Decreasing membrane thickness reduces the reaction time for the competing amine-H 2 S and amine-CO 2 reactions, thus enhancing the selectivity for the “faster”, kinetically favored product, i.e. , hydrosulfide.
Membranes, methods of making the membranes, and methods of using the membranes are described herein. The membranes can comprise a support layer, and a selective polymer layer disposed on the support layer. In some cases, the support layer can comprise a gas permeable polymer and hydrophilic additive dispersed within the gas permeable polymer. In some cases, the selective polymer layer can comprise a selective polymer matrix and carbon nanotubes dispersed within the selective polymer matrix. The membranes can exhibit selective permeability to gases. As such, the membranes can be for the selective removal of carbon dioxide and/or hydrogen sulfide from hydrogen and/or nitrogen.
Membranes, methods of making the membranes, and methods of using the membranes are described herein. The membranes can comprise a support layer, and a selective polymer layer disposed on the support layer. The selective polymer layer can comprise a selective polymer matrix and carbon nanotubes dispersed within the selective polymer matrix. The carbon nanotubes can comprise multi-walled carbon nanotubes wrapped in a hydrophilic polymer, such as polyvinylpyrrolidone or a copolymer thereof, such as poly(1-vinylpyrrolidone-co-vinyl acetate). The membranes can exhibit selective permeability to gases. As such, the membranes can be for the selective removal of carbon dioxide and/or hydrogen sulfide from hydrogen and/or nitrogen.
Natural gas, an important source of hydrogen, is expected to be crucial in the transition to a hydrogen-based economy. The landscape of the gas processing industry is set to change in the near future with the development of highly acidic sour gas wells. Natural gas purification constitutes a major share of the gas separation membrane market, and the shift to low-quality sour gas wells has been mirrored in the trends of membrane material research. Purification also constitutes the major portion of the cost of natural gas, posing implications for the cost of hydrogen production. This review provides an update on the current state of research regarding polymeric membranes for H2S removal, along with CO2 separation, from natural gas that is used for hydrogen production via steam methane reforming. The challenges of adapting polymeric membranes to ternary H2S/CO2/CH4 separations are discussed in detail. Key polymeric materials are highlighted, and the prospects for their application in H2S removal from natural gas are evaluated. Finally, the growing interest in H2 production from H2S is discussed. Advances in the membrane industry and the emergence of new membrane materials may significantly improve the commercial viability of such processes.
Some of amino acid salts (AASs) have been demonstrated to be effective mobile carriers in facilitated transport membranes (FTMs) to achieve superior CO 2 permeance and CO 2 /N 2 selectivity for CO 2 capture from flue gas. Understandings of how the structures of different AASs affect the chemistry of the amine–CO 2 reaction are essential for the future development of more efficient AAS mobile carriers. In this study, the reaction chemistry of selected AASs with CO 2 was investigated by 13 C nuclear magnetic resonance (NMR) spectroscopy. The CO 2 loading and the distribution of major reaction products, including carbamate and bicarbonate products of each studied AAS were quantitatively analyzed. The positive correlation between the CO 2 loading of AAS (mol CO 2 /g AAS) and the CO 2 permeance of FTMs suggested that AAS with a higher CO 2 loading may improve the performance of FTMs. Our results also showed that increasing the steric hindrance of AAS could be a practical way to promote the bicarbonate reaction pathway and thus potentially increase the CO 2 loading (mol CO 2 /mol AAS). Moreover, 2-(1-piperazinyl)ethylamine (PZEA) was found to be a more effective multi-amine than piperazine (PZ) for synthesizing AASs due to the presence of more effective nitrogen sites per molecule. The superior CO 2 permeance of the PZEA-Sar membrane is also attributed to its more uniform membrane formation. As a result, the knowledge gained from this study will inform the rational design of more effective AAS carriers for CO 2 capture.
Not provided.
Membranes, methods of making the membranes, and methods of using the membranes are described herein. The membranes can comprise a gas permeable support layer, an inorganic layer disposed on the support, the inorganic layer comprising a plurality of discreet nanoparticles having an average particle size of less than 1 micron, and a selective polymer layer disposed on the inorganic layer, the selective polymer layer comprising a selective polymer having a CO2:N2 selectivity of at least 10 at 57° C. In some embodiments, the membrane can be selectively permeable to an acidic gas. The membranes can be used, for example, to separate gaseous mixtures, such as flue gas.
Disclosed herein are 2-stage membrane separation methods for capturing CO2 from a feed gas. The methods can employ two selectively permeable membranes, which may be the same or different. The selectively permeable membrane can have a carbon dioxide permeance of from 500 to 3000 GPU at 57° C. and 1 atm feed pressure and a carbon dioxide:nitrogen selectivity of from 10 to 1000 at 57° C. and 1 atm feed pressure. High pressure ratios across the membranes can be achieved by compressing the feed gas to a high pressure, by using vacuum pumps to create a lowered pressure on the permeate side of the membrane, by using a sweep stream, or a combination thereof. When a sweep stream is used, the sweep stream may include a portion of the retentate gas stream obtained from the retentate side of one or more of the membranes used.
A substrate with bicontinuous structure is attractive for thin-film composite (TFC) membrane synthesis due to its high surface porosity and well-interconnected bulk morphology. In this study, the vapor-induced phase separation (VIPS) of the casting solution comprising water, 2-pyrrolidone, and polyethersulfone (PES) was studied. By tuning the water addition in the casting solution and water vapor exposure time, the optimized substrate exhibited a bicontinuous surface with a high porosity of 24.2% (or 216/µm 2 pore density), thereby mitigating pore restriction and showing a high CO 2 permeance of 2.94×10 5 GPU. Compared to the benchmark PES substrate with cellular surface pores and lower gas permeance, the use of the bicontinuous substrate led to a 12% increase in the CO 2 permeance of the TFC membrane. The mitigated pore restriction was further rationalized by a resistance-in-series model. The analysis of the lateral diffusion and substrate resistances indicates that an even higher surface pore density of the substrate is required to fully realize the potential of ultra-permeable, CO 2 -selective polymers in the TFC configuration. As a result, the scalability of the VIPS process was demonstrated by the roll-to-roll fabrication of the optimized bicontinuous substrate with a width of 21" and a length of >100'.
A membrane-based system with a retentate recycle process in tandem with an enriching cascade was studied for >90% carbon capture from coal flue gas. A highly CO 2 -selective facilitated transport membrane (FTM) was utilized particularly to enhance the CO 2 separation efficiency from the CO 2 -lean gases for a high capture degree. A techno-economic analysis showed that the retentate recycle process was advantageous for ≤90% capture owing to the reduced parasitic energy consumption and membrane area. At >90% capture, the enriching cascade outperformed the retentate recycle process since a higher feed-to-permeate pressure ratio could be applied. An overall 99% capture degree could be achieved by combining the two processes, which yielded a low capture cost of USD47.2/tonne, whereas that would be USD 42.0/tonne for 90% capture. This FTM-based approach for deep carbon capture and storage can direct air capture for the mitigation of carbon emissions in the energy sector.
Polymeric facilitated transport membranes (FTMs) have emerged as an innovative class of promising carbon capture technology. Studies have shown that the transport properties of an FTM are significantly influenced by its water uptake. In order to better quantify FTM performance, we herein explore the potential of computational techniques to predict the equilibrium water uptake values of FTMs. Two prediction approaches were examined. First, the water sorption was explicitly simulated by iteratively conducting grand canonical Monte Carlo (GCMC) and molecular dynamics (MD) simulations. Second, the water sorption was predicted based on the chemical potential of the adsorbed water, which was calculated using the Widom insertion or continuous fractional component Monte Carlo (CFCMC) method. The chemical potential-based approach with CFCMC demonstrated good prediction of the equilibrium water uptake values of FTMs with poly(N-vinylformamide-co-vinylamine) as fixed-site carrier and 2-(1-piperazinyl)ethylamine sarcosinate as mobile carrier. The predicted water uptake values increased with increasing mobile carrier content and were in good agreement with the experimental values. Furthermore, the higher water uptake promoted the diffusion of CO 2 , N 2 , and mobile carrier as well as slightly stifled the sorption of N 2 . Such an approach significantly contributes to a more comprehensive theoretical evaluation of FTMs.
Scalable fabrication of thin-film composite (TFC) membrane for post-combustion carbon capture is often limited by the availability of high-performance nanoporous substrate. Ideally, the substrate should allow for fast gas transport at the selective layer/substrate interface as well as in the bulk of the substrate. In this study, highly permeable Matrimid substrates were prepared via vapor- and nonsolvent-induced phase separations. The phase separation mechanism of the Matrimid®/N-methyl-2-pyrrolidone casting solution was modulated by the addition of LiCl to control the solution thermodynamic stability, and nanoporous Matrimid substrates were formed with a bicontinuous surface and macrovoids in the bulk. This hierarchically optimized structure resulted in a CO 2 permeance of 2.60 × 10 5 GPU (1 GPU = 1 × 10 –6 cm 3 (STP) cm –2 s –1 cmHg –1 = 3.349 × 10 –10 mol m –2 s –1 Pa –1 ), which was ca. 11 times more permeable than a benchmark polyethersulfone substrate with cellular pores. The benefit of using this new substrate was demonstrated by coating a 170-nm amine-containing polymer to form a TFC facilitated transport membrane. The membrane exhibited a CO 2 permeance of 932 GPU at 57°C, which was 72 GPU higher than the counterpart coated on the benchmark substrate. Meanwhile, the CO 2 /N 2 selectivity was remained at 158. This permeance improvement could be well explained by the resistance-in-series model, where the improved permeance was attributed to the reductions in substrate and lateral diffusion mass transfer resistances. The upper bound (UB) analysis indicates that the Matrimid substrate is nearly ideal for the state-of-the-art polymers for CO 2 /N 2 separation. Here, the substrate improvement could also reduce the parasitic energy associated with the membrane process due to the reduced membrane cost and flue gas compression requirement.
A single-stage membrane process has been designed for using facilitated transport membranes (FTMs) to decarbonize the coal-derived syngas from an integrated gasification combined cycle (IGCC) power plant. The necessary process model and costing method have also been developed to assess the technical feasibility and process economics. In order to account for the carrier saturation phenomenon associated with FTMs, a homogeneous reactive diffusion model is integrated into the process model. The techno-economic study reveals that the mitigated carrier saturation upon bulk CO 2 removal can lead to appreciable increases in the CO 2 permeance and CO 2 /H 2 selectivity, which can be utilized to achieve 95% CO 2 purity and 95% H 2 recovery with a CO 2 /H 2 selectivity of 50 at the complete carrier saturation. FTMs with different facilitated transport characteristics can also be arranged in a hybrid membrane configuration to render a H 2 recovery of 99% and a cost of electricity of $\$118.5$ /MWh, which is 12.5% lower than that of the benchmark Selexol process.
Over the past decade, CO 2 separation and capture have become the new bandwagon for polymer science and membrane research. This review presents the fundamentals of CO 2 /gas separation in polymeric membranes and discusses how these principles underpin opportunities and challenges for post-combustion carbon capture (CO 2 /N 2 ), hydrogen purification (CO 2 /H 2 ), and natural gas and biogas sweetening (CO 2 /CH 4 ). Emerging polymeric membrane materials are discussed, including a few polymers containing a high content of polar functional groups (i.e., ether oxygen-rich polymers and polymeric ionic liquids), shape-persisting glassy polymers (i.e., perfluoropolymers, thermally rearranged polymers, iptycene-containing polymers), and reactive polymers featuring facilitated transport. Moreover, the promising candidates for each CO 2 separation application are highlighted. Lastly, the permeability-selectivity data reviewed were plotted against their 2008 and 2019 upper bounds.
Membranes for post-combustion CO 2 capture are required to have a high CO 2 permeance due to the limited driving force. For facilitated transport membranes synthesized with polyvinylamine (PVAm), a defect-free selective layer of <200 nm is usually required to render sufficient permeance with high CO 2 /N 2 selectivity. In order to meet such a demand through the knife-coating process, the coating solution needs to have a high viscosity at a relatively low concentration to minimize its penetration into the substrate. The demand was met by synthesizing PVAm with an ultrahigh molecular weight (MW) via inverse emulsion polymerization (IEP) in this study. Compared to solution polymerization, IEP isolates the reaction in inverse micelles suspended in a continuous organic phase, which allows excellent dissipation of the heat generated by the reaction and reduces gel formation drastically. The polymerization parameters, including monomer concentration, initiator concentration, and reaction temperature, were investigated to obtain the optimal MW of PVAm for membrane performance. As compared to solution polymerization, IEP enhanced the MW of PVAm from 1.2 to 12.7 MDa, which minimized the penetration of the coating solution into the substrate and hence the extra mass transfer resistance. The effect of MW and degree of hydrolysis of PVAm on the membrane transport properties were studied. Furthermore, by employing PVAm with a MW of 12.7 MDa to strengthen the polymer matrix, the loading of piperazine glycinate in the membrane was increased up to 85 wt.%. In conclusion, the resultant membrane achieved a CO 2 permeance of 839 GPU and a CO 2 /N 2 selectivity of 161 at the typical flue gas temperature of 57°C.
CO2 capture from coal- or natural gas-derived flue gas has been widely considered as the next opportunity for the large-scale deployment of gas separation membranes. Despite the tremendous progress made in the synthesis of polymeric membranes with high CO2/N2 separation performance, only a few membrane technologies were advanced to the bench-scale study or above from a highly idealized laboratory setting. Therefore, the recent progress in polymeric membranes is reviewed in the perspectives of capture system energetics, process synthesis, membrane scale-up, modular fabrication, and field tests. These engineering considerations can provide a holistic approach to better guide membrane research and accelerate the commercialization of gas separation membranes for post-combustion carbon capture.
Amine-containing mixed-matrix membranes incorporated with amino-functionalized multi-walled carbon nanotubes (AF-MWNTs) were synthesized for CO2/H2 separation based on the facilitated transport mechanism. AF-MWNTs were chosen primarily as the mechanical reinforcing filler to enhance the membrane stability. At 107 °C and 0.2-MPa feed pressure, the membrane incorporated with 10 wt.% AF-MWNTs showed a CO2 permeability of 3196 Barrers and a CO2/H2 selectivity of 205. At the higher feed pressure of 1.5 MPa, owing to the carrier saturation phenomenon, the same membrane exhibited reduced transport performance with a CO2 permeability of 776 Barrers and a CO2/H2 selectivity of 31. These separation performances at both the low and high feed pressures were well above the theoretical upper bound. Furthermore, the incorporation of 10 wt.% AF-MWNTs led to a significant improvement on membrane stability. The transport performance and selective layer thickness of this membrane maintained for 100 h, which suggested that the incorporation of AF-MWNTs improved the resistance to membrane compaction upon a high feed pressure. Therefore, this work is considered as one of the crucial steps to enable the application of facilitated transport membranes to high-pressure gas processing such as syngas purification.