DOE OSTI2023

Shock-induced melting of [100] lithium fluoride: Sound speed and Hugoniot measurements to 230 GPa

Although [100] lithium flouride (LiF) is the most widely used optical window material in dynamic compression experiments, its high stress (>100 GPa) shock compression response, including melting, is not well understood. To address this need, we measured wave profiles in plate impact experiments to determine the Hugoniot states and longitudinal sound speeds in [100] LiF crystals shock compressed to 231 GPa. The measured peak states are fitted well by a linear shock velocity-particle velocity relation, providing an accurate determination of the LiF Hugoniot curve to significantly higher stresses than previous experiments. The longitudinal sound speeds show a near linear increase with density compression to 182 GPa. Between 182 GPa and 195 GPa, the sound speed and the longitudinal modulus decrease abruptly, due to shock-induced melting. The increasing sound speeds and moduli at higher stresses suggest that shock compressed LiF is fully liquid at 195 GPa and above, allowing determination of the Gruneisen parameter for liquid LiF. Here, the melt stress determined here differs from that predicted by current multiphase equations of state for LiF. Our results provide important insight into the high stress solid and liquid states of shock compressed LiF and point to the need for an improved multiphase equation of state at high pressures and high temperatures.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Observations of twinning microstructure in iron ramp-compressed through the α – ε phase transition

Single crystal iron was ramp-compressed along the [100] axis at 4 GPa/ns through the α–ϵ phase transformation at 13 GPa. Unlike shock experiments, in these ramp compression experiments the bcc lattice is observed to be nearly isotropically relaxed before the phase transition. There was a mixed α/ϵ phase region starting at ~13 GPa which was observed for 0.75 ns until the peak stress of 18 GPa was reached. In situ x-ray diffraction measurements show the formation of new hcp orientations not reported in shock or quasistatic compression experiments. The new hcp orientations appear to be caused by {10¯11} <10¯1 ¯2> → {¯1011} <¯101¯2> sequential twins that occur during the phase transition. This twinning mechanism relieves the shear strain caused by the bcc-hcp phase transition from the isotropically relaxed bcc phase while subject to uniaxial compression. Furthermore, these results show that in iron the induced microstructure through a phase transition and the phase transition mechanism depend on the loading history.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2021

Simultaneous compression and opacity data from time-series radiography with a Lagrangian marker

Time-resolved radiography can be used to obtain absolute shock Hugoniot states by simultaneously measuring at least two mechanical parameters of the shock, and this technique is particularly suitable for one-dimensional converging shocks where a single experiment probes a range of pressures as the converging shock strengthens. However, at sufficiently high pressures, the shocked material becomes hot enough that the x-ray opacity falls significantly. Additionally, if the system includes a Lagrangian marker such that the mass within the marker is known, this additional information can be used to constrain the opacity as well as the Hugoniot state. In the limit that the opacity changes only on shock heating, and not significantly on subsequent isentropic compression, the opacity of the shocked material can be determined uniquely. More generally, it is necessary to assume the form of the variation of opacity with isentropic compression or to introduce multiple marker layers. Alternatively, assuming either the equation of state or the opacity, the presence of a marker layer in such experiments enables the non-assumed property to be deduced more accurately than from the radiographic density reconstruction alone. An example analysis is shown for measurements of a converging shock wave in polystyrene at the National Ignition Facility.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

DOE OSTI2021

Probing the lattice structure of dynamically compressed and released single crystal iron through the alpha to epsilon phase transition

In this work, experiments using broadband Laue x-ray diffraction (XRD) were used to examine the lattice structure of dynamically compressed [100]-oriented single crystal iron samples at the Dynamic Compression Sector at the Advanced Photon Source. These experiments used 1 μm thick iron single crystal samples sandwiched between a polyimide ablator and a polycarbonate window. A 100 J, 10 ns duration laser pulse incident on the polyimide ablator was used to shock compress the iron samples to initial stresses greater than 25 GPa, exceeding the ~13 GPa alpha (body-centered-cubic or bcc structure) to epsilon (hexagonal-close-packed or hcp structure) phase transition stress. XRD measurements were performed at various times relative to the shock wave entering the iron sample: early times, <~150 ps while the initial shock waves propagated through the iron; intermediate times, after the iron equilibrated with the ablator and window reaching a plateau stress state (12 or 17 GPa) lasting several nanoseconds; and late times, during uniaxial strain release. The early time measurements show that in <~150 ps, the high-pressure hcp phase is relaxed with a c/a ratio of 1.61, contrary to previous laser shock experiments where a c/a ratio of 1.7 was inferred. In the plateau stress state and partially released states, XRD measurements showed that the hcp structure retained a c/a ratio of 1.61 with no observable changes in the microstructure. Upon stress release at ~1 GPa/ns release rate, the reverse phase transition (hcp to bcc) to the original single crystal orientation (implying a transformation memory effect) was observed to reach completion somewhere between 13 and 11 GPa, indicating little stress hysteresis under rapid uniaxial strain release. A similar memory effect for the reverse hcp to bcc transformation has been previously observed under hydrostatic compression. However, the bcc/hcp orientation relationships differ somewhat between dynamic and static compression experiments, implying that the transformation pathway under uniaxial dynamic strain differs from the Burgers mechanism.

36 MATERIALS SCIENCE↗