NASA NTRS1993

On 'large-scale' stable fiber displacement during interfacial failure in metal matrix composites

Experimental results are presented to show that interfacial failure in sapphire-reinforced niobium is characterized by 'large-scale' (5-15 microns) plasticity-controlled fiber displacements occurring under increasing loads. The results are based on the responses during thin-slice fiber pushout tests wherein the fiber is supported over a hole twice the fiber diameter. The results describe an interfacial failure process that should also occur near fiber ends during pullout when a fiber is well-bonded to a soft, ductile matrix, such that eventual failure occurs by shear within the matrix near the interface.

Petrich, R. R.↗

NASA NTRS1992

Interfacial stress state present in a 'thin-slice' fibre push-out test

An analysis of the stress distributions along the fiber-matrix interface in a 'thin-slice' fiber push-out test is presented for selected test geometries. For the small specimen thicknesses often required to displace large-diameter fibers with high interfacial shear strengths, finite element analysis indicates that large bending stresses may be present. The magnitude of these stresses and their spatial distribution can be very sensitive to the test configuration. For certain test geometries, the specimen configuration itself may alter the interfacial failure process from one which initiates due to a maximum in shear stress near the top surface adjacent to the indentor, to one which involves mixed mode crack growth up from the bottom surface and/or yielding within the matrix near the interface.

Kallas, M. N.↗

NASA NTRS1990

Interfacial shear behavior of sapphire-reinforced NiAl composites

The interfacial shear behavior in near-equiatomic NiAl reinforced by sapphire filaments has been examined at room temperature using a fiber pushout test technique. The load-displacement data indicate a large variability in the initial interface failure stress, although reverse push behavior indicates a comparatively constant interfacial sliding friction stress. The observed behavior suggests that the presence of asperities on the fiber surfaces and nonuniformities in fiber diameter require constrained plastic flow within the NiAl matrix in order for interfacial shear to occur. The location, shape, severity, and distribution of fiber asperities as well as the uniformity of fiber diameter are critical to the interfacial shear process.