DOE OSTI2023

Impact on aggregate/matrix bonding when a refractory contains zinc aluminate instead of spinel and magnesia‐chrome

The high hot strength of MgO–Cr 2 O 3 refractory is often ascribed to its intimate aggregate/matrix bonding. For a fundamental comparison with it, ~2 mm aggregates of MgO and Al 2 O 3 were separately embedded in ZnAl 2 O 4 and MgAl 2 O 4 matrices, sintered at 1600°C, and examined. It was found that similarity of thermal expansion coefficient (TEC) between the aggregate and the matrix is critical to achieve good bonding and this is more important than the extent of interdiffusion. The TEC mismatch of ≥ 5.7 × 10 -6 K -1 caused significant undesirable debonding in MgO aggregate/MgAl 2 O 4 matrix sample and MgO/ZnAl 2 O 4 despite >736 μm Zn 2+ diffusion depth in the latter. Direct bonding, as inferred from a thicker interfacial reaction layer and a greater shift of the aggregate/matrix interface before and after firing, was better in MgAl 2 O 4 /ZnAl 2 O 4 combination, followed by tabular Al 2 O 3 /ZnAl 2 O 4 and Al 2 O 3 /MgAl 2 O 4 . Powder X-ray diffraction indicated that the volatilization of ZnAl 2 O 4 at 1600°C in air was negligible compared to MgO–Cr 2 O 3 .

36 MATERIALS SCIENCE↗

DOE OSTI2022

Chrome-free qandilite (Mg 2 TiO 4 ) refractory aggregates: Role of titania source and evaluation of thermal expansion coefficient

As used chrome-based refractories may contain toxic Cr 6+ , the chrome-free Mg 2 TiO 4 phase is being considered which is known to improve hot strength and resistance to thermal shock and slag corrosion. As in situ Mg 2 TiO 4 formation generates porosity, preformed aggregates are desirable. Dilatometric studies revealed that when dead burned magnesia is combined with industrial anatase instead of rutile, it expanded less (1% versus 7.2%) and the reaction occurred earlier (965°C compared to 1120°C). After sintering at 1,600°C, rutile produced an aggregate with 3.8% open porosity, whereas anatase led to 0 % porosity and a bulk density of 3.24g/cm 3 with a thermal expansion coefficient (70–1,600°C) of 13.5×10 -6 K -1 . Moreover, replacing rutile by anatase eliminates the undesirable MgTiO 3 phase. The anatase-based aggregate consisted of a Mg 2 TiO 4 matrix with residual unreacted MgO and an intergranular, refractory CaTiO 3 phase. In conclusion, the rutile-based aggregate was deemed unsuitable due to a low-melting microstructure of forsterite contiguous with CaTiO 3 .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Thermal conductivity of salvaged fused cast alumina used in the glass industry

Fused cast alumina (FCA) has been and continues to be used as a refractory material in energy intensive industries such as glass melting and chemical processing. In-service degradation due to high temperature exposure in harsh environment affects the designed furnace thermal profiles and energy consumption. Phase transformation may occur at the refractory hot face during glass melting altering the properties. Three FCA blocks recovered from industrial furnaces were investigated in this study. The as-received FCA consists primarily of a mixture of alpha (α) and beta (β) alumina that has a thermal conductivity value of 5–6 W/mK. The Hot Disk method was used to obtain thermal conductivity directly on the refractory blocks. At the hot face, a transformation from β to α alumina occurred and was confirmed by an X-ray diffraction study. Thermal conductivity measurements as a function of position also showed a clear transition from β to α alumina at both ends of a complete block with no voids. Thermal conductivity of the α alumina tripled compared to β alumina. This study provides important information of heat transfer and thermal conductivity evolution to refractory manufacturers and users.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Refractory Issues Related to the Use of Hydrogen as An Alternative Fuel

With the increased interest and funding to investigate hydrogen as an alternative fuel to reduce carbon dioxide emissions, considerations may also be necessary to evaluate the effects of fuel substitutions on industrial processes and process vessels. One area that has not received significant attention is the effects on refractory ceramic lining systems when industrial furnaces are fired on hydrogen in place of or in addition to traditional fuels. Examples of changes in burner design and implementation when firing hydrogen can be found in the literature, but much less is documented regarding the effects on processes and process vessels. As such, this article attempts to present some of the issues encountered when substituting hydrogen as an alternative industrial fuel source and to highlight some examples of where this is occurring. Additionally, the possible ramifications of these issues on refractory ceramic lining systems are discussed.

08 HYDROGEN↗

DOE OSTI2020

Cement having stress-indicating properties

A system and method measures subterranean stress. The system and method includes a cement mixture that is mixed with water to set as a solid and a stress measuring-medium having piezospectroscopic properties that directly reveals stress in situ within the cement mixture in response to a photo stimulation. The stress measuring-medium combines with the cement mixture as a dry blend before being combined with water.

36 MATERIALS SCIENCE↗