8 records

NASA NTRS1998

The Consortium for Advancing Renewable Energy Technology (CARET)

The Consortium for Advancing Renewable Energy (CARET) is a research and education program which uses the theme of renewable energy to build a minority scientist pipeline. CARET is also a consortium of four universities and NASA Lewis Research Center working together to promote science education and research to minority students using the theme of renewable energy. The consortium membership includes the HBCUs (Historically Black Colleges and Universities), Fisk, Wilberforce and Central State Universities as well as Kent State University and NASA Lewis Research Center. The various stages of this pipeline provide participating students experiences with a different emphasis. Some emphasize building enthusiasm for the classroom study of science and technology while others emphasize the nature of research in these disciplines. Still others focus on relating a practical application to science and technology. And, of great importance to the success of the program are the interfaces between the various stages. Successfully managing these transitions is a requirement for producing trained scientists, engineers and technologists. Presentations describing the CARET program have been given at this year's HBCU Research Conference at the Ohio Aerospace Institute and as a seminar in the Solar Circle Seminar series of the Photovoltaic and Space Environments Branch at NASA Lewis Research Center. In this report, we will describe the many positive achievements toward the fulfillment of the goals and outcomes of our program. We will begin with a description of the interactions among the consortium members and end with a description of the activities of each of the member institutions .

Gordon, E. M.↗

NASA NTRS1997

Optical and Atomic Force Microscopy Characterization of PbI2 Quantum Dots

Lead iodide (PbI2) clusters were synthesized from the chemical reaction of NaI (or KI) with Pb(NO3)2 in H2O, D2O, CH3OH, and C3H7OH media. The observation of the absorption features above 350 nm with the help of integrating sphere accessory strongly suggests the quantum dot formation of PbI2 in solution. Spectral comparison between the synthesized PbI2 clusters in solution and PbI2 nanophase by impregnation of PbI2 in four different pore-sized porous silica indicates that the PbI2 cluster size in solution is less than 2.5 nm in lateral dimension. Atomic force microscopy (AFM) measurements show that the PbL clusters deposited onto three different molecularly flat surfaces are single-layered. The measured height is 1.0 - 0.1 nm. The swollen layer thickness can be attributed to the intralayer contraction from the strong lateral interaction among PbI2 molecules, which is supported by ab initio calculation. Raman scattering measurement of LO and TO modes of PbI2 in bulk and in the confined state were also conducted in 50-150 cu cm region. The observed three bands at 74, %, 106 1/cm are assigned to TO2, LO2, and LO, mode, respectively. The relatively small red-shift in LO modes may be caused by the surface phonon polaritons of PbI2 nanophase in the porous silica.

Mu, R.↗

NASA NTRS1997

Au Colloids Formed by Ion Implantation in Muscovite Mica Studied by Vibrational and Electronic Spectroscopes and Atomic Force Microscopy

Au was implanted into the (001) surface of Muscovite mica at an energy of 1.1 MeV and at doses of 1, 3, 6, and 10 x 10(exp 16) ions/cu cm. Optical spectra of the as-implanted samples revealed a peak at 2.28 eV (545 nm) which is attributed to the surface plasmon absorption of Au colloids. The infrared reflectance measurements show a decreasing reflectivity with increasing ion dose in the Si-O stretching region (900-1200 /cm). A new peak observed at 967 /cm increases with the ion dose and is assigned to an Si-O dangling bond. Atomic force microscopy images of freshly cleaved samples implanted with 6 and 10 x 10(exp 16) ions/sq cm indicated metal colloids with diameters between 0.9- 1.5 nm. AFM images of the annealed samples showed irregularly shaped structures with a topology that results from the fusion of smaller colloids.

Tung, Y. S.↗

NASA NTRS1997

Annealing Effects on the Surface Plasmon of MgO Implanted with Gold

Gold ion implantation was carried out with the energy of 1.1 MeV into (100) oriented MgO single crystal. Implanted doses are 1, 3, 6, 10 x 10(exp 16) ions/sq cm. The gold irradiation results in the formation of gold ion implanted layer with a thickness of 0.2 microns and defect formation. In order to form gold colloids from the as-implanted samples, we annealed the gold implanted MgO samples in three kinds of atmospheres: (1)Ar only, (2)H2 and Ar, and (3)O2 and Ar. The annealing over 1200 C enhanced the gold colloid formation which shows surface plasmon resonance band of gold. The surface plasmon bands of samples annealed in three kinds of atmospheres were found to be at 535 nm (Ar only), 524 nm(H2+Ar), and 560 nm (02+Ar), The band positions of surface plasmon can be reversibly changed by an additional annealing.

Ueda, A.↗

NASA NTRS1997

Electronic and Vibrational Spectra of InP Quantum Dots Formed by Sequential Ion Implantation

We have performed sequential ion implantation of indium and phosphorus into silica combined with controlled thermal annealing to fabricate InP quantum dots in a dielectric host. Electronic and vibrational spectra were measured for the as-implanted and annealed samples. The annealed samples show a peak in the infrared spectra near 320/cm which is attributed to a surface phonon mode and is in good agreement with the value calculated from Frolich's theory of surface phonon polaritons. The electronic spectra show the development of a band near 390 nm that is attributed to quantum confined InP.

Hall, C.↗

NASA NTRS1995

Metal colloids and semiconductor quantum dots: Linear and nonlinear optical properties

One aspect of this project involves a collaborative effort with the Solid State Division of ORNL. The thrust behind this research is to develop ion implantion for synthesizing novel materials (quantum dots wires and wells, and metal colloids) for applications in all optical switching devices, up conversion, and the synthesis of novel refractory materials. In general the host material is typically a glass such as optical grade silica. The ions of interest are Au, Ag, Cd, Se, In, P, Sb, Ga and As. An emphasis is placed on host guest interactions between the matrix and the implanted ion and how the matrix effects and implantation parameters can be used to obtain designer level optical devices tailored for specific applications. The specific materials of interest are: CdSe, CdTe, InAs, GaAs, InP, GaP, InSb, GaSb and InGaAs. A second aspect of this research program involves using porous glass (25-200 A) for fabricating materials of finite size. In this part of the program, we are particularly interested in characterizing the thermodynamic and optical properties of these non-composite materials. We also address how phase diagram of the confined material is altered by the interfacial properties between the confined material and the pore wall.

Henderson, D. O.↗

NASA NTRS1993

Study of tellurium precipitates in CdTe crystals

The effect of tellurium precipitates was studied in medium resistivity (10 exp 3-10 exp 6 ohm cm) undoped and Cl-doped CdTe using differential scanning calorimetry (DSC) and mid-infrared spectroscopy and the results were correlated with near-infrared microscopy photographs. When present in a significant quantity (about 0.25 wt pct), we show that Te precipitates are detectable using DSC measurements. In the mid-infrared, the contribution of the absorption by free-carriers is negligible, and therefore, the effect of the Te precipitates in these crystals can be considered uncoupled from the effects of Cd vacancies.

Jayatirtha, H. N.↗

NASA NTRS1989

Purification, growth, and characterization of Zn(x)Cd(1-x)Se crystals

The purification of starting materials which were used in the growth of Zn(x)Cd(1-x)Se (x = 0.2) single crystals using the traveling solution method (TSM) is reported. Up to 13 cm long single crystals and as grown resistivities of 6 x 10(exp 12) ohm/cm could be achieved. Infrared and Raman spectra of Zn(0.2)Cd(0.8)Se are also presented and discussed.

Silberman, E.↗