Thin film design of amorphous hafnium oxide nanocomposites enabling strong interfacial resistive switching uniformity

A design concept of phase-separated amorphous nanocomposite thin films is presented that realizes interfacial resistive switching (RS) in hafnium-oxide-based devices. The films are formed by incorporating an average of 7% Ba into hafnium oxide during pulsed laser deposition at temperatures ≤400°C. The added Ba prevents the films from crystallizing and leads to ~20-nm-thin films consisting of an amorphous HfO x host matrix interspersed with ~2-nm-wide, ~5-to-10-nm-pitch Ba-rich amorphous nanocolumns penetrating approximately two-thirds through the films. This restricts the RS to an interfacial Schottky-like energy barrier whose magnitude is tuned by ionic migration under an applied electric field. Resulting devices achieve stable cycle-to-cycle, device-to-device, and sample-to-sample reproducibility with a measured switching endurance of ≥10 4 cycles for a memory window ≥10 at switching voltages of ±2 V. Each device can be set to multiple intermediate resistance states, which enables synaptic spike-timing–dependent plasticity. The presented concept unlocks additional design variables for RS devices.

36 MATERIALS SCIENCE↗

Engineering of Grain Boundaries in CeO 2 Enabling Tailorable Resistive Switching Properties

Abstract Defect engineering in valence change memories aimed at tuning the concentration and transport of oxygen vacancies are studied extensively, however mostly focusing on contribution from individual extended defects such as single dislocations and grain boundaries. In this work, the impact of engineering large numbers of grain boundaries on resistive switching mechanisms and performances is investigated. Three different grain morphologies, that is, “random network,” “columnar scaffold,” and “island‐like,” are realized in CeO 2 thin films. The devices with the three grain morphologies demonstrate vastly different resistive switching behaviors. The best overall resistive switching performance is shown in the devices with “columnar scaffold” morphology, where the vertical grain boundaries extending through the film facilitate the generation of oxygen vacancies as well as their migration under external bias. The observation of both interfacial and filamentary switching modes only in the devices with a “columnar scaffold” morphology further confirms the contribution from grain boundaries. In contrast, the “random network” or “island‐like” structures result in excessive or insufficient oxygen vacancy concentration migration paths. The research provides design guidelines for grain boundary engineering of oxide‐based resistive switching materials to tune the resistive switching performances for memory and neuromorphic computing applications.

36 MATERIALS SCIENCE↗

High performance, electroforming-free, thin film memristors using ionic Na 0.5 Bi 0.5 TiO 3

Here, in ionically conducting Na 0.5 Bi 0.5 TiO 3 (NBT), we explore the link between growth parameters, stoichiometry and resistive switching behavior and show NBT to be a highly tunable system. We show that the combination of oxygen ionic vacancies and low-level electronic conduction is important for controlling Schottky barrier interfacial switching. We achieve a large ON/OFF ratio for high resistance/low resistance ( R HRS / R LRS ), enabled by an almost constant R HRS of ~10 9 Ω, and composition-tunable R LRS value modulated by growth temperature. R HRS / R LRS ratios of up to 10 4 and pronounced resistive switching at low voltages (SET voltage of <1.2 V without high-voltage electroforming), strong endurance (no change in resistance states after several 10 3 cycles), uniformity, stable switching and fast switching speed are achieved. Of particular interest is that the best performance is achieved at the lowest growth temperature studied (600 °C), which is opposite to the case of most other perovskite oxides for memristors, where higher growth temperatures are required for optimum performance. This is understood based on the oxygen vacancy control of interfacial switching in NBT, whereas a range of other mechanisms (including filamentary switching) occur in other perovskites. The study of NBT has enabled us to determine key parameters for achieving high performance memristors.