Evaluating Iodine Immobilization Technologies: Cermets, Polycermets, and Polyhalmets

The work in this report documents the efforts conducted to assess the feasibility of some of the ideas documented in Pacific Northwest National Laboratory invention disclosure reports (IDRs) including: 1) Iodine capture in polyacrylonitrile (PAN)-containing composite sorbents (32451-E). In this work, the composites evaluated included Ag0, Bi0, Cu0, Bi2S3, and Cu2S embedded in PAN. 2) Metal iodide removal from these sorbents through dissolution in dimethyl sulfoxide (DMSO) (32729-E). In this work, PAN dissolution was evaluated for multiple types of sorbents including Ag-Pan, Bi-PAN, Cu-PAN, Bi2S3-PAN, and Cu2S-PAN. 3) Using metal-sulfide sorbents for iodine capture (32647-E). In this work, the composites evaluated under this IDR included Ag2S, Bi2S3, and Cu2S embedded in PAN. 4) Using low-melting metals to immobilize (encapsulate) iodine-loaded and polymer-containing sorbents into polymer-ceramic-metal (called polycermet) or polymer-halide-metal (called polyhalmet) composite waste forms (32625-E). In this work, the iodine-loaded PAN composites included AgI-PAN, BiI-PAN, and CuI-PAN. 5) Ceramic-metal composite waste form synthesis of polymer-containing materials using low-melting metals like bismuth, tin, or bismuth-tin alloys (32537-E). In this work, the metals evaluated included Bi, 58Bi-42Sn eutectic. 6) Cermets for immobilizing commercial sorbents loaded with radioiodine (32806-E). In this work, AgIX (iodine-loaded silver faujasite zeolite) was evaluated in cermet form.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗

DOE OSTI2023

Improving the Mechanical Properties of Cast Aluminum Via Ultrasonication-Induced Microstructural Refinement

One barrier to the broader use of cast aluminum alloys in automotive applications is their poor mechanical properties, especially compared to wrought materials. This study investigates the use of ultrasound to refine the microstructure of cast aluminum alloys during solidification and thus improve their mechanical properties. An A356 aluminum alloy (Al-Si-Mg) with added Fe (to mimic a recycle-grade alloy) was cast in a graphite mold with the simultaneous application of ultrasound. Tensile specimens were extracted from the castings and heat treated to a T6 temper. Ultrasonication during casting transformed the morphology of primary aluminum grains from dendritic (~140 microns in size) to globular (~36 microns in size), increased the ultimate tensile strength by 10 %, and tripled the ductility compared to casting without ultrasound. This improvement in strength and ductility demonstrates the potential for ultrasonic processing to improve the performance of cast aluminum alloys without altering their chemistry or additional post-processing.

Aluminum, Solidification, Ultrasound, Grain refinm↗