mechanical degradation of duplex SiC-fiber reinforced SiC matrix composite tubes under a controlled high-temperature steam environment

This paper describes results from the mechanical evaluation of unirradiated SiC fiber–reinforced SiC matrix composite tubes under a controlled high-temperature steam environment. The experiments were aimed at identifying key material degradation behavior under environments relevant to loss-of-coolant accidents of light water reactors. Mechanical tests of the SiC composite tubes at 1000 °C under steam and inert environments were conducted using a unique test capability. Further, the material tested was a duplex tube with a thick monolithic SiC layer on the outer surface. The tubes were subjected to preloading at ~100 MPa in tension before exposure to high-temperature steam with up to 75% of the preload at a constant displacement. In the presence of matrix cracks, the steam exposure caused embrittlement of the SiC composite tubes and failure at a stress level below the pretest stress. The material degradation was explained by a fiber oxidation model, which can be applied to various SiC cladding concepts. The embrittlement could be a limiting factor for using SiC cladding subjected to loss-of-coolant accident conditions.

36 MATERIALS SCIENCE↗

DOE OSTI2024

High Temperature Tensile Testing of Molybdenum Before and After Exposure in Flowing He at 600°C to 1000°C

ORNL supported NorthStar Medical Radioisotope’s accelerator-based concept to produce the medical isotope molybdenum-99 (Mo-99). The Mo targets are expected to experience in the accelerator temperature ranging from 200°C to 1000°C, and previous studies have demonstrated the embrittlement of Mo targets at room temperature when exposed to impure He at 800 to 1000°C. The goal of this project was to evaluate potential embrittlement at temperature ranging from 600°C to 1000°C for three Mo materials exposed at the same temperatures for 100h in high purity He (O 2 < 5ppm (µl/l)) with a flow rate of ~1m/s. Enriched Mo-100 (aMo) and conventional pressed and sintered Mo (UHP) disks were provided by NorthStar while low carbon arc cast rolled Mo, fabricated at ORNL, was used for comparison. The as fabricated rolled Mo exhibited superior tensile strength due to the alloy very fine grain size with limited ductility except at 1000°C with the elongation at rupture reaching 30%. The UHP Mo disks showed the lowest strength but highest ductility at 20-1000°C with significant strain hardening during tensile testing. The ductility of the aMo material was quite low at all temperatures due to a high density of voids at grain boundaries. Significant embrittlement of the aMo material was observed after exposure at 600°C to 1000°C, most likely because of oxygen diffusion and segregation at grain boundaries. No embrittlement was observed for the UHP Mo material, with excellent elongation at rupture for some of the specimens oxidized in He and tested at 600-1000°C. Significant variation in ductility from one UHP Mo specimen to another was, however, measured, both in the as fabricated and He-oxidized conditions. The rolled Mo was not affected by oxidation in He at 800°C, but a decrease in strength and increase in ductility was observed at 1000°C, likely due to the material recrystallization.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Mechanical behavior analysis using small-size graphite disc compression testing with digital image correlation methods

The ASTM International Standard Test Method for Tensile Stress-Strain of Carbon and Graphite (ASTM C749) requires dog-bone shaped specimens. Unfortunately, specimen sizes required in ASTM C749 are much too large for irradiation within a test reactor and are incompatible with irradiation capsule volumes, molten salt degradation facilities, or oxidation apparatus. The ASTM International Standard Test Method for Tensile Strength Estimate by Disc Compression of Manufactured Graphite (ASTM D8289) was developed as an alternative that provides a means for testing tensile properties using smaller specimens when geometric constraints are present. However, the important stress–strain relation throughout the test loading history that could be recorded using ASTM C749 is lost by using ASTM D8289 because of the difficulties involved with using traditional strain gauges or extensometers on such a small specimen. In this work, a digital image correlation (DIC) method, which uses a full-field noncontact surface displacement measurement technique, was applied along with the ASTM D8289 splitting tensile test on eight small samples of graphite grade Mersen 2114 to track their deformation during compressive loading. Initial results showed that the DIC technique can measure the surface displacement/strain on these small (Ø6 × 3 mm) graphite specimens with high accuracy and good repeatability, indicating that the DIC technique, combined with the small-disc splitting tensile test in ASTM D8289, can capture the strain evolution in the test. In conclusion, further comparison of measured strains with analytical and numerical simulation results provides additional understanding of the mechanical behaviour of this nuclear graphite material in complex stress states.

36 MATERIALS SCIENCE↗