Engineering topics
He, Guanze
Publications and source records attributed to He, Guanze.
Microstructural and material property changes in severely deformed Eurofer-97
Severe plastic deformation changes the microstructure and properties of steels, which may be favourable for their use in structural components of nuclear reactors. In this study, high-pressure torsion (HPT) was used to refine the grain structure of Eurofer-97, a ferritic/martensitic steel. Electron microscopy and X-ray diffraction were used to characterise the microstructural changes. Following HPT at room temperature to a maximum shear strain of 230, the average grain size reduced by a factor of ~30, with a marked increase in high-angle grain boundaries. Dislocation density also increased by more than one order of magnitude. The thermal stability of the deformed material was investigated via in-situ annealing during synchrotron X-ray diffraction. This revealed substantial recovery between 450 K – 800 K. Irradiation with 20 MeV Fe-ions to ~0.1 dpa caused a 20% reduction in dislocation density compared to the as-deformed material. However, HPT deformation prior to irradiation only had a minor effect in mitigating the irradiation-induced reductions in thermal diffusivity and surface acoustic wave velocity of the material. Microstructural and material property changes are dominated by deformation compared to irradiation. In light of this, the benefits of using HPT to improve the irradiation resistance of Eurofer-97 are limited. These results provide a multi-faceted view of the changes in ferritic/martensitic steels due to severe plastic deformation, and how these changes can be used to alter material properties.
Origin of age softening in the refractory high-entropy alloys
Refractory high-entropy alloys (RHEAs) are emerging materials with potential for use under extreme conditions. As a newly developed material system, a comprehensive understanding of their long-term stability under potential service temperatures remains to be established. This study examined a titanium-vanadium-niobium-tantalum alloy, a promising RHEA known for its superior high-temperature strength and room-temperature ductility. Using a combination of advanced analytical microscopies, Calculation of Phase Diagrams (CALPHAD) software, and nanoindentation, we investigated the evolution of its microstructure and mechanical properties upon aging at 700°C. Trace interstitials such as oxygen and nitrogen, initially contributing to solid solution strengthening, promote phase segregation during thermal aging. As a result of the depletion of solute interstitials within the metal matrix, a progressive softening is observed in the alloy as a function of aging time. This study, therefore, underscores the need for a better control of impurities in future development and application of RHEAs.
Thermal diffusivity recovery and defect annealing kinetics of self-ion implanted tungsten probed by insitu transient grating spectroscopy
Tungsten is a promising candidate material for plasma-facing armour components in future fusion reactors. A key concern is irradiation-induced degradation of its normally excellent thermal transport properties. In this comprehensive study, thermal diffusivity degradation in ion-implanted tungsten and its evolution from room temperature (RT) to 1073 K is considered. Five samples were exposed to 20 MeV self-ions at RT to achieve damage levels ranging from 3.2 x 10 -4 to 3.2 displacements per atom (dpa). Transient grating spectroscopy with in-situ heating was then used to study thermal diffusivity evolution as a function of temperature. Using a kinetic theory model, an equivalent point defect density is estimated from the measured thermal diffusivity. The results showed a prominent recovery of thermal diffusivity between 450 K and 650 K, which coincides with the onset of mono-vacancy mobility. After 1073 K annealing samples with initial damage of 3.2 x 10 -3 dpa or less recover close to the pristine value of thermal diffusivity. For doses of 3.2 x 10 -2 dpa or higher, on the other hand, a residual reduction in thermal diffusivity remains even after 1073 K annealing. Transmission electron microscopy reveals that this is associated with extended, irradiation-induced dislocation structures that are retained after annealing. A sensitivity analysis shows that thermal diffusivity provides an efficient tool for the assessing total defect content in tungsten up to 1000 K.