Heckel, R. W.

Publications and source records attributed to Heckel, R. W..

13 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1988

Diffusional transport during the cyclic oxidation of gamma + beta, Ni-Cr-Al(Y, Zr) alloys

The cyclic oxidation behavior of several cast gamma + beta, Ni-Cr-Al(Y, Zr) alloys and one low-pressure plasma spraying gamma + beta, Ni-Co-Cr-Al(Y) alloy was studied. Cyclic oxidation was found to result in a decreasing Al concentration at the oxide-metal interface due to a high rate of Al consumption coupled with oxide scale cracking and spalling. Diffusion paths plotted on the ternary phase diagram showed higher Ni concentrations with increasing cyclic oxidation exposures. The alloy with the highest rate of Al consumption and the highest Al content underwent breakaway oxidation following 500 1-hr cycles at 1200 C.

Nesbitt, J. A.↗
NASA NTRS1987

Interdiffusion in Ni-rich, Ni-Cr-Al alloys at 1100 and 1200 C. I - Diffusion paths and microstructures. II - Diffusion coefficients and predicted concentration profiles

Interdiffusion in Ni-rich Ni-Cr-Al alloys is investigated experimentally after annealing at 1100 and 1200 C using gamma/gamma, gamma/gamma+beta, gamma/gamma+gamma prime, and gamma/gamma+alpha diffusion couples. The amount and location of Kirkendall porosity suggests that Al diffuses more rapidly than Cr which diffuses more rapidly than Ni in the gamma phase of Ni-Cr-Al alloys. The location and extent of maxima and minima in the concentration profiles of the diffusion couples indicate that both cross-term diffusion coefficients are positive. Measurements are also presented of the ternary interdiffusion coefficients of the gamma phase in the Ni-Cr-Al system. It is shown that the interdiffusion coefficients can be accurately predicted by using a ternary finite-difference interdiffusion model.

Nesbitt, J. A.↗
NASA NTRS1987

Predicting diffusion paths and interface motion in gamma/gamma + beta, Ni-Cr-Al diffusion couples

A simplified model has been developed to predict Beta recession and diffusion paths in ternary gamma/gamma + beta diffusion couples (gamma:fcc, beta: NiAl structure). The model was tested by predicting beta recession and diffusion paths for four gamma/gamma + beta, Ni-Cr-Al couples annealed for 100 hours at 1200 C. The model predicted beta recession within 20 percent of that measured for each of the couples. The model also predicted shifts in the concentration of the gamma phase at the gamma/gamma + beta interface within 2 at. pct Al and 6 at. pct Cr of that measured in each of the couples. A qualitative explanation based on simple kinetic and mass balance arguments has been given which demonstrates the necessity for diffusion in the two-phase region of certain gamma/gamma + beta, Ni-Cr-Al couples.

Nesbitt, J. A.↗
NASA NTRS1986

The effects of tantalum on the microstructure of two polycrystalline nickel-base superalloys - B-1900 + Hf and MAR-M247

The effect of changing the content of Ta on the gamma/gamma-prime carbide microstructure was investigated in two crystalline nickel-base superalloys: conventionally cast B-1900 + Hf, and both conventionally cast and directionally solidified MAR-M247. The changes occurring in the microstructure effects were similar in both alloys. The gamma-prime and carbide volume fractions increased linearly with Ta additions, while the gamma-prime phase compositions did not change. Bulk Ta additions increased the levels of Cr and Co (in addition to that of Ta) of the gamma phase, a result of the approximately constant partitioning ratios for these two elements. The addition of Ta led to a partial replacement of Hf in the MC carbides. In addition, Cr-rich M(23)C(6) carbides formed as a result of MC carbide decomposition during heat treatment.

Heckel, R. W.↗
NASA NTRS1984

Modeling degradation and failure of Ni-Cr-Al overlay coatings

Degradation of a Ni-16Cr-25Al-0.06Zr overlay coating on a Ni-22Cr substrate was examined after oxidation accompanied by thermal cycling. Concentration/distance profiles were measured in the coating and substrate after various one-hour cycles at 1150 C. A numerical model was developed to simulate coating degradation by simultaneous oxidation and coating/substrate interdiffusion. The validity of the model was confirmed by comparison of predicted and measured concentration/distance profiles. The ability of the model to identify critical system parameters was demonstrated for the case of the initial Al and Cr content of the coating and substrate.

Nesbitt, J. A.↗
NASA NTRS1984

Solute transport and the prediction of breakaway oxidation in gamma + beta Ni-Cr-Al alloys

The Al transport and the condition leading to breakaway oxidation during the cyclic oxidation of gamma + beta NiCrAl alloys have been studied. The Al concentration/distance profiles were measured after various cyclic oxidation exposures at 1200 C. It was observed that cyclic oxidation results in a decreasing Al concentration at the oxide/metal interface, maintaining a constant flux of Al to the Al2O3 scale. It was also observed that breakaway oxidation occurs when the Al concentration at the oxide/metal interface approaches zero. A numerical model was developed to simulate the diffusional transport of Al and to predict breakaway oxidation in gamma + beta NiCrAl alloys undergoing cyclic oxidation. In a comparison of two alloys with similar oxide spalling characteristics, the numerical model was shown to predict correctly the onset of breakaway oxidation in the higher Al-content alloy.

Nesbitt, J. A.↗
NASA NTRS1984

Cyclic oxidation behavior of beta+gamma overlay coatings on gamma and gamma+gamma-prime alloys

Detailed experimental studies of the cyclic oxidation behavior of low-pressure plasma sprayed beta+gamma coasting on gamma-phase Ni-Cr-Al alloys have shown the correlation of weight change, oxide type, and Cr and Al concentration-distance profiles as a function of oxidation time. Of special interest was the transition to breakway oxidation due to the loss of the Al flux to the oxide and the failure of the coated alloy to form an Al2O3-rich oxide scale. The experimental results on beta+gamma/gamma coating systems were used as the basis of a numerical model (ternary, semi-infinite, finite-difference analysis) which accurately predicted changes in Cr and Al concentration-distance profiles. The model was used to study parameters critical to enhancing the life of coatings which fail by a combination of Al loss in forming the oxide scale and Al loss via interdiffusion with the substrate alloy. Comparisons of beta+gamma/gamma coating behavior are made to the oxidation of coated gamma+gamma-prime substrates, both ternary Ni-Cr-Al alloys and Mar-M 247-type alloys.

Nesbitt, J. A.↗
NASA NTRS1984

Modeling degradation and failure of Ni-Cr-Al overlay coatings

Degradation of a Ni-16Cr-25Al-0.06Zr overlay coating on a Ni-22Cr substrate was examined after oxidation accompanied by thermal cycling. Concentration/distance profiles were measured in the coating and substrate after various one-hour cycles at 1150 C. A numerical model was developed to simulate coating degradation by simultaneous oxidation and coating/substrate interdiffusion. The validity of the model was confirmed by comparison of predicted and measured concentration/distance profiles. The ability of the model to identify critical system parameters was demonstrated for the case of initial Al and Cr content of the coating and substrate.

Nesbitt, J. A.↗
NASA NTRS1982

Structure-property effects of tantalum additions to nickel-base superalloys

The characterization of the effect of Ta on the structure of Ni base superalloys, the determination of the effects of Ta (structure) variations on the mechanical, thermal, and oxidation behavior, and the identification of alloying elements which have potential as substitutes for Ta are investigated. Mar M247 type alloys are emphasized; nominal and analyzed compositions of ten alloys under study are given. X-ray and composition analysis are being used to determine the partitioning of alloying elements between gamma, gamma primes, and MC (cubic) as a function of Ta content. The diffusional interactions of the Mar M247-type alloys with as cast beta + gamma alloys are studied to determine the effects of Ta on alloy/coating degradation.

Heckel, R. W.↗
NASA NTRS1976

Macroscopic aspects of interfacial reactions

The extent of interdiffusion and formation of new phases is determined by the constitution diagram of the alloy system, the interdiffusion coefficients of the phases present, and the thermal conditions (temperature and time) associated with the bonding process and/or subsequent use of the bonded structure. In many instance, the kinetics of interdiffusion and phase formation can be predicted from known parameters using numerical methods and computer techniques. Predictions are compared with experimentally determined parameters for a variety of metallurgical alloy systems.

Heckel, R. W.↗