Accommodating a hexagonal ζ- phase Mn 2 N film on a cubic MgO (001) substrate
The thin films of c -plane dominated hexagonal ζ- phase Mn 2 N were successfully grown on a cubic MgO (001) substrate directly using plasma-assisted molecular beam epitaxy. The surface was comprehensively studied through experimental and theoretical approaches. Reflection high energy electron diffraction revealed two pseudo-cubic domains along [100] MgO and [110] MgO , and one hexagonal domain, which is 30° apart from the [100] MgO direction. Scanning tunneling microscopy was used to image and resolve the high-quality surface, revealing a distorted hexagonal surface structure. Furthermore, atomic resolution of the hexagonal domain with a 2 × 2 reconstructed surface is presented. For c-plane surface, theoretical investigations were carried out using first principles studies to determine the surface formation energy for various reconstructed surfaces. The theoretical study shows that the nitrogen terminated 2 × 2 structure with a manganese adatom on the surface as the most stable reconstruction that reproduces the experimental results. A corresponding simulated scanning tunneling microscopy model is also presented, providing strong support for the experimentally observed in-plane lattice structures. Furthermore, the manganese: nitrogen stoichiometry within the bulk and surface is in good agreement with the expected ratio of 2:1.