NASA NTRS2012

Small-Scale Mechanical Characterization of Space-Exposed Fluorinated Ethylene Propylene Recovered from the Hubble Space Telescope

Multi-layer insulation panels from the Hubble Space Telescope have been recovered after 19.1 years of on-orbit service and micro-tensile experiments have been performed to characterize the effect of space exposure on the mechanical response of the outermost layer. This outer layer, 127 m thick fluorinated ethylene propylene with a 100 nm thick vapor deposited aluminum reflective coating, maintained significant tensile ductility but exhibited a degradation of strength that scales with severity of space exposure. This change in properties is attributed to damage from incident solar flux, atomic oxygen damage, and thermal cycling.

Jones, J. S.↗
NASA NTRS1986

Microstructures in rapidly solidified Ni-Mo alloys

Ni-Mo alloys of compositions ranging from pure Ni to Ni-40 at. percent Mo were rapidly solidified by Chill Block Melt Spinning in vacuum and were examined by optical metallography, X-ray diffraction and transmission electron microscopy. Rapid solidification resulted in an extension of molybdenum solubility in nickel from 28 to 37.5 at. percent. A number of different phases and microstructures were seen at different depths (solidification conditions) from the quenched surface of the melt spun ribbons.

Jayaraman, N.↗
NASA NTRS1985

Orientation and temperature dependence of some mechanical properties of the single-crystal nickel-base superalloy Rene N4. 3: Tension-compression anisotropy

Single crystal superalloy specimens with various crystallographic directions along their axes were tested in compression at room temperature, 650, 760, 870, and 980 deg C. These results are compared with the tensile behavior studied previously. The alloy, Rene N4, was developed for gas turbine engine blades and has the nominal composition 3.7 Al, 4.2 Ti, 4 Ta, 0.5 Nb, 6 W, 1.5 Mo 9 Cr. 7.5 Co, balance Ni, in weight percent. Slip trace analysis showed that primary cube slip occurred even at room temperature for the 111 specimens. With increasing test temperature more orientations exhibited primary cube slip, until at 870 deg C only the 100 and 011 specimens exhibited normal octahedral slip. The yield strength for octahedral slip was numerically analysed using a model proposed by Lall, Chin, and Pope to explain deviations from Schmid's Law in the yielding behavior of a single phase Gamma prime alloy, Ni3(Al, Nb). The Schmid's Law deviations in Rene N4 were found to be largely due to a tension-compression anisotropy. A second effect, which increases trength for orientations away from 001, was found to be small in Rene N4. Analysis of recently published data on the single crystal superalloy PWA 1480 yielded the same result.

Miner, R. V.↗
NASA NTRS1985

Microstructures in rapidly solidified Ni-Mo alloys

Ni-Mo alloys of compositions ranging from pure Ni to Ni-40 at % Mo were rapidly solidified by Chill Block Melt Spinning in vacuum and were examined by optical metallography, X-ray diffraction and transmission electron microscopy. Rapid solidification resulted in an extension of molybdenum solubility in nickel from 28 to 37.5 at %. A number of different phases and microstructures were seen at different depths (solidification conditions) from the quenched surface of the melt spun ribbons.

Jayaraman, N.↗