A method for determining crack opening load from load-displacement data

The fatigue crack opening load is determined as the tangent point on the ascending load-displacement data between the curved portion and the upper linear region. A model for the 'unzipping' behavior of the crack indicates that the curved portion of the load-deflection curve is second order. The opening load is determined by a nonlinear, least squares fit of the data to the model, which optimally locates the tangent point of the two curves. The method provided consistent results for determining opening load P(op) for 7475-T731 aluminum using data from a crack tip opening gage.

Carman, C. Davis↗

NASA NTRS1988

Fatigue crack closure behavior at high stress ratios

Fatigue crack delay behavior at high stress ratio caused by single peak overloads was investigated in two thicknesses of 7475-T731 aluminum alloy. Closure measurements indicated no closure occurred before or throughout the overload plastic zones following the overload. This was further substantiated by comparing the specimen compliance following the overload with the compliance of a low R ratio test when the crack was fully open. Scanning electron microscope studies revealed that crack tunneling and possibly reinitiation of the crack occurred, most likely a result of crack-tip blunting. The number of delay cycles was greater for the thinner mixed mode stress state specimen than for the thicker plane strain stress state specimen, which is similar to low R ratio test results and may be due to a larger plastic zone for the mixed mode cased.

Turner, C. Christopher↗