Hazeli, Kavan

Publications and source records attributed to Hazeli, Kavan.

10 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

On the Mechanical Behavior of LP-DED C103 Thin-Wall Structures

Laser Powder Directed Energy Deposition (LP-DED) can produce thin-wall features on the order of 1 mm. These features are essential for large structures operating in extreme environments such as regeneratively cooled nozzles and heat exchangers, which often make use of refractory metals. In this work, the mechanical behavior of LP-DED C103 was investigated via quasi-static tensile testing and low cycle fatigue (LCF) testing. The effects of vacuum stress relief (SR) and hot isostatic pressing (HIP) heat treatments were investigated for specimens in the vertical and horizontal build orientations during tensile testing. The AB and SR properties were lower than literature values for wrought and laser powder bed fusion (L-PBF) bulk components but higher than electron beam powder bed fusion (EB-PBF). The application of a HIP cycle improved strength by 7% and ductility by 27% past the initial as-built condition. Fracture images reveal that interlayer stress concentration sites are responsible for fracture in specimens in the vertical orientation. Meanwhile, fracture in the horizontal specimens mainly propagates at a slanted angle typical of plane stress conditions. The LCF results show cycles to failure ranging from 100 cycles to 8000 cycles for max strain levels of 2% and 0.5%, respectively. Fractography on the fatigue specimens reveals an increasing propagation zone as max strain levels are increased. The impact of these findings and future work are discussed in detail.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Temperature-dependent mechanical properties and crystal plasticity parameters for additively manufactured Haynes-214 alloy: Experiments and numerical modeling

Our experimental mechanical testing data demonstrated that the additively manufactured (AM) laser powder bed fusion (L-PBF) Haynes-214 alloy exhibits non-linear mechanical properties as the temperature rises from ambient to 870 °C. Crystal plasticity (CP) simulations provide an effective approach to gaining deeper insights into microstructure-property linkages under thermomechanical loading. This method can reduce the need for costly high-temperature mechanical testing while accounting for the effects of crystallographic texture and grain morphology on the mechanical behavior of AM materials. However, calibrating a CP model is time-consuming because individual simulations are computationally expensive and hundreds (or more) of iterations over parameter sets may be required. To address this issue, we have designed a machine learning-differential evolution (ML-DE) CP framework that can accurately interpolate the tensile properties of AM L-PBF Haynes-214 alloy across a wide temperature range from ambient to 870 °C, with minimal reliance on experimental data. The framework uses electron backscatter diffraction (EBSD) measurements to generate statistically equivalent microstructural volume elements to serve as inputs to the CP modeling framework. Stress–strain curves were generated from 1000 CP simulations, which serve as the training data set for the three ML regression algorithms explored: linear, extra-trees, and multi-layer perceptron. These three regression models were independently evaluated to compare their efficiency and identify the most suitable algorithm for the given problem. Results revealed that the extra-trees ML regressor outperforms the other models in both qualitative and quantitative aspects with an R 2 of 0.98. Subsequently, the differential evolution optimization approach is employed to calibrate the ML-based CP material parameters with experimental results obtained at various temperatures. Finally, temperature-dependent CP material parameters are formulated. The effectiveness and efficiency of the designed framework are validated through comparison with experimental results, demonstrating a high degree of agreement. These calibrated parametric constitutive equations enable further use of the CP model to study the deformation behavior of this alloy under a wide range of thermo-mechanical loading conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2024

GRCop-42: Comparison between laser powder bed fusion and laser powder direct energy deposition

This study involves a comparative analysis of additively manufactured GRCop-42 specimens produced using two processes: laser-powder bed fusion (L-PBF) and laser powder direct energy deposition (LP-DED). The investigation characterizes a range of material attributes, including surface topography, internal defects, microstructural features, quasi-static mechanical properties, and fractographic characteristics. The findings demonstrate that, despite the specimens being fabricated with the same base material, the resulting material properties vary significantly between the two additive manufacturing processes. As such, material properties cannot be presumed to be uniform across different manufacturing methods. Consequently, material characterization must be conducted for individual manufacturing processes based on specific parameters.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Stress localization investigation of additively manufactured GRCop-42 thin-wall structure

A full-field crystal plasticity (CP) framework is presented for the GRCop-42 alloy to study microscopic mechanical behavior and local stress heterogeneities. The microstructures of additively manufactured (AM) materials are often unique relative to conventionally processed materials, and the local thermal histories drive these differences during the build process. These thermal histories depend on the process parameters (laser power, scan speed, and scan strategy) and the part geometry. Prior research has shown that the mechanical properties of thin-walled structures can vary significantly with wall thickness due to changes in the thermal boundary conditions during manufacturing. It is, therefore, desirable to perform CP simulations based on the phenomenological constitutive model to predict the local mechanical responses induced by microstructural heterogeneities. This work generates representative microstructures based on experimentally collected grain information (i.e., texture) for grain scale stress analysis, and the material constitutive parameters are calibrated using the experimental mechanical testing data. Here, we specifically investigated the effect of crystallographic texture and grain morphologies on the size-dependent mechanical properties of AM GRCop-42. The selection of appropriate material properties for implementing an effective free surface boundary condition and the influence of adjacent buffer layers are also discussed. Analysis of local field results reveals a strong correlation between stress localization and the initial grain orientation. However, no significant relationship between the misorientation of the individual adjacent grains and the average misorientation is observed.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Size effect characteristics and influences on fatigue behavior of laser powder bed fusion of thin wall GRCop-42 copper alloy

Size effects, influencing a material's strength, elongation, fatigue limit, and longevity, depend on the operative and dominant deformation and failure mechanisms. This study explores the size effects in additive manufactured (AM) GRCop-42 (Cu-4at%Cr-2at%Nb) thin wall structures fabricated via laser-powder bed fusion (L-PBF) and their impact on fatigue life. The influence of internal defects and surface topography on the fatigue life of specimens in both as-built and hot isostatic pressed (HIP) conditions across different thicknesses is investigated. Where micro-computed tomography (μCT) was used to quantify the internal porosity of as-built, pristine HIP'd, and fatigued HIP'd specimens, and laser microscopy was employed to quantify the surface topography of specimens prior to fatigue. Additionally, quasi-static tests were used to establish baseline mechanical properties (i.e. yield strength (YS), ultimate tensile strength (UTS), and elongation) to frame fatigue testing conditions. Results indicate a significant enhancement in fatigue life for HIP'd specimens for both thicknesses, with internal defects depicting a greater impact than surface topography. Furthermore, fractographic analysis suggests that thicker specimens exhibit higher resistance to crack propagation during fatigue testing in the absence of substantial porosity. Thus, the size effects observed on the fatigue life of L-PBF GRCop-42 appears to be dominated by internal defects.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Additively manufactured β-Ti5553 with laser powder bed fusion: Microstructures and mechanical properties of bulk and lattice parts

Ti5553 (Ti-5Al-5Mo-5V-3Cr wt%) is a titanium alloy widely used for its high strength-to-weight ratio and good formability at elevated temperatures. Unlike Ti-6Al-4V, Ti5553 does not undergo martensitic transformation, preventing cracking of brittle martensite upon rapid cooling. This makes it a strong candidate for additive manufacturing (AM), particularly laser powder bed fusion (L-PBF). L-PBF offers the unique opportunity to make fine lattice structures to reduce component weight. Despite the growing field of AM, there have been limited studies on L-PBF Ti5553 lattices and how their properties differ from the bulk. Here the present work addresses this knowledge gap by investigating microstructures and properties of L-PBF bulk and lattice parts and the effect of post L-PBF heat treatments. Electron microscopy and mechanical testing show that the high dislocation density formed during L-PBF increases bulk part’s yield strength by approximately 100 MPa compared to the conventional alloy. Digital image correlation during compression testing of octet truss lattices reveals a layer-by-layer failure mode. Compared to the bulk, the lattice contains copious ω nanoprecipitation, weaker <001> texture, smaller average grain sizes, and larger content of high-angle grain boundaries. These features elicit differences in Taylor factor distributions for the lattice depending on load direction, underlining challenges in predicting lattice mechanical response based on bulk properties. By examining the processing-structure-property relationships in the bulk and lattice, the present results delineate their microstructural and mechanical differences and establish a benchmark for the future design applications of L-PBF Ti5553.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Effects of size, geometry, and testing temperature on additively manufactured Ti-6Al-4V titanium alloy

This article presents a comprehensive study concerning size and geometry effect on the ambient and high-temperature mechanical behavior of additively manufactured laser powder bed fusion Ti-6Al-4V alloy. Key mechanical property metrics are presented, including strain hardening rate, yield strength, and Young’s modulus as a function of thickness and testing temperature (ambient, 250 °C, and 450 °C). Here, the effect of specimen size on manufacturing-induced microstructural feature formation is demonstrated and discussed. A detailed analysis regarding Young’s modulus, yield strength, and strain hardening rate variation at elevated temperatures is also presented. Size effect and temperature-sensitive deformation mechanisms are linked to the underlying microstructural deformation mechanisms activated at respective temperatures. Counter-intuitively, this study determined that irrespective of the geometry, strain hardening rates increased as temperature increased. An in-depth microstructural examination is presented to explain the stated observation. The texture of Interrupted tensile test samples examined for ambient, 250 °C, and 450 °C post-yield was observed to be unchanged, indicating the strain hardening behavior was not texture dependent. Schmid factor analysis, coupled with experimental findings from previous work, was implemented to generate a hypothesis. This hypothesis suggests that the drop in critical resolved shear stress for basal and pyramidal slip systems, as temperature increases, paired with the high dislocation density of laser powder bed fusion Ti-6Al-4V, leads to dislocation entanglement and results in increased strain hardening at elevated temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Electrochemical Response of Alkaline Batteries Subject to Quasi-Static and Dynamic Loading

We report electrochemical changes were successfully monitored through the coupling of external loading, electrochemical impedance spectroscopy (EIS), and distribution of relaxation times (DRT) analysis. The development of the testing methods allows for detailed observation of changes due to mechanical loading and distinguishes responses between different cell geometries. Comparison of the force vs displacement, voltage vs displacement, and distribution of relaxation times plots to the different cell geometries display failure modes specific to geometry as well as the impact of different loading profiles. Numerical modeling confirmed the movement within individual cells and predicted locations with the most deformation based on the external loading condition applied. The results gathered from combining mechanical loading, electrochemical response, and numerical modeling, yield a viable approach to establishing an improved understanding of the effects of mechanical loading on the electrochemical response of multiple battery geometries and the methods herein may be extensible to additional battery chemistries.

25 ENERGY STORAGE↗
DOE OSTI2020

Localized Strain Analysis of Ce- and Mg-Treated Cast Iron under Uniaxial Compression

Cast iron exhibits a wide range of mechanical properties, depending on its microstructural features. The microstructure of cast iron consists of several microconstituents with different elastic-plastic behavior, making the strain non-uniform across the bulk material. To understand the individual effects of these microconstituents on the overall mechanical behavior, local strain analysis using digital image correlation analysis was carried out. Samples with two different compositions (varying cerium, magnesium and silicon) were processed at different solidification velocities in a Bridgman furnace. Sections of the directionally solidified samples were loaded under uniaxial compression to measure global and local strain behavior. Despite the variability of the microstructure, the stress–strain curves obtained by digital image correlation (DIC) were found to react in a well-controlled way to changes in solidification velocity. It was observed that high-strain failure (greater than 15%) was accompanied by local straining of the softer ferritic phase, but during low-strain failure, local straining was not prominent. Higher nodularities, due to higher solidification velocities, raised the compressive strength without affecting the toughness significantly. Higher percentages of carbides led to higher compressive strengths with corresponding losses in ductility. The continuity of the matrix was also found to play an important role in the behavior during compression.

ductile failure↗